Beryllium | 0.48 | parts per million by weight | AES_AR_P |
Beryllium | 1 | parts per million by weight | ES_SQ |
Boron | 50 | parts per million by weight | ES_SQ |
Boron | N0.1 | parts per million by weight | AES_AR_P |
Magnesium | 1.2 | percent by weight | AES_AR_P |
Magnesium | 2 | percent by weight | ES_SQ |
Aluminum | 2 | percent by weight | AES_AR_P |
Phosphorus | 0.08 | percent by weight | AES_AR_P |
Calcium | 0.94 | percent by weight | AES_AR_P |
Calcium | 1.5 | percent by weight | ES_SQ |
Scandium | 20 | parts per million by weight | ES_SQ |
Titanium | 0.06 | percent by weight | AES_AR_P |
Titanium | 0.7 | percent by weight | ES_SQ |
Vanadium | 65 | parts per million by weight | AES_AR_P |
Vanadium | 200 | parts per million by weight | ES_SQ |
Chromium | N2.7 | parts per million by weight | AES_AR_P |
Chromium | 150 | parts per million by weight | ES_SQ |
Manganese | 0.08 | percent by weight | AES_AR_P |
Manganese | 0.07 | percent by weight | ES_SQ |
Iron | 5.9 | percent by weight | AES_AR_P |
Iron | 10 | percent by weight | ES_SQ |
Cobalt | 20 | parts per million by weight | ES_SQ |
Cobalt | 17 | parts per million by weight | AES_AR_P |
Nickel | 53 | parts per million by weight | AES_AR_P |
Nickel | 100 | parts per million by weight | ES_SQ |
Copper | 170 | parts per million by weight | AES_AR_P |
Copper | 150 | parts per million by weight | ES_SQ |
Zinc | 630 | parts per million by weight | AES_AR_P |
Zinc | 700 | parts per million by weight | ES_SQ |
Arsenic | 120 | parts per million by weight | AES_AR_P |
Arsenic | 200 | parts per million by weight | ES_SQ |
Strontium | 61 | parts per million by weight | AES_AR_P |
Strontium | 150 | parts per million by weight | ES_SQ |
Yttrium | 0.62 | parts per million by weight | AES_AR_P |
Yttrium | 30 | parts per million by weight | ES_SQ |
Zirconium | N1 | parts per million by weight | AES_AR_P |
Zirconium | 100 | parts per million by weight | ES_SQ |
Niobium | N1 | parts per million by weight | AES_AR_P |
Niobium | 10 | parts per million by weight | ES_SQ |
Molybdenum | L0.58 | parts per million by weight | AES_AR_P |
Molybdenum | 5 | parts per million by weight | ES_SQ |
Silver | 7.1 | parts per million by weight | AES_AR_P |
Silver | 3 | parts per million by weight | ES_SQ |
Cadmium | N20 | parts per million by weight | ES_SQ |
Cadmium | 4.8 | parts per million by weight | AES_AR_P |
Tin | 29 | parts per million by weight | AES_AR_P |
Tin | 100 | parts per million by weight | ES_SQ |
Antimony | N5 | parts per million by weight | AES_AR_P |
Antimony | N100 | parts per million by weight | ES_SQ |
Barium | 31 | parts per million by weight | AES_AR_P |
Barium | 2000 | parts per million by weight | ES_SQ |
Lanthanum | 9.1 | parts per million by weight | AES_AR_P |
Lanthanum | 30 | parts per million by weight | ES_SQ |
Cerium | 9.3 | parts per million by weight | AES_AR_P |
Tungsten | N5 | parts per million by weight | AES_AR_P |
Tungsten | N50 | parts per million by weight | ES_SQ |
Gold | N10 | parts per million by weight | ES_SQ |
Gold | 3.8 | parts per million by weight | AA_F_HBr |
Lead | 740 | parts per million by weight | AES_AR_P |
Lead | 1000 | parts per million by weight | ES_SQ |
Bismuth | N8 | parts per million by weight | AES_AR_P |
Bismuth | N10 | parts per million by weight | ES_SQ |