Lithium | 489 | parts per million by weight | MS_HF |
Lithium | 519 | parts per million by weight | AES_HF |
Beryllium | <2 | parts per million by weight | AES_HF |
Beryllium | 1.8 | parts per million by weight | MS_HF |
Sodium | 4.88 | percent by weight | MS_HF |
Sodium | 4.64 | percent by weight | AES_HF |
Magnesium | 3.21 | percent by weight | AES_HF |
Magnesium | 3.34 | percent by weight | MS_HF |
Aluminum | 5.32 | percent by weight | AES_HF |
Aluminum | 5.48 | percent by weight | MS_HF |
Phosphorus | 0.03 | percent by weight | MS_HF |
Phosphorus | 0.03 | percent by weight | AES_HF |
Potassium | 2.84 | percent by weight | AES_HF |
Potassium | 2.91 | percent by weight | MS_HF |
Calcium | 4.56 | percent by weight | AES_HF |
Calcium | 4.66 | percent by weight | MS_HF |
Scandium | 7.3 | parts per million by weight | MS_HF |
Scandium | 6.62 | parts per million by weight | AES_HF |
Titanium | 0.18 | percent by weight | AES_HF |
Titanium | 0.26 | percent by weight | MS_HF |
Vanadium | 41.5 | parts per million by weight | AES_HF |
Vanadium | 45.2 | parts per million by weight | MS_HF |
Chromium | 17.8 | parts per million by weight | AES_HF |
Chromium | 27.7 | parts per million by weight | MS_HF |
Manganese | 0.05 | percent by weight | AES_HF |
Manganese | 0.05 | percent by weight | MS_HF |
Iron | 2.2 | percent by weight | AES_HF |
Iron | 2.26 | percent by weight | MS_HF |
Cobalt | 8.4 | parts per million by weight | MS_HF |
Cobalt | 9.13 | parts per million by weight | AES_HF |
Nickel | 15.7 | parts per million by weight | MS_HF |
Nickel | 15.3 | parts per million by weight | AES_HF |
Copper | 16.2 | parts per million by weight | AES_HF |
Copper | 20.3 | parts per million by weight | MS_HF |
Zinc | 64.6 | parts per million by weight | MS_HF |
Zinc | 67 | parts per million by weight | AES_HF |
Gallium | 12.9 | parts per million by weight | MS_HF |
Gallium | 12.8 | parts per million by weight | AES_HF |
Arsenic | 28.3 | parts per million by weight | AES_HF |
Arsenic | 30 | parts per million by weight | MS_HF |
Rubidium | 113 | parts per million by weight | MS_HF |
Strontium | 662 | parts per million by weight | MS_HF |
Strontium | 650 | parts per million by weight | AES_HF |
Yttrium | 15.8 | parts per million by weight | MS_HF |
Yttrium | 12.3 | parts per million by weight | AES_HF |
Niobium | 9.9 | parts per million by weight | MS_HF |
Niobium | 8.64 | parts per million by weight | AES_HF |
Molybdenum | 3.2 | parts per million by weight | MS_HF |
Molybdenum | <4 | parts per million by weight | AES_HF |
Silver | <4 | parts per million by weight | AES_HF |
Silver | <2 | parts per million by weight | MS_HF |
Cadmium | <4 | parts per million by weight | AES_HF |
Cadmium | 0.14 | parts per million by weight | MS_HF |
Tin | <10 | parts per million by weight | AES_HF |
Antimony | 0.99 | parts per million by weight | MS_HF |
Cesium | 8.8 | parts per million by weight | MS_HF |
Barium | 446 | parts per million by weight | AES_HF |
Barium | 504 | parts per million by weight | MS_HF |
Lanthanum | 27.5 | parts per million by weight | MS_HF |
Lanthanum | 28.9 | parts per million by weight | AES_HF |
Cerium | 47.8 | parts per million by weight | MS_HF |
Cerium | 43.6 | parts per million by weight | AES_HF |
Neodymium | 19.2 | parts per million by weight | AES_HF |
Europium | <4 | parts per million by weight | AES_HF |
Holmium | <8 | parts per million by weight | AES_HF |
Ytterbium | <2 | parts per million by weight | AES_HF |
Tantalum | <30 | parts per million by weight | AES_HF |
Gold | <20 | parts per million by weight | AES_HF |
Thallium | 0.59 | parts per million by weight | MS_HF |
Lead | 14.7 | parts per million by weight | MS_HF |
Bismuth | 0.13 | parts per million by weight | MS_HF |
Bismuth | <20 | parts per million by weight | AES_HF |
Thorium | 8.41 | parts per million by weight | MS_HF |
Thorium | <8 | parts per million by weight | AES_HF |
Uranium | 1.47 | parts per million by weight | MS_HF |
Uranium | <200 | parts per million by weight | AES_HF |