Beryllium | 0.37 | parts per million by weight | AES_AR_P |
Beryllium | L1 | parts per million by weight | ES_SQ |
Boron | N0.1 | parts per million by weight | AES_AR_P |
Boron | 30 | parts per million by weight | ES_SQ |
Magnesium | 1.1 | percent by weight | AES_AR_P |
Magnesium | 3 | percent by weight | ES_SQ |
Aluminum | 2.1 | percent by weight | AES_AR_P |
Phosphorus | 0.1 | percent by weight | AES_AR_P |
Calcium | 0.47 | percent by weight | AES_AR_P |
Calcium | 2 | percent by weight | ES_SQ |
Scandium | 15 | parts per million by weight | ES_SQ |
Titanium | 0.05 | percent by weight | AES_AR_P |
Titanium | 0.3 | percent by weight | ES_SQ |
Vanadium | 73 | parts per million by weight | AES_AR_P |
Vanadium | 100 | parts per million by weight | ES_SQ |
Chromium | 29 | parts per million by weight | AES_AR_P |
Chromium | 300 | parts per million by weight | ES_SQ |
Manganese | 0.24 | percent by weight | AES_AR_P |
Manganese | 0.2 | percent by weight | ES_SQ |
Iron | 4.1 | percent by weight | AES_AR_P |
Iron | 5 | percent by weight | ES_SQ |
Cobalt | 17 | parts per million by weight | AES_AR_P |
Cobalt | 15 | parts per million by weight | ES_SQ |
Nickel | 55 | parts per million by weight | AES_AR_P |
Nickel | 50 | parts per million by weight | ES_SQ |
Copper | 28 | parts per million by weight | AES_AR_P |
Copper | 30 | parts per million by weight | ES_SQ |
Zinc | 66 | parts per million by weight | AES_AR_P |
Zinc | N200 | parts per million by weight | ES_SQ |
Arsenic | N5 | parts per million by weight | AES_AR_P |
Arsenic | N200 | parts per million by weight | ES_SQ |
Strontium | 55 | parts per million by weight | AES_AR_P |
Strontium | 300 | parts per million by weight | ES_SQ |
Yttrium | 1.2 | parts per million by weight | AES_AR_P |
Yttrium | 15 | parts per million by weight | ES_SQ |
Zirconium | 70 | parts per million by weight | ES_SQ |
Zirconium | N1 | parts per million by weight | AES_AR_P |
Niobium | L10 | parts per million by weight | ES_SQ |
Niobium | N1 | parts per million by weight | AES_AR_P |
Molybdenum | N5 | parts per million by weight | ES_SQ |
Molybdenum | N0.4 | parts per million by weight | AES_AR_P |
Silver | N0.3 | parts per million by weight | AES_AR_P |
Silver | N0.5 | parts per million by weight | ES_SQ |
Cadmium | N0.4 | parts per million by weight | AES_AR_P |
Cadmium | N20 | parts per million by weight | ES_SQ |
Tin | N4 | parts per million by weight | AES_AR_P |
Tin | N10 | parts per million by weight | ES_SQ |
Antimony | N5 | parts per million by weight | AES_AR_P |
Antimony | N100 | parts per million by weight | ES_SQ |
Barium | 1000 | parts per million by weight | ES_SQ |
Barium | 130 | parts per million by weight | AES_AR_P |
Lanthanum | 7.3 | parts per million by weight | AES_AR_P |
Lanthanum | 20 | parts per million by weight | ES_SQ |
Cerium | 12 | parts per million by weight | AES_AR_P |
Tungsten | N50 | parts per million by weight | ES_SQ |
Tungsten | N5 | parts per million by weight | AES_AR_P |
Gold | N10 | parts per million by weight | ES_SQ |
Gold | L0.02 | parts per million by weight | AA_F_HBr |
Lead | L11 | parts per million by weight | AES_AR_P |
Lead | 15 | parts per million by weight | ES_SQ |
Bismuth | N8 | parts per million by weight | AES_AR_P |
Bismuth | N10 | parts per million by weight | ES_SQ |