Field | Value |
---|---|
Lab ID | BAT215 |
Field ID | HID6-06 |
Job ID | HM5486 |
Sample submitter | Clark, Allen L. |
Date submitted | 6/28/1971 |
Project name | SW Alaska |
State | AK |
Country | United States |
Latitude (WGS84) | 58.9703047 |
Longitude (WGS84) | -161.75864605 |
Original datum | (NAD27) |
Original latitude | 58.97111 |
Original longitude | -161.75639 |
Location precision | 1 second |
Sample source | stream/river |
Primary media type | sediment |
Notes on sample | stream |
Sieve size | -80 mesh |
(click for info) | |
Geologic map unit | -161.75864605, 58.9703047 |
Nearby scientific data | Find additional scientific data near this location |
Element | Measured value | Units of measure | Analytical method |
---|---|---|---|
Beryllium | <1 | parts per million by weight | ES_SQ |
Boron | 10 | parts per million by weight | ES_SQ |
Magnesium | 10 | percent by weight | ES_SQ |
Calcium | 0.7 | percent by weight | ES_SQ |
Scandium | 20 | parts per million by weight | ES_SQ |
Titanium | 0.2 | percent by weight | ES_SQ |
Vanadium | 150 | parts per million by weight | ES_SQ |
Chromium | 3000 | parts per million by weight | ES_SQ |
Manganese | 0.2 | percent by weight | ES_SQ |
Iron | 15 | percent by weight | ES_SQ |
Cobalt | 200 | parts per million by weight | ES_SQ |
Nickel | 1500 | parts per million by weight | ES_SQ |
Copper | 70 | parts per million by weight | ES_SQ |
Zinc | <200 | parts per million by weight | ES_SQ |
Arsenic | <200 | parts per million by weight | ES_SQ |
Strontium | <100 | parts per million by weight | ES_SQ |
Yttrium | 15 | parts per million by weight | ES_SQ |
Zirconium | 70 | parts per million by weight | ES_SQ |
Niobium | <10 | parts per million by weight | ES_SQ |
Molybdenum | <5 | parts per million by weight | ES_SQ |
Silver | <0.5 | parts per million by weight | ES_SQ |
Cadmium | <20 | parts per million by weight | ES_SQ |
Tin | <10 | parts per million by weight | ES_SQ |
Antimony | <100 | parts per million by weight | ES_SQ |
Barium | 150 | parts per million by weight | ES_SQ |
Lanthanum | <20 | parts per million by weight | ES_SQ |
Tungsten | <50 | parts per million by weight | ES_SQ |
Gold | <0.02 | parts per million by weight | AA_F_HBr |
Mercury | 1.1 | parts per million by weight | AA_TR |
Lead | 10 | parts per million by weight | ES_SQ |
Bismuth | <10 | parts per million by weight | ES_SQ |
Element | Value | Units | Technique |
---|---|---|---|
Beryllium | N1 | parts per million by weight | ES_SQ |
Boron | 10 | parts per million by weight | ES_SQ |
Magnesium | 10 | percent by weight | ES_SQ |
Calcium | 0.7 | percent by weight | ES_SQ |
Scandium | 20 | parts per million by weight | ES_SQ |
Titanium | 0.2 | percent by weight | ES_SQ |
Vanadium | 150 | parts per million by weight | ES_SQ |
Chromium | 3000 | parts per million by weight | ES_SQ |
Manganese | 0.2 | percent by weight | ES_SQ |
Iron | 15 | percent by weight | ES_SQ |
Cobalt | 200 | parts per million by weight | ES_SQ |
Nickel | 1500 | parts per million by weight | ES_SQ |
Copper | 70 | parts per million by weight | ES_SQ |
Zinc | N200 | parts per million by weight | ES_SQ |
Arsenic | N200 | parts per million by weight | ES_SQ |
Strontium | L100 | parts per million by weight | ES_SQ |
Yttrium | 15 | parts per million by weight | ES_SQ |
Zirconium | 70 | parts per million by weight | ES_SQ |
Niobium | L10 | parts per million by weight | ES_SQ |
Molybdenum | L5 | parts per million by weight | ES_SQ |
Silver | N0.5 | parts per million by weight | ES_SQ |
Cadmium | N20 | parts per million by weight | ES_SQ |
Tin | N10 | parts per million by weight | ES_SQ |
Antimony | N100 | parts per million by weight | ES_SQ |
Barium | 150 | parts per million by weight | ES_SQ |
Lanthanum | N20 | parts per million by weight | ES_SQ |
Tungsten | N50 | parts per million by weight | ES_SQ |
Gold | N10 | parts per million by weight | ES_SQ |
Gold | L0.02 | parts per million by weight | AA_F_HBr |
Mercury | 1.1 | parts per million by weight | AA_TR |
Lead | 10 | parts per million by weight | ES_SQ |
Bismuth | N10 | parts per million by weight | ES_SQ |