Lithium | 165 | parts per million by weight | AES_HF |
Lithium | 137 | parts per million by weight | MS_HF |
Beryllium | 1.5 | parts per million by weight | AES_HF |
Beryllium | 1.6 | parts per million by weight | MS_HF |
Sodium | <0.005 | percent by weight | AES_HF |
Sodium | 9.47 | percent by weight | MS_HF |
Magnesium | 2.3 | percent by weight | AES_HF |
Magnesium | 2.44 | percent by weight | MS_HF |
Aluminum | 5 | percent by weight | AES_HF |
Aluminum | 4.54 | percent by weight | MS_HF |
Phosphorus | 0.05 | percent by weight | AES_HF |
Phosphorus | 0.05 | percent by weight | MS_HF |
Potassium | 2.4 | percent by weight | AES_HF |
Potassium | 2.13 | percent by weight | MS_HF |
Calcium | 7.3 | percent by weight | AES_HF |
Calcium | 7 | percent by weight | MS_HF |
Scandium | 7.5 | parts per million by weight | AES_HF |
Scandium | 7.4 | parts per million by weight | MS_HF |
Titanium | 0.27 | percent by weight | AES_HF |
Titanium | 0.29 | percent by weight | MS_HF |
Vanadium | 48 | parts per million by weight | AES_HF |
Vanadium | 50 | parts per million by weight | MS_HF |
Chromium | 30 | parts per million by weight | AES_HF |
Chromium | 31.6 | parts per million by weight | MS_HF |
Manganese | 0.04 | percent by weight | AES_HF |
Manganese | 0.04 | percent by weight | MS_HF |
Iron | 2.1 | percent by weight | AES_HF |
Iron | 2.13 | percent by weight | MS_HF |
Cobalt | 7 | parts per million by weight | AES_HF |
Cobalt | 6.9 | parts per million by weight | MS_HF |
Nickel | 14 | parts per million by weight | AES_HF |
Nickel | 11.8 | parts per million by weight | MS_HF |
Copper | 12 | parts per million by weight | AES_HF |
Copper | 16.1 | parts per million by weight | MS_HF |
Zinc | 52 | parts per million by weight | AES_HF |
Zinc | 51 | parts per million by weight | MS_HF |
Gallium | <4 | parts per million by weight | AES_HF |
Gallium | 10.7 | parts per million by weight | MS_HF |
Arsenic | <10 | parts per million by weight | AES_HF |
Arsenic | 12.5 | parts per million by weight | MS_HF |
Rubidium | 83.8 | parts per million by weight | MS_HF |
Strontium | 1050 | parts per million by weight | AES_HF |
Strontium | 982 | parts per million by weight | MS_HF |
Yttrium | 17 | parts per million by weight | AES_HF |
Yttrium | 23.8 | parts per million by weight | MS_HF |
Niobium | 7.2 | parts per million by weight | AES_HF |
Niobium | 11 | parts per million by weight | MS_HF |
Molybdenum | <2 | parts per million by weight | AES_HF |
Molybdenum | 0.87 | parts per million by weight | MS_HF |
Silver | <2 | parts per million by weight | AES_HF |
Silver | <2 | parts per million by weight | MS_HF |
Cadmium | <2 | parts per million by weight | AES_HF |
Cadmium | 0.17 | parts per million by weight | MS_HF |
Tin | <5 | parts per million by weight | AES_HF |
Antimony | 0.91 | parts per million by weight | MS_HF |
Cesium | 5.6 | parts per million by weight | MS_HF |
Barium | 511 | parts per million by weight | AES_HF |
Barium | 516 | parts per million by weight | MS_HF |
Lanthanum | 40 | parts per million by weight | AES_HF |
Lanthanum | 41.7 | parts per million by weight | MS_HF |
Cerium | 70 | parts per million by weight | AES_HF |
Cerium | 71.3 | parts per million by weight | MS_HF |
Neodymium | 32 | parts per million by weight | AES_HF |
Europium | <2 | parts per million by weight | AES_HF |
Holmium | <4 | parts per million by weight | AES_HF |
Ytterbium | 1.9 | parts per million by weight | AES_HF |
Tantalum | <40 | parts per million by weight | AES_HF |
Gold | <8 | parts per million by weight | AES_HF |
Thallium | 0.52 | parts per million by weight | MS_HF |
Lead | 11 | parts per million by weight | AES_HF |
Lead | 15.3 | parts per million by weight | MS_HF |
Bismuth | <10 | parts per million by weight | AES_HF |
Bismuth | 0.15 | parts per million by weight | MS_HF |
Thorium | 14 | parts per million by weight | AES_HF |
Thorium | 11.7 | parts per million by weight | MS_HF |
Uranium | 1.78 | parts per million by weight | MS_HF |
Uranium | <100 | parts per million by weight | AES_HF |