Beryllium | 1.5 | parts per million by weight | ES_SQ |
Beryllium | 0.47 | parts per million by weight | AES_AR_P |
Boron | N0.1 | parts per million by weight | AES_AR_P |
Boron | 10 | parts per million by weight | ES_SQ |
Magnesium | 1.6 | percent by weight | AES_AR_P |
Magnesium | 3 | percent by weight | ES_SQ |
Aluminum | 2.7 | percent by weight | AES_AR_P |
Phosphorus | 0.14 | percent by weight | AES_AR_P |
Calcium | 0.36 | percent by weight | AES_AR_P |
Calcium | 2 | percent by weight | ES_SQ |
Scandium | 30 | parts per million by weight | ES_SQ |
Titanium | 0.22 | percent by weight | AES_AR_P |
Titanium | 1 | percent by weight | ES_SQ |
Vanadium | 110 | parts per million by weight | AES_AR_P |
Vanadium | 150 | parts per million by weight | ES_SQ |
Chromium | 150 | parts per million by weight | ES_SQ |
Chromium | L27 | parts per million by weight | AES_AR_P |
Manganese | 0.06 | percent by weight | AES_AR_P |
Manganese | 0.1 | percent by weight | ES_SQ |
Iron | 5.8 | percent by weight | AES_AR_P |
Iron | 10 | percent by weight | ES_SQ |
Cobalt | 19 | parts per million by weight | AES_AR_P |
Cobalt | 20 | parts per million by weight | ES_SQ |
Nickel | 50 | parts per million by weight | ES_SQ |
Nickel | 31 | parts per million by weight | AES_AR_P |
Copper | 70 | parts per million by weight | ES_SQ |
Copper | 84 | parts per million by weight | AES_AR_P |
Zinc | 98 | parts per million by weight | AES_AR_P |
Zinc | L200 | parts per million by weight | ES_SQ |
Arsenic | N200 | parts per million by weight | ES_SQ |
Arsenic | N5 | parts per million by weight | AES_AR_P |
Strontium | 20 | parts per million by weight | AES_AR_P |
Strontium | 500 | parts per million by weight | ES_SQ |
Yttrium | 5 | parts per million by weight | AES_AR_P |
Yttrium | 30 | parts per million by weight | ES_SQ |
Zirconium | N1 | parts per million by weight | AES_AR_P |
Zirconium | 70 | parts per million by weight | ES_SQ |
Niobium | L10 | parts per million by weight | ES_SQ |
Niobium | N1 | parts per million by weight | AES_AR_P |
Molybdenum | N0.4 | parts per million by weight | AES_AR_P |
Molybdenum | N5 | parts per million by weight | ES_SQ |
Silver | N0.3 | parts per million by weight | AES_AR_P |
Silver | N0.5 | parts per million by weight | ES_SQ |
Cadmium | N0.4 | parts per million by weight | AES_AR_P |
Cadmium | N20 | parts per million by weight | ES_SQ |
Tin | N200 | parts per million by weight | ES_SQ |
Tin | N4 | parts per million by weight | AES_AR_P |
Antimony | N100 | parts per million by weight | ES_SQ |
Antimony | N5 | parts per million by weight | AES_AR_P |
Barium | N0.2 | parts per million by weight | AES_AR_P |
Barium | 700 | parts per million by weight | ES_SQ |
Lanthanum | 8.1 | parts per million by weight | AES_AR_P |
Lanthanum | 70 | parts per million by weight | ES_SQ |
Cerium | 9.1 | parts per million by weight | AES_AR_P |
Tungsten | N5 | parts per million by weight | AES_AR_P |
Tungsten | N50 | parts per million by weight | ES_SQ |
Gold | N10 | parts per million by weight | ES_SQ |
Gold | L0.02 | parts per million by weight | AA_F_HBr |
Lead | 10 | parts per million by weight | ES_SQ |
Lead | N2.4 | parts per million by weight | AES_AR_P |
Bismuth | N8 | parts per million by weight | AES_AR_P |
Bismuth | N10 | parts per million by weight | ES_SQ |