Field | Value |
---|---|
Lab ID | ACF381 |
Field ID | 67AWK070S |
Job ID | HM965 |
Sample submitter | MacKevett, Edward M., Jr., and Smith, James G. |
Date submitted | 7/19/1966 |
Project name | Wrangell Mtns |
State | AK |
Country | United States |
Latitude (WGS84) | 61.40817054 |
Longitude (WGS84) | -142.29400688 |
Original datum | (NAD27) |
Original latitude | 61.40861 |
Original longitude | -142.29195 |
Location precision | 1 second |
Sample source | stream/river |
Primary media type | sediment |
Notes on sample | stream |
Sieve size | -80 mesh |
(click for info) | |
Geologic map unit | -142.29400688, 61.40817054 |
Nearby scientific data | Find additional scientific data near this location |
Element | Measured value | Units of measure | Analytical method |
---|---|---|---|
Beryllium | <1 | parts per million by weight | ES_SQ |
Boron | 50 | parts per million by weight | ES_SQ |
Magnesium | 3 | percent by weight | ES_SQ |
Calcium | 7 | percent by weight | ES_SQ |
Scandium | 50 | parts per million by weight | ES_SQ |
Titanium | 1 | percent by weight | ES_SQ |
Vanadium | 300 | parts per million by weight | ES_SQ |
Chromium | 150 | parts per million by weight | ES_SQ |
Manganese | 0.15 | percent by weight | ES_SQ |
Iron | 10 | percent by weight | ES_SQ |
Cobalt | 30 | parts per million by weight | ES_SQ |
Nickel | 70 | parts per million by weight | ES_SQ |
Copper | 200 | parts per million by weight | ES_SQ |
Zinc | <200 | parts per million by weight | ES_SQ |
Arsenic | <200 | parts per million by weight | ES_SQ |
Strontium | 300 | parts per million by weight | ES_SQ |
Yttrium | 30 | parts per million by weight | ES_SQ |
Zirconium | 150 | parts per million by weight | ES_SQ |
Niobium | 10 | parts per million by weight | ES_SQ |
Molybdenum | <5 | parts per million by weight | ES_SQ |
Silver | <0.5 | parts per million by weight | ES_SQ |
Cadmium | <20 | parts per million by weight | ES_SQ |
Tin | <10 | parts per million by weight | ES_SQ |
Antimony | <100 | parts per million by weight | ES_SQ |
Barium | 500 | parts per million by weight | ES_SQ |
Lanthanum | <20 | parts per million by weight | ES_SQ |
Tungsten | <50 | parts per million by weight | ES_SQ |
Gold | 9.6 | parts per million by weight | AA_F_HBr |
Lead | 15 | parts per million by weight | ES_SQ |
Bismuth | <10 | parts per million by weight | ES_SQ |
Element | Value | Units | Technique |
---|---|---|---|
Beryllium | L1 | parts per million by weight | ES_SQ |
Boron | 50 | parts per million by weight | ES_SQ |
Magnesium | 3 | percent by weight | ES_SQ |
Calcium | 7 | percent by weight | ES_SQ |
Scandium | 50 | parts per million by weight | ES_SQ |
Titanium | 1 | percent by weight | ES_SQ |
Vanadium | 300 | parts per million by weight | ES_SQ |
Chromium | 150 | parts per million by weight | ES_SQ |
Manganese | 0.15 | percent by weight | ES_SQ |
Iron | 10 | percent by weight | ES_SQ |
Cobalt | 30 | parts per million by weight | ES_SQ |
Nickel | 70 | parts per million by weight | ES_SQ |
Copper | 200 | parts per million by weight | ES_SQ |
Zinc | L200 | parts per million by weight | ES_SQ |
Arsenic | N200 | parts per million by weight | ES_SQ |
Strontium | 300 | parts per million by weight | ES_SQ |
Yttrium | 30 | parts per million by weight | ES_SQ |
Zirconium | 150 | parts per million by weight | ES_SQ |
Niobium | 10 | parts per million by weight | ES_SQ |
Molybdenum | N5 | parts per million by weight | ES_SQ |
Silver | N0.5 | parts per million by weight | ES_SQ |
Cadmium | N20 | parts per million by weight | ES_SQ |
Tin | N10 | parts per million by weight | ES_SQ |
Antimony | N100 | parts per million by weight | ES_SQ |
Barium | 500 | parts per million by weight | ES_SQ |
Lanthanum | L20 | parts per million by weight | ES_SQ |
Tungsten | N50 | parts per million by weight | ES_SQ |
Gold | N10 | parts per million by weight | ES_SQ |
Gold | 9.6 | parts per million by weight | AA_F_HBr |
Lead | 15 | parts per million by weight | ES_SQ |
Bismuth | N10 | parts per million by weight | ES_SQ |