Field | Value |
---|---|
Lab ID | C194519 |
Field ID | 99Eb720SD |
Job ID | MRP03481 |
Sample submitter | Bailey, Elizabeth A. |
Date collected | 07/10/1999 |
Date submitted | 9/11/2001 |
Project name | Hg & As |
State | AK |
Country | United States |
Latitude (WGS84) | 61.75899 |
Longitude (WGS84) | -157.30871 |
Original datum | WGS84 |
Original latitude | 61.75899 |
Original longitude | -157.30871 |
Location precision | 1 second |
Sampling depth | Surface (0-25cm) |
Description of location | downstream of Red Devil mine on Kuskokwim River |
Sample source | stream/river |
Collection method | composite |
Primary media type | sediment |
Notes on sample | stream |
Sample preparation method | standard;;samples dried at 40 degrees C |
Sieve size | -80 mesh |
(click for info) | |
Geologic map unit | -157.30871, 61.75899 |
Nearby scientific data | Find additional scientific data near this location |
Element | Measured value | Units of measure | Analytical method |
---|---|---|---|
Lithium | 109 | parts per million by weight | AES_HF |
Beryllium | 2 | parts per million by weight | AES_HF |
Sodium | 1.23 | percent by weight | AES_HF |
Magnesium | 0.67 | percent by weight | AES_HF |
Aluminum | 7.08 | percent by weight | AES_HF |
Phosphorus | 0.08 | percent by weight | AES_HF |
Sulfur | <0.05 | percent by weight | CB_IRC |
Potassium | 1.91 | percent by weight | AES_HF |
Calcium | 0.94 | percent by weight | AES_HF |
Scandium | 13 | parts per million by weight | AES_HF |
Titanium | 0.37 | percent by weight | AES_HF |
Vanadium | 131 | parts per million by weight | AES_HF |
Chromium | 88 | parts per million by weight | AES_HF |
Manganese | 0.07 | percent by weight | AES_HF |
Iron | 3.5 | percent by weight | AES_HF |
Cobalt | 14 | parts per million by weight | AES_HF |
Nickel | 37 | parts per million by weight | AES_HF |
Copper | 36 | parts per million by weight | AES_HF |
Zinc | 98 | parts per million by weight | AES_HF |
Gallium | 18 | parts per million by weight | AES_HF |
Arsenic | 625 | parts per million by weight | AA_HG_ST |
Selenium | 0.4 | parts per million by weight | AA_HG_HF |
Strontium | 199 | parts per million by weight | AES_HF |
Yttrium | 17 | parts per million by weight | AES_HF |
Niobium | 9 | parts per million by weight | AES_HF |
Molybdenum | <2 | parts per million by weight | AES_HF |
Silver | <2 | parts per million by weight | AES_HF |
Cadmium | <2 | parts per million by weight | AES_HF |
Tin | <50 | parts per million by weight | AES_HF |
Antimony | 64.6 | parts per million by weight | AA_HG_ST |
Barium | 1140 | parts per million by weight | AES_HF |
Lanthanum | 39 | parts per million by weight | AES_HF |
Cerium | 83 | parts per million by weight | AES_HF |
Neodymium | 35 | parts per million by weight | AES_HF |
Europium | <2 | parts per million by weight | AES_HF |
Holmium | <4 | parts per million by weight | AES_HF |
Ytterbium | 2 | parts per million by weight | AES_HF |
Tantalum | <40 | parts per million by weight | AES_HF |
Gold | <8 | parts per million by weight | AES_HF |
Mercury | 142 | parts per million by weight | AA_CV |
Lead | 16 | parts per million by weight | AES_HF |
Bismuth | <50 | parts per million by weight | AES_HF |
Thorium | 7 | parts per million by weight | AES_HF |
Uranium | <100 | parts per million by weight | AES_HF |
C_crb | 0.04 | percent by weight | TT_HCl |
C_org | 0.46 | percent by weight | CP |
C_tot | 0.5 | percent by weight | CB_IRC |
CO2 | 0.15 | percent by weight | TT_HCl |
Element | Value | Units | Technique |
---|---|---|---|
Lithium | 109 | parts per million by weight | AES_HF |
Beryllium | 2 | parts per million by weight | AES_HF |
Sodium | 1.23 | percent by weight | AES_HF |
Magnesium | 0.67 | percent by weight | AES_HF |
Aluminum | 7.08 | percent by weight | AES_HF |
Phosphorus | 0.08 | percent by weight | AES_HF |
Sulfur | <0.05 | percent by weight | CB_IRC |
Potassium | 1.91 | percent by weight | AES_HF |
Calcium | 0.94 | percent by weight | AES_HF |
Scandium | 13 | parts per million by weight | AES_HF |
Titanium | 0.37 | percent by weight | AES_HF |
Vanadium | 131 | parts per million by weight | AES_HF |
Chromium | 88 | parts per million by weight | AES_HF |
Manganese | 0.07 | percent by weight | AES_HF |
Iron | 3.5 | percent by weight | AES_HF |
Cobalt | 14 | parts per million by weight | AES_HF |
Nickel | 37 | parts per million by weight | AES_HF |
Copper | 36 | parts per million by weight | AES_HF |
Copper | 34.4 | parts per million by weight | AES_AZ_P |
Zinc | 98 | parts per million by weight | AES_HF |
Zinc | 104 | parts per million by weight | AES_AZ_P |
Gallium | 18 | parts per million by weight | AES_HF |
Arsenic | 631 | parts per million by weight | AES_HF |
Arsenic | 677 | parts per million by weight | AES_AZ_P |
Arsenic | 625 | parts per million by weight | AA_HG_ST |
Selenium | 0.4 | parts per million by weight | AA_HG_HF |
Strontium | 199 | parts per million by weight | AES_HF |
Yttrium | 17 | parts per million by weight | AES_HF |
Niobium | 9 | parts per million by weight | AES_HF |
Molybdenum | <2 | parts per million by weight | AES_HF |
Molybdenum | 1.1 | parts per million by weight | AES_AZ_P |
Silver | <2 | parts per million by weight | AES_HF |
Silver | 0.1 | parts per million by weight | AES_AZ_P |
Cadmium | <2 | parts per million by weight | AES_HF |
Cadmium | <0.05 | parts per million by weight | AES_AZ_P |
Tin | <50 | parts per million by weight | AES_HF |
Antimony | 59 | parts per million by weight | AES_AZ_P |
Antimony | 64.6 | parts per million by weight | AA_HG_ST |
Barium | 1140 | parts per million by weight | AES_HF |
Lanthanum | 39 | parts per million by weight | AES_HF |
Cerium | 83 | parts per million by weight | AES_HF |
Neodymium | 35 | parts per million by weight | AES_HF |
Europium | <2 | parts per million by weight | AES_HF |
Holmium | <4 | parts per million by weight | AES_HF |
Ytterbium | 2 | parts per million by weight | AES_HF |
Tantalum | <40 | parts per million by weight | AES_HF |
Gold | <8 | parts per million by weight | AES_HF |
Gold | <0.1 | parts per million by weight | AES_AZ_P |
Mercury | 142 | parts per million by weight | AA_CV |
Lead | 16 | parts per million by weight | AES_HF |
Lead | 10 | parts per million by weight | AES_AZ_P |
Bismuth | <50 | parts per million by weight | AES_HF |
Bismuth | <1 | parts per million by weight | AES_AZ_P |
Thorium | 7 | parts per million by weight | AES_HF |
Uranium | <100 | parts per million by weight | AES_HF |
Carbon (total) | 0.5 | percent by weight | CB_IRC |
Carbon dioxide | 0.15 | percent by weight | TT_HCl |
Carbon (organic) | 0.46 | percent by weight | CP |
Carbon (carbonate) | 0.04 | percent by weight | TT_HCl |