Field | Value |
---|---|
Lab ID | ECV698 |
Field ID | 77GU201M |
Job ID | 31388 |
Sample submitter | Watts, Kenneth C. |
Date submitted | 12/27/1977 |
State | AZ |
Country | United States |
Latitude (WGS84) | 32.77340126 |
Longitude (WGS84) | -109.25256646 |
Original datum | (NAD27) |
Original latitude | 32.77333333 |
Original longitude | -109.25194444 |
Location precision | 1 second |
Sample source | stream/river |
Collection method | composite |
Primary media type | sediment |
Secondary media type | concentrate |
Sample media name | C2 fraction |
Notes on sample | C2; stream |
Sample preparation method | panned; sieved; bromoform separation; electromagnetic separation |
(click for info) | |
Geologic map unit | -109.25256646, 32.77340126 |
Nearby scientific data | Find additional scientific data near this location |
Element | Measured value | Units of measure | Analytical method |
---|---|---|---|
Beryllium | 2 | parts per million by weight | ES_SQ |
Boron | <20 | parts per million by weight | ES_SQ |
Magnesium | 0.7 | percent by weight | ES_SQ |
Calcium | 1 | percent by weight | ES_SQ |
Scandium | 20 | parts per million by weight | ES_SQ |
Titanium | 0.7 | percent by weight | ES_SQ |
Vanadium | 700 | parts per million by weight | ES_SQ |
Chromium | 300 | parts per million by weight | ES_SQ |
Manganese | 0.51 | percent by weight | ES_SQ |
Iron | > 20 | percent by weight | ES_SQ |
Cobalt | 100 | parts per million by weight | ES_SQ |
Nickel | 100 | parts per million by weight | ES_SQ |
Copper | 300 | parts per million by weight | ES_SQ |
Zinc | <500 | parts per million by weight | ES_SQ |
Arsenic | <500 | parts per million by weight | ES_SQ |
Strontium | 700 | parts per million by weight | ES_SQ |
Yttrium | 50 | parts per million by weight | ES_SQ |
Zirconium | 300 | parts per million by weight | ES_SQ |
Niobium | <50 | parts per million by weight | ES_SQ |
Molybdenum | <10 | parts per million by weight | ES_SQ |
Silver | <1 | parts per million by weight | ES_SQ |
Cadmium | <50 | parts per million by weight | ES_SQ |
Tin | 20 | parts per million by weight | ES_SQ |
Antimony | <200 | parts per million by weight | ES_SQ |
Barium | > 5000 | parts per million by weight | ES_SQ |
Lanthanum | 20 | parts per million by weight | ES_SQ |
Tungsten | <100 | parts per million by weight | ES_SQ |
Gold | <20 | parts per million by weight | ES_SQ |
Lead | 100 | parts per million by weight | ES_SQ |
Bismuth | <20 | parts per million by weight | ES_SQ |
Element | Value | Units | Technique |
---|---|---|---|
Beryllium | 2 | parts per million by weight | ES_SQ |
Boron | L20 | parts per million by weight | ES_SQ |
Magnesium | 0.7 | percent by weight | ES_SQ |
Calcium | 1 | percent by weight | ES_SQ |
Scandium | 20 | parts per million by weight | ES_SQ |
Titanium | 0.7 | percent by weight | ES_SQ |
Vanadium | 700 | parts per million by weight | ES_SQ |
Chromium | 300 | parts per million by weight | ES_SQ |
Manganese | G0.51 | percent by weight | ES_SQ |
Iron | G20.11 | percent by weight | ES_SQ |
Cobalt | 100 | parts per million by weight | ES_SQ |
Nickel | 100 | parts per million by weight | ES_SQ |
Copper | 300 | parts per million by weight | ES_SQ |
Zinc | L500 | parts per million by weight | ES_SQ |
Arsenic | N500 | parts per million by weight | ES_SQ |
Strontium | 700 | parts per million by weight | ES_SQ |
Yttrium | 50 | parts per million by weight | ES_SQ |
Zirconium | 300 | parts per million by weight | ES_SQ |
Niobium | N50 | parts per million by weight | ES_SQ |
Molybdenum | N10 | parts per million by weight | ES_SQ |
Silver | N1 | parts per million by weight | ES_SQ |
Cadmium | N50 | parts per million by weight | ES_SQ |
Tin | 20 | parts per million by weight | ES_SQ |
Antimony | N200 | parts per million by weight | ES_SQ |
Barium | G5000.11 | parts per million by weight | ES_SQ |
Lanthanum | 20 | parts per million by weight | ES_SQ |
Tungsten | L100 | parts per million by weight | ES_SQ |
Gold | N20 | parts per million by weight | ES_SQ |
Lead | 100 | parts per million by weight | ES_SQ |
Bismuth | N20 | parts per million by weight | ES_SQ |