Field | Value |
---|---|
Lab ID | C194513 |
Field ID | 99Eb713SD |
Job ID | MRP03481 |
Sample submitter | Bailey, Elizabeth A. |
Date collected | 07/09/1999 |
Date submitted | 9/11/2001 |
Project name | Hg & As |
State | AK |
Country | United States |
Latitude (WGS84) | 61.75536 |
Longitude (WGS84) | -157.32037 |
Original datum | WGS84 |
Original latitude | 61.75536 |
Original longitude | -157.32037 |
Location precision | 1 second |
Sampling depth | Surface (0-25cm) |
Description of location | upstream on red Devil Creek, well above site 701 |
Sample source | stream/river |
Collection method | composite |
Primary media type | sediment |
Notes on sample | stream |
Sample preparation method | standard;;samples dried at 40 degrees C |
Sieve size | -80 mesh |
(click for info) | |
Geologic map unit | -157.32037, 61.75536 |
Nearby scientific data | Find additional scientific data near this location |
Element | Measured value | Units of measure | Analytical method |
---|---|---|---|
Lithium | 82 | parts per million by weight | AES_HF |
Beryllium | 1 | parts per million by weight | AES_HF |
Sodium | 0.58 | percent by weight | AES_HF |
Magnesium | 0.53 | percent by weight | AES_HF |
Aluminum | 5.75 | percent by weight | AES_HF |
Phosphorus | 0.1 | percent by weight | AES_HF |
Sulfur | <0.05 | percent by weight | CB_IRC |
Potassium | 1.51 | percent by weight | AES_HF |
Calcium | 0.31 | percent by weight | AES_HF |
Scandium | 10 | parts per million by weight | AES_HF |
Titanium | 0.23 | percent by weight | AES_HF |
Vanadium | 141 | parts per million by weight | AES_HF |
Chromium | 54 | parts per million by weight | AES_HF |
Manganese | 0.05 | percent by weight | AES_HF |
Iron | 4.32 | percent by weight | AES_HF |
Cobalt | 15 | parts per million by weight | AES_HF |
Nickel | 42 | parts per million by weight | AES_HF |
Copper | 27 | parts per million by weight | AES_HF |
Zinc | 121 | parts per million by weight | AES_HF |
Gallium | 15 | parts per million by weight | AES_HF |
Arsenic | 77.2 | parts per million by weight | AA_HG_ST |
Selenium | 0.6 | parts per million by weight | AA_HG_HF |
Strontium | 59 | parts per million by weight | AES_HF |
Yttrium | 11 | parts per million by weight | AES_HF |
Niobium | 8 | parts per million by weight | AES_HF |
Molybdenum | 2 | parts per million by weight | AES_HF |
Silver | <2 | parts per million by weight | AES_HF |
Cadmium | <2 | parts per million by weight | AES_HF |
Tin | <50 | parts per million by weight | AES_HF |
Antimony | 19.1 | parts per million by weight | AA_HG_ST |
Barium | 821 | parts per million by weight | AES_HF |
Lanthanum | 22 | parts per million by weight | AES_HF |
Cerium | 48 | parts per million by weight | AES_HF |
Neodymium | 21 | parts per million by weight | AES_HF |
Europium | <2 | parts per million by weight | AES_HF |
Holmium | <4 | parts per million by weight | AES_HF |
Ytterbium | 1 | parts per million by weight | AES_HF |
Tantalum | <40 | parts per million by weight | AES_HF |
Gold | <8 | parts per million by weight | AES_HF |
Mercury | 0.91 | parts per million by weight | AA_CV |
Lead | 17 | parts per million by weight | AES_HF |
Bismuth | <50 | parts per million by weight | AES_HF |
Thorium | <6 | parts per million by weight | AES_HF |
Uranium | <100 | parts per million by weight | AES_HF |
C_crb | 0.01 | percent by weight | TT_HCl |
C_org | 0.63 | percent by weight | CP |
C_tot | 0.64 | percent by weight | CB_IRC |
CO2 | 0.03 | percent by weight | TT_HCl |
Element | Value | Units | Technique |
---|---|---|---|
Lithium | 82 | parts per million by weight | AES_HF |
Beryllium | 1 | parts per million by weight | AES_HF |
Sodium | 0.58 | percent by weight | AES_HF |
Magnesium | 0.53 | percent by weight | AES_HF |
Aluminum | 5.75 | percent by weight | AES_HF |
Phosphorus | 0.1 | percent by weight | AES_HF |
Sulfur | <0.05 | percent by weight | CB_IRC |
Potassium | 1.51 | percent by weight | AES_HF |
Calcium | 0.31 | percent by weight | AES_HF |
Scandium | 10 | parts per million by weight | AES_HF |
Titanium | 0.23 | percent by weight | AES_HF |
Vanadium | 141 | parts per million by weight | AES_HF |
Chromium | 54 | parts per million by weight | AES_HF |
Manganese | 0.05 | percent by weight | AES_HF |
Iron | 4.32 | percent by weight | AES_HF |
Cobalt | 15 | parts per million by weight | AES_HF |
Nickel | 42 | parts per million by weight | AES_HF |
Copper | 27 | parts per million by weight | AES_HF |
Copper | 25.6 | parts per million by weight | AES_AZ_P |
Zinc | 121 | parts per million by weight | AES_HF |
Zinc | 113 | parts per million by weight | AES_AZ_P |
Gallium | 15 | parts per million by weight | AES_HF |
Arsenic | 68 | parts per million by weight | AES_HF |
Arsenic | 64 | parts per million by weight | AES_AZ_P |
Arsenic | 77.2 | parts per million by weight | AA_HG_ST |
Selenium | 0.6 | parts per million by weight | AA_HG_HF |
Strontium | 59 | parts per million by weight | AES_HF |
Yttrium | 11 | parts per million by weight | AES_HF |
Niobium | 8 | parts per million by weight | AES_HF |
Molybdenum | 2 | parts per million by weight | AES_HF |
Molybdenum | 1.2 | parts per million by weight | AES_AZ_P |
Silver | <2 | parts per million by weight | AES_HF |
Silver | <0.08 | parts per million by weight | AES_AZ_P |
Cadmium | <2 | parts per million by weight | AES_HF |
Cadmium | 0.17 | parts per million by weight | AES_AZ_P |
Tin | <50 | parts per million by weight | AES_HF |
Antimony | 17 | parts per million by weight | AES_AZ_P |
Antimony | 19.1 | parts per million by weight | AA_HG_ST |
Barium | 821 | parts per million by weight | AES_HF |
Lanthanum | 22 | parts per million by weight | AES_HF |
Cerium | 48 | parts per million by weight | AES_HF |
Neodymium | 21 | parts per million by weight | AES_HF |
Europium | <2 | parts per million by weight | AES_HF |
Holmium | <4 | parts per million by weight | AES_HF |
Ytterbium | 1 | parts per million by weight | AES_HF |
Tantalum | <40 | parts per million by weight | AES_HF |
Gold | <8 | parts per million by weight | AES_HF |
Gold | <0.1 | parts per million by weight | AES_AZ_P |
Mercury | 0.91 | parts per million by weight | AA_CV |
Lead | 17 | parts per million by weight | AES_HF |
Lead | 10 | parts per million by weight | AES_AZ_P |
Bismuth | <50 | parts per million by weight | AES_HF |
Bismuth | <1 | parts per million by weight | AES_AZ_P |
Thorium | <6 | parts per million by weight | AES_HF |
Uranium | <100 | parts per million by weight | AES_HF |
Carbon (total) | 0.64 | percent by weight | CB_IRC |
Carbon dioxide | 0.03 | percent by weight | TT_HCl |
Carbon (organic) | 0.63 | percent by weight | CP |
Carbon (carbonate) | 0.01 | percent by weight | TT_HCl |