Field | Value |
---|---|
Lab ID | CAA528 |
Field ID | 72ANC211 |
Job ID | 10011 |
Sample submitter | Sorg, Dennis H. |
Date submitted | 3/16/1970 |
Project name | Alaska Ultramafics |
State | AK |
Country | United States |
Latitude (WGS84) | 61.76543248 |
Longitude (WGS84) | -157.31018539 |
Original datum | (NAD27) |
Original latitude | 61.76611 |
Original longitude | -157.30779 |
Location precision | 1 second |
Collection method | single/grab |
Primary media type | sediment |
Secondary media type | concentrate |
Sample media name | pan concentrate (raw) |
Notes on sample | not a conventional bulk panned concentrate; |
Sample preparation method | panned; sieved |
Sieve size | -250 mesh |
(click for info) | |
Geologic map unit | -157.31018539, 61.76543248 |
Nearby scientific data | Find additional scientific data near this location |
Element | Measured value | Units of measure | Analytical method |
---|---|---|---|
Beryllium | <1 | parts per million by weight | ES_SQ |
Boron | 50 | parts per million by weight | ES_SQ |
Magnesium | 1.5 | percent by weight | ES_SQ |
Calcium | 1 | percent by weight | ES_SQ |
Scandium | 10 | parts per million by weight | ES_SQ |
Titanium | 1 | percent by weight | ES_SQ |
Vanadium | 200 | parts per million by weight | ES_SQ |
Chromium | 200 | parts per million by weight | ES_SQ |
Manganese | 0.3 | percent by weight | ES_SQ |
Iron | 10 | percent by weight | ES_SQ |
Cobalt | 20 | parts per million by weight | ES_SQ |
Nickel | 20 | parts per million by weight | ES_SQ |
Copper | 20 | parts per million by weight | ES_SQ |
Zinc | <200 | parts per million by weight | ES_SQ |
Arsenic | <200 | parts per million by weight | ES_SQ |
Strontium | <100 | parts per million by weight | ES_SQ |
Yttrium | 150 | parts per million by weight | ES_SQ |
Zirconium | > 000 | parts per million by weight | ES_SQ |
Niobium | <20 | parts per million by weight | ES_SQ |
Molybdenum | <5 | parts per million by weight | ES_SQ |
Silver | 1.5 | parts per million by weight | ES_SQ |
Cadmium | <20 | parts per million by weight | ES_SQ |
Tin | <10 | parts per million by weight | ES_SQ |
Antimony | <100 | parts per million by weight | ES_SQ |
Barium | 500 | parts per million by weight | ES_SQ |
Lanthanum | 500 | parts per million by weight | ES_SQ |
Tungsten | <50 | parts per million by weight | ES_SQ |
Gold | <10 | parts per million by weight | ES_SQ |
Lead | 20 | parts per million by weight | ES_SQ |
Bismuth | <10 | parts per million by weight | ES_SQ |
Element | Value | Units | Technique |
---|---|---|---|
Beryllium | N1 | parts per million by weight | ES_SQ |
Boron | 50 | parts per million by weight | ES_SQ |
Magnesium | 1.5 | percent by weight | ES_SQ |
Calcium | 1 | percent by weight | ES_SQ |
Scandium | 10 | parts per million by weight | ES_SQ |
Titanium | 1 | percent by weight | ES_SQ |
Vanadium | 200 | parts per million by weight | ES_SQ |
Chromium | 200 | parts per million by weight | ES_SQ |
Manganese | 0.3 | percent by weight | ES_SQ |
Iron | 10 | percent by weight | ES_SQ |
Cobalt | 20 | parts per million by weight | ES_SQ |
Nickel | 20 | parts per million by weight | ES_SQ |
Copper | 20 | parts per million by weight | ES_SQ |
Zinc | N200 | parts per million by weight | ES_SQ |
Arsenic | N200 | parts per million by weight | ES_SQ |
Strontium | L100 | parts per million by weight | ES_SQ |
Yttrium | 150 | parts per million by weight | ES_SQ |
Zirconium | G1000.11 | parts per million by weight | ES_SQ |
Niobium | L20 | parts per million by weight | ES_SQ |
Molybdenum | N5 | parts per million by weight | ES_SQ |
Silver | 1.5 | parts per million by weight | ES_SQ |
Cadmium | N20 | parts per million by weight | ES_SQ |
Tin | N10 | parts per million by weight | ES_SQ |
Antimony | N100 | parts per million by weight | ES_SQ |
Barium | 500 | parts per million by weight | ES_SQ |
Lanthanum | 500 | parts per million by weight | ES_SQ |
Tungsten | N50 | parts per million by weight | ES_SQ |
Gold | N10 | parts per million by weight | ES_SQ |
Lead | 20 | parts per million by weight | ES_SQ |
Bismuth | N10 | parts per million by weight | ES_SQ |