Beryllium | 0.31 | parts per million by weight | AES_AR_P |
Beryllium | L1 | parts per million by weight | ES_SQ |
Boron | N0.1 | parts per million by weight | AES_AR_P |
Boron | 50 | parts per million by weight | ES_SQ |
Magnesium | 1.3 | percent by weight | AES_AR_P |
Magnesium | 2 | percent by weight | ES_SQ |
Aluminum | 2.1 | percent by weight | AES_AR_P |
Phosphorus | 0.08 | percent by weight | AES_AR_P |
Calcium | 0.64 | percent by weight | AES_AR_P |
Calcium | 1.5 | percent by weight | ES_SQ |
Scandium | 20 | parts per million by weight | ES_SQ |
Titanium | 0.01 | percent by weight | AES_AR_P |
Titanium | 0.7 | percent by weight | ES_SQ |
Vanadium | 58 | parts per million by weight | AES_AR_P |
Vanadium | 200 | parts per million by weight | ES_SQ |
Chromium | 100 | parts per million by weight | ES_SQ |
Chromium | N2.7 | parts per million by weight | AES_AR_P |
Manganese | 0.2 | percent by weight | AES_AR_P |
Manganese | 0.15 | percent by weight | ES_SQ |
Iron | 7.5 | percent by weight | AES_AR_P |
Iron | 10 | percent by weight | ES_SQ |
Cobalt | 32 | parts per million by weight | AES_AR_P |
Cobalt | 20 | parts per million by weight | ES_SQ |
Nickel | 70 | parts per million by weight | ES_SQ |
Nickel | 50 | parts per million by weight | AES_AR_P |
Copper | 150 | parts per million by weight | ES_SQ |
Copper | 150 | parts per million by weight | AES_AR_P |
Zinc | 110 | parts per million by weight | AES_AR_P |
Zinc | 200 | parts per million by weight | ES_SQ |
Arsenic | N5 | parts per million by weight | AES_AR_P |
Arsenic | N200 | parts per million by weight | ES_SQ |
Strontium | 48 | parts per million by weight | AES_AR_P |
Strontium | 300 | parts per million by weight | ES_SQ |
Yttrium | N0.04 | parts per million by weight | AES_AR_P |
Yttrium | 15 | parts per million by weight | ES_SQ |
Zirconium | N1 | parts per million by weight | AES_AR_P |
Zirconium | 150 | parts per million by weight | ES_SQ |
Niobium | N1 | parts per million by weight | AES_AR_P |
Niobium | 10 | parts per million by weight | ES_SQ |
Molybdenum | N0.4 | parts per million by weight | AES_AR_P |
Molybdenum | L5 | parts per million by weight | ES_SQ |
Silver | N0.3 | parts per million by weight | AES_AR_P |
Silver | N0.5 | parts per million by weight | ES_SQ |
Cadmium | N0.4 | parts per million by weight | AES_AR_P |
Cadmium | N20 | parts per million by weight | ES_SQ |
Tin | N10 | parts per million by weight | ES_SQ |
Tin | N4 | parts per million by weight | AES_AR_P |
Antimony | N5 | parts per million by weight | AES_AR_P |
Antimony | N100 | parts per million by weight | ES_SQ |
Barium | 86 | parts per million by weight | AES_AR_P |
Barium | 700 | parts per million by weight | ES_SQ |
Lanthanum | 8.4 | parts per million by weight | AES_AR_P |
Lanthanum | 30 | parts per million by weight | ES_SQ |
Cerium | 14 | parts per million by weight | AES_AR_P |
Tungsten | N5 | parts per million by weight | AES_AR_P |
Tungsten | N50 | parts per million by weight | ES_SQ |
Gold | N10 | parts per million by weight | ES_SQ |
Gold | 0.04 | parts per million by weight | AA_F_HBr |
Lead | L16 | parts per million by weight | AES_AR_P |
Lead | 10 | parts per million by weight | ES_SQ |
Bismuth | N10 | parts per million by weight | ES_SQ |
Bismuth | N8 | parts per million by weight | AES_AR_P |