Field | Value |
---|---|
Lab ID | BEB408 |
Field ID | WCE0057 |
Job ID | HM3515 |
Sample submitter | Seeland, David A. |
Date submitted | 7/23/1971 |
State | ID |
Country | United States |
Latitude (WGS84) | 44.17130146 |
Longitude (WGS84) | -114.6381256 |
Original datum | (NAD27) |
Original latitude | 44.17138889 |
Original longitude | -114.63722222 |
Location precision | 1 second |
Description of location | Custer Co. |
Sample source | stream/river |
Collection method | single/grab |
Primary media type | sediment |
Notes on sample | SD; stream |
Geologic age | holocene |
Sieve size | -80 mesh |
(click for info) | |
Geologic map unit | -114.6381256, 44.17130146 |
Nearby scientific data | Find additional scientific data near this location |
Element | Measured value | Units of measure | Analytical method |
---|---|---|---|
Beryllium | <1 | parts per million by weight | ES_SQ |
Boron | 30 | parts per million by weight | ES_SQ |
Magnesium | 1 | percent by weight | ES_SQ |
Calcium | 3 | percent by weight | ES_SQ |
Scandium | 5 | parts per million by weight | ES_SQ |
Titanium | 0.1 | percent by weight | ES_SQ |
Vanadium | 70 | parts per million by weight | ES_SQ |
Chromium | 20 | parts per million by weight | ES_SQ |
Manganese | 0.02 | percent by weight | ES_SQ |
Iron | 2 | percent by weight | ES_SQ |
Cobalt | 5 | parts per million by weight | ES_SQ |
Nickel | 30 | parts per million by weight | ES_SQ |
Copper | 15 | parts per million by weight | ES_SQ |
Zinc | 7000 | parts per million by weight | ES_SQ |
Arsenic | <200 | parts per million by weight | ES_SQ |
Strontium | 100 | parts per million by weight | ES_SQ |
Yttrium | 10 | parts per million by weight | ES_SQ |
Zirconium | 200 | parts per million by weight | ES_SQ |
Niobium | <10 | parts per million by weight | ES_SQ |
Molybdenum | <5 | parts per million by weight | ES_SQ |
Silver | 0.7 | parts per million by weight | ES_SQ |
Cadmium | 70 | parts per million by weight | ES_SQ |
Tin | <10 | parts per million by weight | ES_SQ |
Antimony | <100 | parts per million by weight | ES_SQ |
Barium | 700 | parts per million by weight | ES_SQ |
Lanthanum | 20 | parts per million by weight | ES_SQ |
Tungsten | <50 | parts per million by weight | ES_SQ |
Gold | <0.02 | parts per million by weight | AA_F_HBr |
Lead | 150 | parts per million by weight | ES_SQ |
Bismuth | <10 | parts per million by weight | ES_SQ |
Element | Value | Units | Technique |
---|---|---|---|
Beryllium | L1 | parts per million by weight | ES_SQ |
Boron | 30 | parts per million by weight | ES_SQ |
Magnesium | 1 | percent by weight | ES_SQ |
Calcium | 3 | percent by weight | ES_SQ |
Scandium | 5 | parts per million by weight | ES_SQ |
Titanium | 0.1 | percent by weight | ES_SQ |
Vanadium | 70 | parts per million by weight | ES_SQ |
Chromium | 20 | parts per million by weight | ES_SQ |
Manganese | 0.02 | percent by weight | ES_SQ |
Iron | 2 | percent by weight | ES_SQ |
Cobalt | 5 | parts per million by weight | ES_SQ |
Nickel | 30 | parts per million by weight | ES_SQ |
Copper | 15 | parts per million by weight | ES_SQ |
Copper | 25 | parts per million by weight | AA_F_HNO3_P |
Zinc | 40000 | parts per million by weight | AA_F_HNO3_P |
Zinc | 7000 | parts per million by weight | ES_SQ |
Arsenic | N200 | parts per million by weight | ES_SQ |
Strontium | 100 | parts per million by weight | ES_SQ |
Yttrium | 10 | parts per million by weight | ES_SQ |
Zirconium | 200 | parts per million by weight | ES_SQ |
Niobium | N10 | parts per million by weight | ES_SQ |
Molybdenum | 4 | parts per million by weight | CM_Fuse_P |
Molybdenum | N5 | parts per million by weight | ES_SQ |
Silver | 1.5 | parts per million by weight | AA_F_HNO3_P |
Silver | 0.7 | parts per million by weight | ES_SQ |
Cadmium | 70 | parts per million by weight | ES_SQ |
Tin | N10 | parts per million by weight | ES_SQ |
Antimony | 20 | parts per million by weight | CM_Fuse_P |
Antimony | N100 | parts per million by weight | ES_SQ |
Barium | 700 | parts per million by weight | ES_SQ |
Lanthanum | 20 | parts per million by weight | ES_SQ |
Tungsten | N20 | parts per million by weight | CM_ST_P |
Tungsten | L50 | parts per million by weight | ES_SQ |
Gold | L0.02 | parts per million by weight | AA_F_HBr |
Gold | N10 | parts per million by weight | ES_SQ |
Lead | 400 | parts per million by weight | AA_F_HNO3_P |
Lead | 150 | parts per million by weight | ES_SQ |
Bismuth | N10 | parts per million by weight | ES_SQ |