Field | Value |
---|---|
Lab ID | EDF165 |
Field ID | 77GU200N |
Job ID | 31385 |
Sample submitter | Watts, Kenneth C. |
Date submitted | 12/13/1977 |
Country | United States |
Latitude (WGS84) | 32.77506791 |
Longitude (WGS84) | -109.25228871 |
Original datum | (NAD27) |
Original latitude | 32.775 |
Original longitude | -109.25166667 |
Location precision | 1 second |
Sample source | stream/river |
Collection method | composite |
Primary media type | sediment |
Secondary media type | concentrate |
Sample media name | C3 fraction |
Notes on sample | C3; stream |
Sample preparation method | panned; sieved; bromoform separation; electromagnetic separation |
(click for info) | |
Geologic map unit | -109.25228871, 32.77506791 |
Nearby scientific data | Find additional scientific data near this location |
Element | Measured value | Units of measure | Analytical method |
---|---|---|---|
Beryllium | 20 | parts per million by weight | ES_SQ |
Boron | <20 | parts per million by weight | ES_SQ |
Magnesium | 0.05 | percent by weight | ES_SQ |
Calcium | 5 | percent by weight | ES_SQ |
Scandium | 30 | parts per million by weight | ES_SQ |
Titanium | 1 | percent by weight | ES_SQ |
Vanadium | 30 | parts per million by weight | ES_SQ |
Chromium | 20 | parts per million by weight | ES_SQ |
Manganese | 0.05 | percent by weight | ES_SQ |
Iron | 0.7 | percent by weight | ES_SQ |
Cobalt | <10 | parts per million by weight | ES_SQ |
Nickel | <10 | parts per million by weight | ES_SQ |
Copper | 300 | parts per million by weight | ES_SQ |
Zinc | <500 | parts per million by weight | ES_SQ |
Arsenic | <500 | parts per million by weight | ES_SQ |
Strontium | <200 | parts per million by weight | ES_SQ |
Yttrium | 500 | parts per million by weight | ES_SQ |
Zirconium | > 000 | parts per million by weight | ES_SQ |
Niobium | <50 | parts per million by weight | ES_SQ |
Molybdenum | <10 | parts per million by weight | ES_SQ |
Silver | <1 | parts per million by weight | ES_SQ |
Cadmium | <50 | parts per million by weight | ES_SQ |
Tin | > 000 | parts per million by weight | ES_SQ |
Antimony | <200 | parts per million by weight | ES_SQ |
Barium | 300 | parts per million by weight | ES_SQ |
Lanthanum | 300 | parts per million by weight | ES_SQ |
Tungsten | <100 | parts per million by weight | ES_SQ |
Gold | <20 | parts per million by weight | ES_SQ |
Lead | 30 | parts per million by weight | ES_SQ |
Bismuth | <20 | parts per million by weight | ES_SQ |
Element | Value | Units | Technique |
---|---|---|---|
Beryllium | 20 | parts per million by weight | ES_SQ |
Boron | L20 | parts per million by weight | ES_SQ |
Magnesium | 0.05 | percent by weight | ES_SQ |
Calcium | 5 | percent by weight | ES_SQ |
Scandium | 30 | parts per million by weight | ES_SQ |
Titanium | 1 | percent by weight | ES_SQ |
Vanadium | 30 | parts per million by weight | ES_SQ |
Chromium | 20 | parts per million by weight | ES_SQ |
Manganese | 0.05 | percent by weight | ES_SQ |
Iron | 0.7 | percent by weight | ES_SQ |
Cobalt | L10 | parts per million by weight | ES_SQ |
Nickel | L10 | parts per million by weight | ES_SQ |
Copper | 300 | parts per million by weight | ES_SQ |
Zinc | N500 | parts per million by weight | ES_SQ |
Arsenic | N500 | parts per million by weight | ES_SQ |
Strontium | L200 | parts per million by weight | ES_SQ |
Yttrium | 500 | parts per million by weight | ES_SQ |
Zirconium | G1000.11 | parts per million by weight | ES_SQ |
Niobium | L50 | parts per million by weight | ES_SQ |
Molybdenum | N10 | parts per million by weight | ES_SQ |
Silver | N1 | parts per million by weight | ES_SQ |
Cadmium | L50 | parts per million by weight | ES_SQ |
Tin | G1000.11 | parts per million by weight | ES_SQ |
Antimony | N200 | parts per million by weight | ES_SQ |
Barium | 300 | parts per million by weight | ES_SQ |
Lanthanum | 300 | parts per million by weight | ES_SQ |
Tungsten | N100 | parts per million by weight | ES_SQ |
Gold | N20 | parts per million by weight | ES_SQ |
Lead | 30 | parts per million by weight | ES_SQ |
Bismuth | N20 | parts per million by weight | ES_SQ |