Lithium | 260 | parts per million by weight | MS_HF |
Lithium | 276 | parts per million by weight | AES_HF |
Beryllium | 1.9 | parts per million by weight | MS_HF |
Beryllium | <2 | parts per million by weight | AES_HF |
Sodium | 3.5 | percent by weight | AES_HF |
Sodium | 3.5 | percent by weight | MS_HF |
Magnesium | 3.19 | percent by weight | AES_HF |
Magnesium | 3.27 | percent by weight | MS_HF |
Aluminum | 5.82 | percent by weight | AES_HF |
Aluminum | 5.78 | percent by weight | MS_HF |
Phosphorus | 0.03 | percent by weight | MS_HF |
Phosphorus | 0.03 | percent by weight | AES_HF |
Potassium | 2.85 | percent by weight | MS_HF |
Potassium | 2.91 | percent by weight | AES_HF |
Calcium | 5.58 | percent by weight | AES_HF |
Calcium | 5.45 | percent by weight | MS_HF |
Scandium | 6.8 | parts per million by weight | MS_HF |
Scandium | 6.41 | parts per million by weight | AES_HF |
Titanium | 0.21 | percent by weight | MS_HF |
Titanium | 0.18 | percent by weight | AES_HF |
Vanadium | 43.6 | parts per million by weight | MS_HF |
Vanadium | 40.8 | parts per million by weight | AES_HF |
Chromium | 20 | parts per million by weight | AES_HF |
Chromium | 29.6 | parts per million by weight | MS_HF |
Manganese | 0.05 | percent by weight | MS_HF |
Manganese | 0.05 | percent by weight | AES_HF |
Iron | 2.21 | percent by weight | AES_HF |
Iron | 2.24 | percent by weight | MS_HF |
Cobalt | 4.57 | parts per million by weight | AES_HF |
Cobalt | 8 | parts per million by weight | MS_HF |
Nickel | 14.8 | parts per million by weight | MS_HF |
Nickel | 14.7 | parts per million by weight | AES_HF |
Copper | 19.6 | parts per million by weight | AES_HF |
Copper | 23 | parts per million by weight | MS_HF |
Zinc | 67.3 | parts per million by weight | MS_HF |
Zinc | 70.4 | parts per million by weight | AES_HF |
Gallium | 13.6 | parts per million by weight | MS_HF |
Gallium | 15 | parts per million by weight | AES_HF |
Arsenic | 24.4 | parts per million by weight | AES_HF |
Arsenic | 12.9 | parts per million by weight | MS_HF |
Rubidium | 114 | parts per million by weight | MS_HF |
Strontium | 800 | parts per million by weight | MS_HF |
Strontium | 797 | parts per million by weight | AES_HF |
Yttrium | 17.3 | parts per million by weight | MS_HF |
Yttrium | 13.7 | parts per million by weight | AES_HF |
Niobium | 12 | parts per million by weight | MS_HF |
Niobium | <8 | parts per million by weight | AES_HF |
Molybdenum | 0.78 | parts per million by weight | MS_HF |
Molybdenum | <4 | parts per million by weight | AES_HF |
Silver | <4 | parts per million by weight | AES_HF |
Silver | <2 | parts per million by weight | MS_HF |
Cadmium | <4 | parts per million by weight | AES_HF |
Cadmium | 0.16 | parts per million by weight | MS_HF |
Tin | <10 | parts per million by weight | AES_HF |
Antimony | 1.1 | parts per million by weight | MS_HF |
Cesium | 8.4 | parts per million by weight | MS_HF |
Barium | 538 | parts per million by weight | AES_HF |
Barium | 589 | parts per million by weight | MS_HF |
Lanthanum | 29.1 | parts per million by weight | MS_HF |
Lanthanum | 31.2 | parts per million by weight | AES_HF |
Cerium | 49.8 | parts per million by weight | MS_HF |
Cerium | 46 | parts per million by weight | AES_HF |
Neodymium | 21 | parts per million by weight | AES_HF |
Europium | <4 | parts per million by weight | AES_HF |
Holmium | <8 | parts per million by weight | AES_HF |
Ytterbium | <2 | parts per million by weight | AES_HF |
Tantalum | <30 | parts per million by weight | AES_HF |
Gold | <20 | parts per million by weight | AES_HF |
Thallium | 0.59 | parts per million by weight | MS_HF |
Lead | 15.6 | parts per million by weight | MS_HF |
Bismuth | 0.12 | parts per million by weight | MS_HF |
Bismuth | <20 | parts per million by weight | AES_HF |
Thorium | 8.43 | parts per million by weight | MS_HF |
Thorium | <8 | parts per million by weight | AES_HF |
Uranium | 1.38 | parts per million by weight | MS_HF |
Uranium | <200 | parts per million by weight | AES_HF |