Field | Value |
---|---|
Lab ID | EHP367 |
Field ID | BI115KN |
Job ID | 73184 |
Sample submitter | Chaffee, Maurice A. |
Date submitted | 9/25/1980 |
State | CA |
Country | United States |
Latitude (WGS84) | 37.4493728 |
Longitude (WGS84) | -118.28427263 |
Original datum | (NAD27) |
Original latitude | 37.44944444 |
Original longitude | -118.28333333 |
Location precision | 1 second |
Primary media type | sediment |
Secondary media type | concentrate |
Sample media name | panned (type undetermined) |
Notes on sample | C |
(click for info) | |
Geologic map unit | -118.28427263, 37.4493728 |
Nearby scientific data | Find additional scientific data near this location |
Element | Measured value | Units of measure | Analytical method |
---|---|---|---|
Beryllium | <2 | parts per million by weight | ES_SQ |
Boron | 100 | parts per million by weight | ES_SQ |
Magnesium | 0.7 | percent by weight | ES_SQ |
Calcium | 5 | percent by weight | ES_SQ |
Scandium | 50 | parts per million by weight | ES_SQ |
Titanium | > 2 | percent by weight | ES_SQ |
Vanadium | 200 | parts per million by weight | ES_SQ |
Chromium | 50 | parts per million by weight | ES_SQ |
Manganese | 0.1 | percent by weight | ES_SQ |
Iron | 1.5 | percent by weight | ES_SQ |
Cobalt | 20 | parts per million by weight | ES_SQ |
Nickel | <10 | parts per million by weight | ES_SQ |
Copper | 20 | parts per million by weight | ES_SQ |
Zinc | <500 | parts per million by weight | ES_SQ |
Arsenic | <500 | parts per million by weight | ES_SQ |
Strontium | 500 | parts per million by weight | ES_SQ |
Yttrium | 500 | parts per million by weight | ES_SQ |
Zirconium | > 2000 | parts per million by weight | ES_SQ |
Niobium | 150 | parts per million by weight | ES_SQ |
Molybdenum | 30 | parts per million by weight | ES_SQ |
Silver | 5 | parts per million by weight | ES_SQ |
Cadmium | <50 | parts per million by weight | ES_SQ |
Tin | 50 | parts per million by weight | ES_SQ |
Antimony | <200 | parts per million by weight | ES_SQ |
Barium | 7000 | parts per million by weight | ES_SQ |
Lanthanum | 500 | parts per million by weight | ES_SQ |
Tungsten | 200 | parts per million by weight | ES_SQ |
Gold | <20 | parts per million by weight | ES_SQ |
Lead | 2000 | parts per million by weight | ES_SQ |
Bismuth | <20 | parts per million by weight | ES_SQ |
Thorium | 700 | parts per million by weight | ES_SQ |
Element | Value | Units | Technique |
---|---|---|---|
Beryllium | N2 | parts per million by weight | ES_SQ |
Boron | 100 | parts per million by weight | ES_SQ |
Magnesium | 0.7 | percent by weight | ES_SQ |
Calcium | 5 | percent by weight | ES_SQ |
Scandium | 50 | parts per million by weight | ES_SQ |
Titanium | G2.11 | percent by weight | ES_SQ |
Vanadium | 200 | parts per million by weight | ES_SQ |
Chromium | 50 | parts per million by weight | ES_SQ |
Manganese | 0.1 | percent by weight | ES_SQ |
Iron | 1.5 | percent by weight | ES_SQ |
Cobalt | 20 | parts per million by weight | ES_SQ |
Nickel | N10 | parts per million by weight | ES_SQ |
Copper | 20 | parts per million by weight | ES_SQ |
Zinc | N500 | parts per million by weight | ES_SQ |
Arsenic | N500 | parts per million by weight | ES_SQ |
Strontium | 500 | parts per million by weight | ES_SQ |
Yttrium | 500 | parts per million by weight | ES_SQ |
Zirconium | G2000.11 | parts per million by weight | ES_SQ |
Niobium | 150 | parts per million by weight | ES_SQ |
Molybdenum | 30 | parts per million by weight | ES_SQ |
Silver | 5 | parts per million by weight | ES_SQ |
Cadmium | N50 | parts per million by weight | ES_SQ |
Tin | 50 | parts per million by weight | ES_SQ |
Antimony | N200 | parts per million by weight | ES_SQ |
Barium | 7000 | parts per million by weight | ES_SQ |
Lanthanum | 500 | parts per million by weight | ES_SQ |
Tungsten | 200 | parts per million by weight | ES_SQ |
Gold | N20 | parts per million by weight | ES_SQ |
Lead | 2000 | parts per million by weight | ES_SQ |
Bismuth | N20 | parts per million by weight | ES_SQ |
Thorium | 700 | parts per million by weight | ES_SQ |