Lithium | 490 | parts per million by weight | MS_HF |
Lithium | 512 | parts per million by weight | AES_HF |
Beryllium | <2 | parts per million by weight | AES_HF |
Beryllium | 1.8 | parts per million by weight | MS_HF |
Sodium | 6.12 | percent by weight | MS_HF |
Sodium | 5.62 | percent by weight | AES_HF |
Magnesium | 3.38 | percent by weight | MS_HF |
Magnesium | 3.16 | percent by weight | AES_HF |
Aluminum | 5.05 | percent by weight | AES_HF |
Aluminum | 5.36 | percent by weight | MS_HF |
Phosphorus | 0.03 | percent by weight | MS_HF |
Phosphorus | 0.03 | percent by weight | AES_HF |
Potassium | 2.74 | percent by weight | AES_HF |
Potassium | 2.87 | percent by weight | MS_HF |
Calcium | 4.07 | percent by weight | AES_HF |
Calcium | 4.26 | percent by weight | MS_HF |
Scandium | 7 | parts per million by weight | MS_HF |
Scandium | 6.32 | parts per million by weight | AES_HF |
Titanium | 0.26 | percent by weight | MS_HF |
Titanium | 0.17 | percent by weight | AES_HF |
Vanadium | 39.6 | parts per million by weight | AES_HF |
Vanadium | 44.5 | parts per million by weight | MS_HF |
Chromium | 16.4 | parts per million by weight | AES_HF |
Chromium | 27.7 | parts per million by weight | MS_HF |
Manganese | 0.05 | percent by weight | AES_HF |
Manganese | 0.05 | percent by weight | MS_HF |
Iron | 2.11 | percent by weight | AES_HF |
Iron | 2.23 | percent by weight | MS_HF |
Cobalt | 8.2 | parts per million by weight | MS_HF |
Cobalt | 4.98 | parts per million by weight | AES_HF |
Nickel | 14.2 | parts per million by weight | AES_HF |
Nickel | 15.4 | parts per million by weight | MS_HF |
Copper | 14.6 | parts per million by weight | AES_HF |
Copper | 19.1 | parts per million by weight | MS_HF |
Zinc | 64.5 | parts per million by weight | MS_HF |
Zinc | 63.7 | parts per million by weight | AES_HF |
Gallium | 12.6 | parts per million by weight | MS_HF |
Gallium | 12.8 | parts per million by weight | AES_HF |
Arsenic | 33 | parts per million by weight | AES_HF |
Arsenic | 30.4 | parts per million by weight | MS_HF |
Rubidium | 112 | parts per million by weight | MS_HF |
Strontium | 635 | parts per million by weight | MS_HF |
Strontium | 608 | parts per million by weight | AES_HF |
Yttrium | 14.7 | parts per million by weight | MS_HF |
Yttrium | 11.5 | parts per million by weight | AES_HF |
Niobium | 9.8 | parts per million by weight | MS_HF |
Niobium | <8 | parts per million by weight | AES_HF |
Molybdenum | 4.6 | parts per million by weight | MS_HF |
Molybdenum | <4 | parts per million by weight | AES_HF |
Silver | <4 | parts per million by weight | AES_HF |
Silver | <2 | parts per million by weight | MS_HF |
Cadmium | <4 | parts per million by weight | AES_HF |
Cadmium | 0.18 | parts per million by weight | MS_HF |
Tin | <10 | parts per million by weight | AES_HF |
Antimony | 0.97 | parts per million by weight | MS_HF |
Cesium | 8.6 | parts per million by weight | MS_HF |
Barium | 421 | parts per million by weight | AES_HF |
Barium | 485 | parts per million by weight | MS_HF |
Lanthanum | 22.9 | parts per million by weight | MS_HF |
Lanthanum | 24 | parts per million by weight | AES_HF |
Cerium | 39.2 | parts per million by weight | MS_HF |
Cerium | 34.4 | parts per million by weight | AES_HF |
Neodymium | 16.3 | parts per million by weight | AES_HF |
Europium | <4 | parts per million by weight | AES_HF |
Holmium | <8 | parts per million by weight | AES_HF |
Ytterbium | <2 | parts per million by weight | AES_HF |
Tantalum | <30 | parts per million by weight | AES_HF |
Gold | <20 | parts per million by weight | AES_HF |
Thallium | 0.56 | parts per million by weight | MS_HF |
Lead | 13.8 | parts per million by weight | MS_HF |
Bismuth | 0.13 | parts per million by weight | MS_HF |
Bismuth | <20 | parts per million by weight | AES_HF |
Thorium | 7.24 | parts per million by weight | MS_HF |
Thorium | <8 | parts per million by weight | AES_HF |
Uranium | 1.46 | parts per million by weight | MS_HF |
Uranium | <200 | parts per million by weight | AES_HF |