Field | Value |
---|---|
Lab ID | ACC805 |
Field ID | 67ARR060B |
Job ID | HM564 |
Sample submitter | Brosge, William P., and Reiser, Hillard N. |
Date submitted | 7/11/1967 |
Project name | E Brooks Range |
State | AK |
Country | United States |
Latitude (WGS84) | 67.49292788 |
Longitude (WGS84) | -150.19529922 |
Original datum | (NAD27) |
Original latitude | 67.49333 |
Original longitude | -150.1925 |
Location precision | 1 second |
Sample source | stream/river |
Primary media type | sediment |
Notes on sample | stream |
Sieve size | -80 mesh |
(click for info) | |
Geologic map unit | -150.19529922, 67.49292788 |
Nearby scientific data | Find additional scientific data near this location |
Element | Measured value | Units of measure | Analytical method |
---|---|---|---|
Beryllium | <1 | parts per million by weight | ES_SQ |
Boron | 100 | parts per million by weight | ES_SQ |
Magnesium | 1 | percent by weight | ES_SQ |
Calcium | 0.7 | percent by weight | ES_SQ |
Scandium | 15 | parts per million by weight | ES_SQ |
Titanium | 0.5 | percent by weight | ES_SQ |
Vanadium | 150 | parts per million by weight | ES_SQ |
Chromium | 70 | parts per million by weight | ES_SQ |
Manganese | 0.1 | percent by weight | ES_SQ |
Iron | 3 | percent by weight | ES_SQ |
Cobalt | 10 | parts per million by weight | ES_SQ |
Nickel | 15 | parts per million by weight | ES_SQ |
Copper | 15 | parts per million by weight | ES_SQ |
Zinc | <200 | parts per million by weight | ES_SQ |
Arsenic | <200 | parts per million by weight | ES_SQ |
Strontium | 150 | parts per million by weight | ES_SQ |
Yttrium | 30 | parts per million by weight | ES_SQ |
Zirconium | 100 | parts per million by weight | ES_SQ |
Niobium | <20 | parts per million by weight | ES_SQ |
Molybdenum | <2 | parts per million by weight | ES_SQ |
Silver | <0.5 | parts per million by weight | ES_SQ |
Cadmium | <20 | parts per million by weight | ES_SQ |
Tin | <10 | parts per million by weight | ES_SQ |
Antimony | 1500 | parts per million by weight | ES_SQ |
Barium | 300 | parts per million by weight | ES_SQ |
Lanthanum | 50 | parts per million by weight | ES_SQ |
Tungsten | <50 | parts per million by weight | ES_SQ |
Gold | <0.02 | parts per million by weight | AA_F_HBr |
Lead | <10 | parts per million by weight | ES_SQ |
Bismuth | <5 | parts per million by weight | ES_SQ |
Element | Value | Units | Technique |
---|---|---|---|
Beryllium | L1 | parts per million by weight | ES_SQ |
Boron | 100 | parts per million by weight | ES_SQ |
Magnesium | 1 | percent by weight | ES_SQ |
Calcium | 0.7 | percent by weight | ES_SQ |
Scandium | 15 | parts per million by weight | ES_SQ |
Titanium | 0.5 | percent by weight | ES_SQ |
Vanadium | 150 | parts per million by weight | ES_SQ |
Chromium | 70 | parts per million by weight | ES_SQ |
Manganese | 0.1 | percent by weight | ES_SQ |
Iron | 3 | percent by weight | ES_SQ |
Cobalt | 10 | parts per million by weight | ES_SQ |
Nickel | 15 | parts per million by weight | ES_SQ |
Copper | 15 | parts per million by weight | ES_SQ |
Copper | 12 | parts per million by weight | AA_F_HNO3_P |
Zinc | 45 | parts per million by weight | AA_F_HNO3_P |
Zinc | L200 | parts per million by weight | ES_SQ |
Arsenic | 30 | parts per million by weight | CM_Acid_P |
Arsenic | L200 | parts per million by weight | ES_SQ |
Strontium | 150 | parts per million by weight | ES_SQ |
Yttrium | 30 | parts per million by weight | ES_SQ |
Zirconium | 100 | parts per million by weight | ES_SQ |
Niobium | L20 | parts per million by weight | ES_SQ |
Molybdenum | L2 | parts per million by weight | ES_SQ |
Silver | 0.2 | parts per million by weight | AA_F_HNO3_P |
Silver | L0.5 | parts per million by weight | ES_SQ |
Cadmium | L20 | parts per million by weight | ES_SQ |
Tin | L10 | parts per million by weight | ES_SQ |
Antimony | 1500 | parts per million by weight | ES_SQ |
Barium | 300 | parts per million by weight | ES_SQ |
Lanthanum | 50 | parts per million by weight | ES_SQ |
Tungsten | L50 | parts per million by weight | ES_SQ |
Gold | L0.02 | parts per million by weight | AA_F_HBr |
Lead | L25 | parts per million by weight | AA_F_HNO3_P |
Lead | L10 | parts per million by weight | ES_SQ |
Bismuth | L5 | parts per million by weight | ES_SQ |