Lithium | 749 | parts per million by weight | AES_HF |
Lithium | 583 | parts per million by weight | MS_HF |
Beryllium | 2.1 | parts per million by weight | AES_HF |
Beryllium | 2 | parts per million by weight | MS_HF |
Sodium | <0.005 | percent by weight | AES_HF |
Sodium | 6.32 | percent by weight | MS_HF |
Magnesium | 4.4 | percent by weight | AES_HF |
Magnesium | 4.03 | percent by weight | MS_HF |
Aluminum | 5.8 | percent by weight | AES_HF |
Aluminum | 5.34 | percent by weight | MS_HF |
Phosphorus | 0.04 | percent by weight | AES_HF |
Phosphorus | 0.04 | percent by weight | MS_HF |
Potassium | 3.2 | percent by weight | AES_HF |
Potassium | 2.92 | percent by weight | MS_HF |
Calcium | 5.7 | percent by weight | AES_HF |
Calcium | 5.44 | percent by weight | MS_HF |
Scandium | 8.6 | parts per million by weight | AES_HF |
Scandium | 8.8 | parts per million by weight | MS_HF |
Titanium | 0.25 | percent by weight | AES_HF |
Titanium | 0.27 | percent by weight | MS_HF |
Vanadium | 50 | parts per million by weight | AES_HF |
Vanadium | 50.9 | parts per million by weight | MS_HF |
Chromium | 32 | parts per million by weight | AES_HF |
Chromium | 31.6 | parts per million by weight | MS_HF |
Manganese | 0.06 | percent by weight | AES_HF |
Manganese | 0.06 | percent by weight | MS_HF |
Iron | 2.5 | percent by weight | AES_HF |
Iron | 2.6 | percent by weight | MS_HF |
Cobalt | 9.8 | parts per million by weight | MS_HF |
Cobalt | 12 | parts per million by weight | AES_HF |
Nickel | 20 | parts per million by weight | AES_HF |
Nickel | 18.4 | parts per million by weight | MS_HF |
Copper | 24 | parts per million by weight | AES_HF |
Copper | 24 | parts per million by weight | MS_HF |
Zinc | 77 | parts per million by weight | AES_HF |
Zinc | 73.6 | parts per million by weight | MS_HF |
Gallium | <4 | parts per million by weight | AES_HF |
Gallium | 12.9 | parts per million by weight | MS_HF |
Arsenic | 40 | parts per million by weight | AES_HF |
Arsenic | 36.6 | parts per million by weight | MS_HF |
Rubidium | 121 | parts per million by weight | MS_HF |
Strontium | 917 | parts per million by weight | AES_HF |
Strontium | 842 | parts per million by weight | MS_HF |
Yttrium | 13 | parts per million by weight | AES_HF |
Yttrium | 19 | parts per million by weight | MS_HF |
Niobium | 10 | parts per million by weight | AES_HF |
Niobium | 12 | parts per million by weight | MS_HF |
Molybdenum | 5.6 | parts per million by weight | AES_HF |
Molybdenum | 5.1 | parts per million by weight | MS_HF |
Silver | <2 | parts per million by weight | AES_HF |
Silver | <2 | parts per million by weight | MS_HF |
Cadmium | <2 | parts per million by weight | AES_HF |
Cadmium | 0.16 | parts per million by weight | MS_HF |
Tin | <5 | parts per million by weight | AES_HF |
Antimony | 1.2 | parts per million by weight | MS_HF |
Cesium | 10.3 | parts per million by weight | MS_HF |
Barium | 364 | parts per million by weight | AES_HF |
Barium | 382 | parts per million by weight | MS_HF |
Lanthanum | 29 | parts per million by weight | AES_HF |
Lanthanum | 29.7 | parts per million by weight | MS_HF |
Cerium | 47 | parts per million by weight | AES_HF |
Cerium | 47 | parts per million by weight | MS_HF |
Neodymium | 23 | parts per million by weight | AES_HF |
Europium | <2 | parts per million by weight | AES_HF |
Holmium | <4 | parts per million by weight | AES_HF |
Ytterbium | 1.6 | parts per million by weight | AES_HF |
Tantalum | <40 | parts per million by weight | AES_HF |
Gold | <8 | parts per million by weight | AES_HF |
Thallium | 0.64 | parts per million by weight | MS_HF |
Lead | 13 | parts per million by weight | AES_HF |
Lead | 14.8 | parts per million by weight | MS_HF |
Bismuth | <10 | parts per million by weight | AES_HF |
Bismuth | 0.19 | parts per million by weight | MS_HF |
Thorium | 12 | parts per million by weight | AES_HF |
Thorium | 10 | parts per million by weight | MS_HF |
Uranium | <100 | parts per million by weight | AES_HF |
Uranium | 1.76 | parts per million by weight | MS_HF |