Lithium | 254 | parts per million by weight | AES_HF |
Lithium | 194 | parts per million by weight | MS_HF |
Beryllium | 1.8 | parts per million by weight | AES_HF |
Beryllium | 1.9 | parts per million by weight | MS_HF |
Sodium | 5.4 | percent by weight | AES_HF |
Sodium | 4.35 | percent by weight | MS_HF |
Magnesium | 2.9 | percent by weight | AES_HF |
Magnesium | 2.82 | percent by weight | MS_HF |
Aluminum | 6 | percent by weight | AES_HF |
Aluminum | 5.15 | percent by weight | MS_HF |
Phosphorus | 0.05 | percent by weight | AES_HF |
Phosphorus | 0.04 | percent by weight | MS_HF |
Potassium | 2.9 | percent by weight | AES_HF |
Potassium | 2.39 | percent by weight | MS_HF |
Calcium | 10.2 | percent by weight | AES_HF |
Calcium | 9.17 | percent by weight | MS_HF |
Scandium | 8.2 | parts per million by weight | AES_HF |
Scandium | 8.1 | parts per million by weight | MS_HF |
Titanium | 0.29 | percent by weight | AES_HF |
Titanium | 0.29 | percent by weight | MS_HF |
Vanadium | 49 | parts per million by weight | AES_HF |
Vanadium | 48.4 | parts per million by weight | MS_HF |
Chromium | 29 | parts per million by weight | AES_HF |
Chromium | 29 | parts per million by weight | MS_HF |
Manganese | 0.05 | percent by weight | AES_HF |
Manganese | 0.05 | percent by weight | MS_HF |
Iron | 2.2 | percent by weight | AES_HF |
Iron | 2.26 | percent by weight | MS_HF |
Cobalt | 9.4 | parts per million by weight | AES_HF |
Cobalt | 7.7 | parts per million by weight | MS_HF |
Nickel | 16 | parts per million by weight | AES_HF |
Nickel | 13.3 | parts per million by weight | MS_HF |
Copper | 15 | parts per million by weight | AES_HF |
Copper | 16.6 | parts per million by weight | MS_HF |
Zinc | 62 | parts per million by weight | AES_HF |
Zinc | 55.6 | parts per million by weight | MS_HF |
Gallium | <4 | parts per million by weight | AES_HF |
Gallium | 12.2 | parts per million by weight | MS_HF |
Arsenic | 16 | parts per million by weight | AES_HF |
Arsenic | 12.3 | parts per million by weight | MS_HF |
Rubidium | 98 | parts per million by weight | MS_HF |
Strontium | 1450 | parts per million by weight | AES_HF |
Strontium | 1300 | parts per million by weight | MS_HF |
Yttrium | 20 | parts per million by weight | AES_HF |
Yttrium | 27.1 | parts per million by weight | MS_HF |
Niobium | 13 | parts per million by weight | AES_HF |
Niobium | 12 | parts per million by weight | MS_HF |
Molybdenum | 0.69 | parts per million by weight | MS_HF |
Molybdenum | <2 | parts per million by weight | AES_HF |
Silver | <2 | parts per million by weight | AES_HF |
Silver | <2 | parts per million by weight | MS_HF |
Cadmium | <2 | parts per million by weight | AES_HF |
Cadmium | 0.21 | parts per million by weight | MS_HF |
Tin | <5 | parts per million by weight | AES_HF |
Antimony | 1 | parts per million by weight | MS_HF |
Cesium | 6.7 | parts per million by weight | MS_HF |
Barium | 606 | parts per million by weight | AES_HF |
Barium | 590 | parts per million by weight | MS_HF |
Lanthanum | 45 | parts per million by weight | AES_HF |
Lanthanum | 42.4 | parts per million by weight | MS_HF |
Cerium | 76 | parts per million by weight | AES_HF |
Cerium | 69.7 | parts per million by weight | MS_HF |
Neodymium | 37 | parts per million by weight | AES_HF |
Europium | <2 | parts per million by weight | AES_HF |
Holmium | <4 | parts per million by weight | AES_HF |
Ytterbium | 2.2 | parts per million by weight | AES_HF |
Tantalum | <40 | parts per million by weight | AES_HF |
Gold | <8 | parts per million by weight | AES_HF |
Thallium | 0.55 | parts per million by weight | MS_HF |
Lead | 12 | parts per million by weight | AES_HF |
Lead | 16.9 | parts per million by weight | MS_HF |
Bismuth | <10 | parts per million by weight | AES_HF |
Bismuth | 0.16 | parts per million by weight | MS_HF |
Thorium | 19 | parts per million by weight | AES_HF |
Thorium | 13.1 | parts per million by weight | MS_HF |
Uranium | <100 | parts per million by weight | AES_HF |
Uranium | 1.73 | parts per million by weight | MS_HF |