Lithium | 461 | parts per million by weight | AES_HF |
Lithium | 359 | parts per million by weight | MS_HF |
Beryllium | 2.2 | parts per million by weight | AES_HF |
Beryllium | 2.1 | parts per million by weight | MS_HF |
Sodium | 6.07 | percent by weight | MS_HF |
Sodium | 7.1 | percent by weight | AES_HF |
Magnesium | 4.3 | percent by weight | AES_HF |
Magnesium | 3.99 | percent by weight | MS_HF |
Aluminum | 5.43 | percent by weight | MS_HF |
Aluminum | 5.9 | percent by weight | AES_HF |
Phosphorus | 0.04 | percent by weight | AES_HF |
Phosphorus | 0.03 | percent by weight | MS_HF |
Potassium | 2.84 | percent by weight | MS_HF |
Potassium | 3.2 | percent by weight | AES_HF |
Calcium | 5.4 | percent by weight | AES_HF |
Calcium | 5.15 | percent by weight | MS_HF |
Scandium | 8.5 | parts per million by weight | AES_HF |
Scandium | 8.6 | parts per million by weight | MS_HF |
Titanium | 0.25 | percent by weight | AES_HF |
Titanium | 0.27 | percent by weight | MS_HF |
Vanadium | 52.9 | parts per million by weight | MS_HF |
Vanadium | 52 | parts per million by weight | AES_HF |
Chromium | 34 | parts per million by weight | AES_HF |
Chromium | 31.4 | parts per million by weight | MS_HF |
Manganese | 0.06 | percent by weight | MS_HF |
Manganese | 0.06 | percent by weight | AES_HF |
Iron | 2.63 | percent by weight | MS_HF |
Iron | 2.6 | percent by weight | AES_HF |
Cobalt | 9.9 | parts per million by weight | MS_HF |
Cobalt | 12 | parts per million by weight | AES_HF |
Nickel | 21 | parts per million by weight | AES_HF |
Nickel | 18.5 | parts per million by weight | MS_HF |
Copper | 23.8 | parts per million by weight | MS_HF |
Copper | 24 | parts per million by weight | AES_HF |
Zinc | 82 | parts per million by weight | AES_HF |
Zinc | 74.9 | parts per million by weight | MS_HF |
Gallium | <4 | parts per million by weight | AES_HF |
Gallium | 13.4 | parts per million by weight | MS_HF |
Arsenic | 16 | parts per million by weight | AES_HF |
Arsenic | 18.2 | parts per million by weight | MS_HF |
Rubidium | 120 | parts per million by weight | MS_HF |
Strontium | 845 | parts per million by weight | AES_HF |
Strontium | 792 | parts per million by weight | MS_HF |
Yttrium | 13 | parts per million by weight | AES_HF |
Yttrium | 19.5 | parts per million by weight | MS_HF |
Niobium | 14 | parts per million by weight | AES_HF |
Niobium | 12 | parts per million by weight | MS_HF |
Molybdenum | <2 | parts per million by weight | AES_HF |
Molybdenum | 0.97 | parts per million by weight | MS_HF |
Silver | <2 | parts per million by weight | MS_HF |
Silver | <2 | parts per million by weight | AES_HF |
Cadmium | <2 | parts per million by weight | AES_HF |
Cadmium | 0.14 | parts per million by weight | MS_HF |
Tin | <5 | parts per million by weight | AES_HF |
Antimony | 1.2 | parts per million by weight | MS_HF |
Cesium | 10 | parts per million by weight | MS_HF |
Barium | 394 | parts per million by weight | MS_HF |
Barium | 379 | parts per million by weight | AES_HF |
Lanthanum | 31 | parts per million by weight | AES_HF |
Lanthanum | 29.1 | parts per million by weight | MS_HF |
Cerium | 47 | parts per million by weight | AES_HF |
Cerium | 47 | parts per million by weight | MS_HF |
Neodymium | 24 | parts per million by weight | AES_HF |
Europium | <2 | parts per million by weight | AES_HF |
Holmium | <4 | parts per million by weight | AES_HF |
Ytterbium | 1.6 | parts per million by weight | AES_HF |
Tantalum | <40 | parts per million by weight | AES_HF |
Gold | <8 | parts per million by weight | AES_HF |
Thallium | 0.63 | parts per million by weight | MS_HF |
Lead | 14.6 | parts per million by weight | MS_HF |
Lead | 12 | parts per million by weight | AES_HF |
Bismuth | <10 | parts per million by weight | AES_HF |
Bismuth | 0.18 | parts per million by weight | MS_HF |
Thorium | 9.7 | parts per million by weight | AES_HF |
Thorium | 9.09 | parts per million by weight | MS_HF |
Uranium | <100 | parts per million by weight | AES_HF |
Uranium | 1.6 | parts per million by weight | MS_HF |