Field | Value |
---|---|
Lab ID | CDF688 |
Field ID | M001C3 |
Job ID | 11218 |
Sample submitter | King, Harley D. |
Date submitted | 9/22/1978 |
Project name | Medfra AMRAP |
State | AK |
Country | United States |
Latitude (WGS84) | 63.23105973 |
Longitude (WGS84) | -154.76608149 |
Original datum | (NAD27) |
Original latitude | 63.23166 |
Original longitude | -154.76361 |
Location precision | 1 second |
Sample source | stream/river |
Collection method | single/grab |
Primary media type | sediment |
Secondary media type | concentrate |
Sample media name | C3 fraction |
Notes on sample | stream |
Sample preparation method | panned; sieved; bromoform separation; electromagnetic separation |
Sieve size | -20 mesh |
(click for info) | |
Geologic map unit | -154.76608149, 63.23105973 |
Nearby scientific data | Find additional scientific data near this location |
Element | Measured value | Units of measure | Analytical method |
---|---|---|---|
Beryllium | <2 | parts per million by weight | ES_SQ |
Boron | 50 | parts per million by weight | ES_SQ |
Magnesium | 0.2 | percent by weight | ES_SQ |
Calcium | 7 | percent by weight | ES_SQ |
Scandium | 50 | parts per million by weight | ES_SQ |
Titanium | > | percent by weight | ES_SQ |
Vanadium | 100 | parts per million by weight | ES_SQ |
Chromium | 100 | parts per million by weight | ES_SQ |
Manganese | 0.05 | percent by weight | ES_SQ |
Iron | 2 | percent by weight | ES_SQ |
Cobalt | <10 | parts per million by weight | ES_SQ |
Nickel | <10 | parts per million by weight | ES_SQ |
Copper | 200 | parts per million by weight | ES_SQ |
Zinc | <500 | parts per million by weight | ES_SQ |
Arsenic | <500 | parts per million by weight | ES_SQ |
Strontium | 200 | parts per million by weight | ES_SQ |
Yttrium | 1000 | parts per million by weight | ES_SQ |
Zirconium | > 000 | parts per million by weight | ES_SQ |
Niobium | <50 | parts per million by weight | ES_SQ |
Molybdenum | 70 | parts per million by weight | ES_SQ |
Silver | <1 | parts per million by weight | ES_SQ |
Cadmium | <50 | parts per million by weight | ES_SQ |
Tin | 150 | parts per million by weight | ES_SQ |
Antimony | <200 | parts per million by weight | ES_SQ |
Barium | 200 | parts per million by weight | ES_SQ |
Lanthanum | 700 | parts per million by weight | ES_SQ |
Tungsten | <100 | parts per million by weight | ES_SQ |
Gold | 20 | parts per million by weight | ES_SQ |
Lead | 700 | parts per million by weight | ES_SQ |
Bismuth | 50 | parts per million by weight | ES_SQ |
Thorium | <200 | parts per million by weight | ES_SQ |
Element | Value | Units | Technique |
---|---|---|---|
Beryllium | L2 | parts per million by weight | ES_SQ |
Boron | 50 | parts per million by weight | ES_SQ |
Magnesium | 0.2 | percent by weight | ES_SQ |
Calcium | 7 | percent by weight | ES_SQ |
Scandium | 50 | parts per million by weight | ES_SQ |
Titanium | G1.11 | percent by weight | ES_SQ |
Vanadium | 100 | parts per million by weight | ES_SQ |
Chromium | 100 | parts per million by weight | ES_SQ |
Manganese | 0.05 | percent by weight | ES_SQ |
Iron | 2 | percent by weight | ES_SQ |
Cobalt | L10 | parts per million by weight | ES_SQ |
Nickel | L10 | parts per million by weight | ES_SQ |
Copper | 200 | parts per million by weight | ES_SQ |
Zinc | N500 | parts per million by weight | ES_SQ |
Arsenic | N500 | parts per million by weight | ES_SQ |
Strontium | 200 | parts per million by weight | ES_SQ |
Yttrium | 1000 | parts per million by weight | ES_SQ |
Zirconium | G1000.11 | parts per million by weight | ES_SQ |
Niobium | L50 | parts per million by weight | ES_SQ |
Molybdenum | 70 | parts per million by weight | ES_SQ |
Silver | N1 | parts per million by weight | ES_SQ |
Cadmium | N50 | parts per million by weight | ES_SQ |
Tin | 150 | parts per million by weight | ES_SQ |
Antimony | N200 | parts per million by weight | ES_SQ |
Barium | 200 | parts per million by weight | ES_SQ |
Lanthanum | 700 | parts per million by weight | ES_SQ |
Tungsten | N100 | parts per million by weight | ES_SQ |
Gold | 20 | parts per million by weight | ES_SQ |
Lead | 700 | parts per million by weight | ES_SQ |
Bismuth | 50 | parts per million by weight | ES_SQ |
Thorium | L200 | parts per million by weight | ES_SQ |