Lithium | 432 | parts per million by weight | AES_HF |
Lithium | 333 | parts per million by weight | MS_HF |
Beryllium | 2.2 | parts per million by weight | AES_HF |
Beryllium | 2.2 | parts per million by weight | MS_HF |
Sodium | 4.5 | percent by weight | AES_HF |
Sodium | 3.88 | percent by weight | MS_HF |
Magnesium | 4.6 | percent by weight | AES_HF |
Magnesium | 4.24 | percent by weight | MS_HF |
Aluminum | 6.4 | percent by weight | AES_HF |
Aluminum | 5.7 | percent by weight | MS_HF |
Phosphorus | 0.04 | percent by weight | AES_HF |
Phosphorus | 0.04 | percent by weight | MS_HF |
Potassium | 3.4 | percent by weight | AES_HF |
Potassium | 2.92 | percent by weight | MS_HF |
Calcium | 7 | percent by weight | AES_HF |
Calcium | 6.32 | percent by weight | MS_HF |
Scandium | 9 | parts per million by weight | AES_HF |
Scandium | 8.9 | parts per million by weight | MS_HF |
Titanium | 0.27 | percent by weight | AES_HF |
Titanium | 0.29 | percent by weight | MS_HF |
Vanadium | 55 | parts per million by weight | AES_HF |
Vanadium | 54.8 | parts per million by weight | MS_HF |
Chromium | 35 | parts per million by weight | AES_HF |
Chromium | 34.7 | parts per million by weight | MS_HF |
Manganese | 0.07 | percent by weight | AES_HF |
Manganese | 0.07 | percent by weight | MS_HF |
Iron | 2.7 | percent by weight | AES_HF |
Iron | 2.74 | percent by weight | MS_HF |
Cobalt | 12 | parts per million by weight | AES_HF |
Cobalt | 10.3 | parts per million by weight | MS_HF |
Nickel | 21 | parts per million by weight | AES_HF |
Nickel | 18.8 | parts per million by weight | MS_HF |
Copper | 23 | parts per million by weight | AES_HF |
Copper | 23.8 | parts per million by weight | MS_HF |
Zinc | 85 | parts per million by weight | AES_HF |
Zinc | 78.5 | parts per million by weight | MS_HF |
Gallium | 13.6 | parts per million by weight | MS_HF |
Gallium | <4 | parts per million by weight | AES_HF |
Arsenic | 21 | parts per million by weight | AES_HF |
Arsenic | 16.4 | parts per million by weight | MS_HF |
Rubidium | 125 | parts per million by weight | MS_HF |
Strontium | 1060 | parts per million by weight | AES_HF |
Strontium | 940 | parts per million by weight | MS_HF |
Yttrium | 16 | parts per million by weight | AES_HF |
Yttrium | 21.1 | parts per million by weight | MS_HF |
Niobium | 12 | parts per million by weight | AES_HF |
Niobium | 13 | parts per million by weight | MS_HF |
Molybdenum | <2 | parts per million by weight | AES_HF |
Molybdenum | 0.78 | parts per million by weight | MS_HF |
Silver | <2 | parts per million by weight | AES_HF |
Silver | <2 | parts per million by weight | MS_HF |
Cadmium | <2 | parts per million by weight | AES_HF |
Cadmium | 0.18 | parts per million by weight | MS_HF |
Tin | <5 | parts per million by weight | AES_HF |
Antimony | 1.3 | parts per million by weight | MS_HF |
Cesium | 10.3 | parts per million by weight | MS_HF |
Barium | 458 | parts per million by weight | AES_HF |
Barium | 445 | parts per million by weight | MS_HF |
Lanthanum | 34 | parts per million by weight | AES_HF |
Lanthanum | 33.9 | parts per million by weight | MS_HF |
Cerium | 58 | parts per million by weight | AES_HF |
Cerium | 55.8 | parts per million by weight | MS_HF |
Neodymium | 27 | parts per million by weight | AES_HF |
Europium | <2 | parts per million by weight | AES_HF |
Holmium | <4 | parts per million by weight | AES_HF |
Ytterbium | 1.8 | parts per million by weight | AES_HF |
Tantalum | <40 | parts per million by weight | AES_HF |
Gold | <8 | parts per million by weight | AES_HF |
Thallium | 0.69 | parts per million by weight | MS_HF |
Lead | 11 | parts per million by weight | AES_HF |
Lead | 17.2 | parts per million by weight | MS_HF |
Bismuth | <10 | parts per million by weight | AES_HF |
Bismuth | 0.2 | parts per million by weight | MS_HF |
Thorium | 15 | parts per million by weight | AES_HF |
Thorium | 10.9 | parts per million by weight | MS_HF |
Uranium | <100 | parts per million by weight | AES_HF |
Uranium | 1.88 | parts per million by weight | MS_HF |