Field | Value |
---|---|
Lab ID | EKC515 |
Field ID | IN005KN |
Job ID | 34292 |
Sample submitter | Chaffee, Maurice A. |
Date submitted | 8/12/1981 |
State | CA |
Country | United States |
Latitude (WGS84) | 36.76826491 |
Longitude (WGS84) | -118.05731182 |
Original datum | (NAD27) |
Original latitude | 36.76833333 |
Original longitude | -118.05638889 |
Location precision | 1 second |
Primary media type | sediment |
Secondary media type | concentrate |
Sample media name | panned (type undetermined) |
Notes on sample | C |
(click for info) | |
Geologic map unit | -118.05731182, 36.76826491 |
Nearby scientific data | Find additional scientific data near this location |
Element | Measured value | Units of measure | Analytical method |
---|---|---|---|
Beryllium | <2 | parts per million by weight | ES_SQ |
Boron | 30 | parts per million by weight | ES_SQ |
Magnesium | 2 | percent by weight | ES_SQ |
Calcium | 5 | percent by weight | ES_SQ |
Scandium | 30 | parts per million by weight | ES_SQ |
Titanium | > 2 | percent by weight | ES_SQ |
Vanadium | 200 | parts per million by weight | ES_SQ |
Chromium | 100 | parts per million by weight | ES_SQ |
Manganese | 0.05 | percent by weight | ES_SQ |
Iron | 1 | percent by weight | ES_SQ |
Cobalt | 10 | parts per million by weight | ES_SQ |
Nickel | <10 | parts per million by weight | ES_SQ |
Copper | 15 | parts per million by weight | ES_SQ |
Zinc | <500 | parts per million by weight | ES_SQ |
Arsenic | <500 | parts per million by weight | ES_SQ |
Strontium | 200 | parts per million by weight | ES_SQ |
Yttrium | 300 | parts per million by weight | ES_SQ |
Zirconium | > 2000 | parts per million by weight | ES_SQ |
Niobium | 200 | parts per million by weight | ES_SQ |
Molybdenum | 20 | parts per million by weight | ES_SQ |
Silver | <1 | parts per million by weight | ES_SQ |
Cadmium | <50 | parts per million by weight | ES_SQ |
Tin | 50 | parts per million by weight | ES_SQ |
Antimony | <200 | parts per million by weight | ES_SQ |
Barium | 700 | parts per million by weight | ES_SQ |
Lanthanum | 700 | parts per million by weight | ES_SQ |
Tungsten | <100 | parts per million by weight | ES_SQ |
Gold | <20 | parts per million by weight | ES_SQ |
Lead | 30 | parts per million by weight | ES_SQ |
Bismuth | <20 | parts per million by weight | ES_SQ |
Thorium | 200 | parts per million by weight | ES_SQ |
Element | Value | Units | Technique |
---|---|---|---|
Beryllium | N2 | parts per million by weight | ES_SQ |
Boron | 30 | parts per million by weight | ES_SQ |
Magnesium | 2 | percent by weight | ES_SQ |
Calcium | 5 | percent by weight | ES_SQ |
Scandium | 30 | parts per million by weight | ES_SQ |
Titanium | G2.11 | percent by weight | ES_SQ |
Vanadium | 200 | parts per million by weight | ES_SQ |
Chromium | 100 | parts per million by weight | ES_SQ |
Manganese | 0.05 | percent by weight | ES_SQ |
Iron | 1 | percent by weight | ES_SQ |
Cobalt | 10 | parts per million by weight | ES_SQ |
Nickel | N10 | parts per million by weight | ES_SQ |
Copper | 15 | parts per million by weight | ES_SQ |
Zinc | N500 | parts per million by weight | ES_SQ |
Arsenic | N500 | parts per million by weight | ES_SQ |
Strontium | 200 | parts per million by weight | ES_SQ |
Yttrium | 300 | parts per million by weight | ES_SQ |
Zirconium | G2000.11 | parts per million by weight | ES_SQ |
Niobium | 200 | parts per million by weight | ES_SQ |
Molybdenum | 20 | parts per million by weight | ES_SQ |
Silver | N1 | parts per million by weight | ES_SQ |
Cadmium | N50 | parts per million by weight | ES_SQ |
Tin | 50 | parts per million by weight | ES_SQ |
Antimony | N200 | parts per million by weight | ES_SQ |
Barium | 700 | parts per million by weight | ES_SQ |
Lanthanum | 700 | parts per million by weight | ES_SQ |
Tungsten | N100 | parts per million by weight | ES_SQ |
Gold | N20 | parts per million by weight | ES_SQ |
Lead | 30 | parts per million by weight | ES_SQ |
Bismuth | N20 | parts per million by weight | ES_SQ |
Thorium | 200 | parts per million by weight | ES_SQ |