Beryllium | 0.37 | parts per million by weight | AES_AR_P |
Beryllium | 2 | parts per million by weight | ES_SQ |
Boron | N0.1 | parts per million by weight | AES_AR_P |
Boron | 30 | parts per million by weight | ES_SQ |
Magnesium | 1.4 | percent by weight | AES_AR_P |
Magnesium | 3 | percent by weight | ES_SQ |
Aluminum | 1.7 | percent by weight | AES_AR_P |
Phosphorus | 0.13 | percent by weight | AES_AR_P |
Calcium | 0.35 | percent by weight | AES_AR_P |
Calcium | 3 | percent by weight | ES_SQ |
Scandium | 30 | parts per million by weight | ES_SQ |
Titanium | 0.08 | percent by weight | AES_AR_P |
Titanium | 1 | percent by weight | ES_SQ |
Vanadium | 85 | parts per million by weight | AES_AR_P |
Vanadium | 200 | parts per million by weight | ES_SQ |
Chromium | 150 | parts per million by weight | ES_SQ |
Chromium | L15 | parts per million by weight | AES_AR_P |
Manganese | 0.04 | percent by weight | AES_AR_P |
Manganese | 0.1 | percent by weight | ES_SQ |
Iron | 4.3 | percent by weight | AES_AR_P |
Iron | 7 | percent by weight | ES_SQ |
Cobalt | 15 | parts per million by weight | AES_AR_P |
Cobalt | 30 | parts per million by weight | ES_SQ |
Nickel | 70 | parts per million by weight | ES_SQ |
Nickel | 37 | parts per million by weight | AES_AR_P |
Copper | 100 | parts per million by weight | ES_SQ |
Copper | 78 | parts per million by weight | AES_AR_P |
Zinc | 120 | parts per million by weight | AES_AR_P |
Zinc | 300 | parts per million by weight | ES_SQ |
Arsenic | N5 | parts per million by weight | AES_AR_P |
Arsenic | N200 | parts per million by weight | ES_SQ |
Strontium | 500 | parts per million by weight | ES_SQ |
Strontium | 24 | parts per million by weight | AES_AR_P |
Yttrium | 2 | parts per million by weight | AES_AR_P |
Yttrium | 30 | parts per million by weight | ES_SQ |
Zirconium | N1 | parts per million by weight | AES_AR_P |
Zirconium | 70 | parts per million by weight | ES_SQ |
Niobium | N1 | parts per million by weight | AES_AR_P |
Niobium | 10 | parts per million by weight | ES_SQ |
Molybdenum | N0.4 | parts per million by weight | AES_AR_P |
Molybdenum | L5 | parts per million by weight | ES_SQ |
Silver | N0.3 | parts per million by weight | AES_AR_P |
Silver | L0.5 | parts per million by weight | ES_SQ |
Cadmium | N0.4 | parts per million by weight | AES_AR_P |
Cadmium | N20 | parts per million by weight | ES_SQ |
Tin | N4 | parts per million by weight | AES_AR_P |
Tin | N10 | parts per million by weight | ES_SQ |
Antimony | N100 | parts per million by weight | ES_SQ |
Antimony | N5 | parts per million by weight | AES_AR_P |
Barium | 100 | parts per million by weight | AES_AR_P |
Barium | 1500 | parts per million by weight | ES_SQ |
Lanthanum | 7.4 | parts per million by weight | AES_AR_P |
Lanthanum | 30 | parts per million by weight | ES_SQ |
Cerium | 9.7 | parts per million by weight | AES_AR_P |
Tungsten | N5 | parts per million by weight | AES_AR_P |
Tungsten | N50 | parts per million by weight | ES_SQ |
Gold | N10 | parts per million by weight | ES_SQ |
Gold | 0.04 | parts per million by weight | AA_F_HBr |
Lead | 19 | parts per million by weight | AES_AR_P |
Lead | 30 | parts per million by weight | ES_SQ |
Bismuth | N10 | parts per million by weight | ES_SQ |
Bismuth | N8 | parts per million by weight | AES_AR_P |