Field | Value |
---|---|
Lab ID | C168080 |
Field ID | 443247 |
Job ID | MRP02426 |
Sample submitter | Grosz, Andrew E. |
Date submitted | 3/24/2000 |
Project name | Regional Survey & Analysis |
State | AK |
Country | United States |
Latitude (WGS84) | 61.24983458 |
Longitude (WGS84) | -142.30621351 |
Original datum | (NAD27) |
Original latitude | 61.25027778 |
Original longitude | -142.30416667 |
Location precision | 1 second |
Sample source | surface |
Collection method | single/grab |
Primary media type | sediment |
(click for info) | |
Geologic map unit | -142.30621351, 61.24983458 |
Nearby scientific data | Find additional scientific data near this location |
Element | Measured value | Units of measure | Analytical method |
---|---|---|---|
Lithium | 49 | parts per million by weight | AES_HF |
Beryllium | <1 | parts per million by weight | AES_HF |
Sodium | 1.87 | percent by weight | AES_HF |
Magnesium | 1.29 | percent by weight | AES_HF |
Aluminum | 7.17 | percent by weight | AES_HF |
Phosphorus | 0.08 | percent by weight | AES_HF |
Potassium | 1.39 | percent by weight | AES_HF |
Calcium | 1.17 | percent by weight | AES_HF |
Scandium | 14 | parts per million by weight | AES_HF |
Titanium | 0.41 | percent by weight | AES_HF |
Vanadium | 149 | parts per million by weight | AES_HF |
Chromium | 82 | parts per million by weight | AES_HF |
Manganese | 0.06 | percent by weight | AES_HF |
Iron | 3.89 | percent by weight | AES_HF |
Cobalt | 17 | parts per million by weight | AES_HF |
Nickel | 66 | parts per million by weight | AES_HF |
Copper | 30 | parts per million by weight | AES_HF |
Zinc | 90 | parts per million by weight | AES_HF |
Gallium | 20 | parts per million by weight | AES_HF |
Arsenic | 28.2 | parts per million by weight | AA_HG_ST |
Selenium | 0.3 | parts per million by weight | AA_HG_HF |
Strontium | 240 | parts per million by weight | AES_HF |
Yttrium | 17 | parts per million by weight | AES_HF |
Niobium | 16 | parts per million by weight | AES_HF |
Molybdenum | 5 | parts per million by weight | AES_HF |
Silver | <2 | parts per million by weight | AES_HF |
Cadmium | <2 | parts per million by weight | AES_HF |
Tin | <50 | parts per million by weight | AES_HF |
Barium | 1010 | parts per million by weight | AES_HF |
Lanthanum | 22 | parts per million by weight | AES_HF |
Cerium | 43 | parts per million by weight | AES_HF |
Neodymium | 25 | parts per million by weight | AES_HF |
Europium | <2 | parts per million by weight | AES_HF |
Holmium | <4 | parts per million by weight | AES_HF |
Ytterbium | 2 | parts per million by weight | AES_HF |
Tantalum | <40 | parts per million by weight | AES_HF |
Gold | <8 | parts per million by weight | AES_HF |
Mercury | 0.17 | parts per million by weight | AA_CV |
Lead | 22 | parts per million by weight | AES_HF |
Bismuth | <50 | parts per million by weight | AES_HF |
Thorium | <6 | parts per million by weight | AES_HF |
Uranium | <100 | parts per million by weight | AES_HF |
Element | Value | Units | Technique |
---|---|---|---|
Lithium | 49 | parts per million by weight | AES_HF |
Beryllium | <1 | parts per million by weight | AES_HF |
Sodium | 1.87 | percent by weight | AES_HF |
Magnesium | 1.29 | percent by weight | AES_HF |
Aluminum | 7.17 | percent by weight | AES_HF |
Phosphorus | 0.08 | percent by weight | AES_HF |
Potassium | 1.39 | percent by weight | AES_HF |
Calcium | 1.17 | percent by weight | AES_HF |
Scandium | 14 | parts per million by weight | AES_HF |
Titanium | 0.41 | percent by weight | AES_HF |
Vanadium | 149 | parts per million by weight | AES_HF |
Chromium | 82 | parts per million by weight | AES_HF |
Manganese | 0.06 | percent by weight | AES_HF |
Iron | 3.89 | percent by weight | AES_HF |
Cobalt | 17 | parts per million by weight | AES_HF |
Nickel | 66 | parts per million by weight | AES_HF |
Copper | 30 | parts per million by weight | AES_HF |
Zinc | 90 | parts per million by weight | AES_HF |
Gallium | 20 | parts per million by weight | AES_HF |
Arsenic | 20 | parts per million by weight | AES_HF |
Arsenic | 28.2 | parts per million by weight | AA_HG_ST |
Selenium | 0.3 | parts per million by weight | AA_HG_HF |
Strontium | 240 | parts per million by weight | AES_HF |
Yttrium | 17 | parts per million by weight | AES_HF |
Niobium | 16 | parts per million by weight | AES_HF |
Molybdenum | 5 | parts per million by weight | AES_HF |
Silver | <2 | parts per million by weight | AES_HF |
Cadmium | <2 | parts per million by weight | AES_HF |
Tin | <50 | parts per million by weight | AES_HF |
Barium | 1010 | parts per million by weight | AES_HF |
Lanthanum | 22 | parts per million by weight | AES_HF |
Cerium | 43 | parts per million by weight | AES_HF |
Neodymium | 25 | parts per million by weight | AES_HF |
Europium | <2 | parts per million by weight | AES_HF |
Holmium | <4 | parts per million by weight | AES_HF |
Ytterbium | 2 | parts per million by weight | AES_HF |
Tantalum | <40 | parts per million by weight | AES_HF |
Gold | <8 | parts per million by weight | AES_HF |
Mercury | 0.17 | parts per million by weight | AA_CV |
Lead | 22 | parts per million by weight | AES_HF |
Bismuth | <50 | parts per million by weight | AES_HF |
Thorium | <6 | parts per million by weight | AES_HF |
Uranium | <100 | parts per million by weight | AES_HF |