Beryllium | 0.28 | parts per million by weight | AES_AR_P |
Beryllium | 1 | parts per million by weight | ES_SQ |
Boron | 30 | parts per million by weight | ES_SQ |
Boron | N0.1 | parts per million by weight | AES_AR_P |
Magnesium | 1.1 | percent by weight | AES_AR_P |
Magnesium | 1.5 | percent by weight | ES_SQ |
Aluminum | 1.9 | percent by weight | AES_AR_P |
Phosphorus | 0.07 | percent by weight | AES_AR_P |
Calcium | 0.52 | percent by weight | AES_AR_P |
Calcium | 1 | percent by weight | ES_SQ |
Scandium | 15 | parts per million by weight | ES_SQ |
Titanium | 0.0088 | percent by weight | AES_AR_P |
Titanium | 0.5 | percent by weight | ES_SQ |
Vanadium | 150 | parts per million by weight | ES_SQ |
Vanadium | 55 | parts per million by weight | AES_AR_P |
Chromium | N2.7 | parts per million by weight | AES_AR_P |
Chromium | 150 | parts per million by weight | ES_SQ |
Manganese | 0.2 | percent by weight | ES_SQ |
Manganese | 0.26 | percent by weight | AES_AR_P |
Iron | 5.4 | percent by weight | AES_AR_P |
Iron | 7 | percent by weight | ES_SQ |
Cobalt | 25 | parts per million by weight | AES_AR_P |
Cobalt | 20 | parts per million by weight | ES_SQ |
Nickel | 29 | parts per million by weight | AES_AR_P |
Nickel | 30 | parts per million by weight | ES_SQ |
Copper | 72 | parts per million by weight | AES_AR_P |
Copper | 50 | parts per million by weight | ES_SQ |
Zinc | 77 | parts per million by weight | AES_AR_P |
Zinc | L200 | parts per million by weight | ES_SQ |
Arsenic | 81 | parts per million by weight | AES_AR_P |
Arsenic | L200 | parts per million by weight | ES_SQ |
Strontium | 48 | parts per million by weight | AES_AR_P |
Strontium | 300 | parts per million by weight | ES_SQ |
Yttrium | N0.04 | parts per million by weight | AES_AR_P |
Yttrium | 15 | parts per million by weight | ES_SQ |
Zirconium | N1 | parts per million by weight | AES_AR_P |
Zirconium | 70 | parts per million by weight | ES_SQ |
Niobium | 10 | parts per million by weight | ES_SQ |
Niobium | N1 | parts per million by weight | AES_AR_P |
Molybdenum | L5 | parts per million by weight | ES_SQ |
Molybdenum | N0.4 | parts per million by weight | AES_AR_P |
Silver | N0.5 | parts per million by weight | ES_SQ |
Silver | N0.3 | parts per million by weight | AES_AR_P |
Cadmium | N0.4 | parts per million by weight | AES_AR_P |
Cadmium | N20 | parts per million by weight | ES_SQ |
Tin | N4 | parts per million by weight | AES_AR_P |
Tin | N10 | parts per million by weight | ES_SQ |
Antimony | N100 | parts per million by weight | ES_SQ |
Antimony | N5 | parts per million by weight | AES_AR_P |
Barium | 500 | parts per million by weight | ES_SQ |
Barium | 95 | parts per million by weight | AES_AR_P |
Lanthanum | 6.7 | parts per million by weight | AES_AR_P |
Lanthanum | 20 | parts per million by weight | ES_SQ |
Cerium | 12 | parts per million by weight | AES_AR_P |
Tungsten | N5 | parts per million by weight | AES_AR_P |
Tungsten | N50 | parts per million by weight | ES_SQ |
Gold | N10 | parts per million by weight | ES_SQ |
Gold | 0.06 | parts per million by weight | AA_F_HBr |
Lead | 15 | parts per million by weight | ES_SQ |
Lead | L14 | parts per million by weight | AES_AR_P |
Bismuth | N8 | parts per million by weight | AES_AR_P |
Bismuth | N10 | parts per million by weight | ES_SQ |