Beryllium | 0.38 | parts per million by weight | AES_AR_P |
Beryllium | L1 | parts per million by weight | ES_SQ |
Boron | N0.5 | parts per million by weight | AES_AR_P |
Boron | 30 | parts per million by weight | ES_SQ |
Magnesium | 0.85 | percent by weight | AES_AR_P |
Magnesium | 3 | percent by weight | ES_SQ |
Aluminum | 1.8 | percent by weight | AES_AR_P |
Phosphorus | 0.14 | percent by weight | AES_AR_P |
Calcium | 0.44 | percent by weight | AES_AR_P |
Calcium | 2 | percent by weight | ES_SQ |
Scandium | 15 | parts per million by weight | ES_SQ |
Titanium | 0.05 | percent by weight | AES_AR_P |
Titanium | 0.3 | percent by weight | ES_SQ |
Vanadium | 86 | parts per million by weight | AES_AR_P |
Vanadium | 150 | parts per million by weight | ES_SQ |
Chromium | L20 | parts per million by weight | AES_AR_P |
Chromium | 150 | parts per million by weight | ES_SQ |
Manganese | 0.61 | percent by weight | AES_AR_P |
Manganese | 0.3 | percent by weight | ES_SQ |
Iron | 5.5 | percent by weight | AES_AR_P |
Iron | 5 | percent by weight | ES_SQ |
Cobalt | 29 | parts per million by weight | AES_AR_P |
Cobalt | 30 | parts per million by weight | ES_SQ |
Nickel | 53 | parts per million by weight | AES_AR_P |
Nickel | 50 | parts per million by weight | ES_SQ |
Copper | 36 | parts per million by weight | AES_AR_P |
Copper | 15 | parts per million by weight | ES_SQ |
Zinc | 88 | parts per million by weight | AES_AR_P |
Zinc | L200 | parts per million by weight | ES_SQ |
Arsenic | L34 | parts per million by weight | AES_AR_P |
Arsenic | N200 | parts per million by weight | ES_SQ |
Strontium | 52 | parts per million by weight | AES_AR_P |
Strontium | 300 | parts per million by weight | ES_SQ |
Yttrium | N0.2 | parts per million by weight | AES_AR_P |
Yttrium | 15 | parts per million by weight | ES_SQ |
Zirconium | 100 | parts per million by weight | ES_SQ |
Zirconium | N1 | parts per million by weight | AES_AR_P |
Niobium | N5 | parts per million by weight | AES_AR_P |
Niobium | L10 | parts per million by weight | ES_SQ |
Molybdenum | N2 | parts per million by weight | AES_AR_P |
Molybdenum | N5 | parts per million by weight | ES_SQ |
Silver | N1.5 | parts per million by weight | AES_AR_P |
Silver | N0.5 | parts per million by weight | ES_SQ |
Cadmium | N1 | parts per million by weight | AES_AR_P |
Cadmium | N20 | parts per million by weight | ES_SQ |
Tin | N10 | parts per million by weight | AES_AR_P |
Tin | N10 | parts per million by weight | ES_SQ |
Antimony | N13 | parts per million by weight | AES_AR_P |
Antimony | N100 | parts per million by weight | ES_SQ |
Barium | 150 | parts per million by weight | AES_AR_P |
Barium | 700 | parts per million by weight | ES_SQ |
Lanthanum | 5.2 | parts per million by weight | AES_AR_P |
Lanthanum | 20 | parts per million by weight | ES_SQ |
Cerium | 7.8 | parts per million by weight | AES_AR_P |
Tungsten | N50 | parts per million by weight | ES_SQ |
Tungsten | N15 | parts per million by weight | AES_AR_P |
Gold | N10 | parts per million by weight | ES_SQ |
Gold | L0.02 | parts per million by weight | AA_F_HBr |
Lead | 46 | parts per million by weight | AES_AR_P |
Lead | 15 | parts per million by weight | ES_SQ |
Bismuth | N40 | parts per million by weight | AES_AR_P |
Bismuth | N10 | parts per million by weight | ES_SQ |