Lithium | 222 | parts per million by weight | MS_HF |
Lithium | 229 | parts per million by weight | AES_HF |
Beryllium | <2 | parts per million by weight | AES_HF |
Beryllium | 2 | parts per million by weight | MS_HF |
Sodium | 2.82 | percent by weight | AES_HF |
Sodium | 2.87 | percent by weight | MS_HF |
Magnesium | 2.86 | percent by weight | AES_HF |
Magnesium | 2.96 | percent by weight | MS_HF |
Aluminum | 5.91 | percent by weight | AES_HF |
Aluminum | 5.98 | percent by weight | MS_HF |
Phosphorus | 0.04 | percent by weight | MS_HF |
Phosphorus | 0.04 | percent by weight | AES_HF |
Potassium | 2.87 | percent by weight | AES_HF |
Potassium | 2.85 | percent by weight | MS_HF |
Calcium | 5.52 | percent by weight | MS_HF |
Calcium | 5.58 | percent by weight | AES_HF |
Scandium | 6.9 | parts per million by weight | MS_HF |
Scandium | 6.43 | parts per million by weight | AES_HF |
Titanium | 0.28 | percent by weight | MS_HF |
Titanium | 0.2 | percent by weight | AES_HF |
Vanadium | 43.6 | parts per million by weight | MS_HF |
Vanadium | 41.1 | parts per million by weight | AES_HF |
Chromium | 21.6 | parts per million by weight | AES_HF |
Chromium | 29.6 | parts per million by weight | MS_HF |
Manganese | 0.05 | percent by weight | AES_HF |
Manganese | 0.05 | percent by weight | MS_HF |
Iron | 2.13 | percent by weight | AES_HF |
Iron | 2.16 | percent by weight | MS_HF |
Cobalt | 5.15 | parts per million by weight | AES_HF |
Cobalt | 7.6 | parts per million by weight | MS_HF |
Nickel | 13.4 | parts per million by weight | AES_HF |
Nickel | 13.7 | parts per million by weight | MS_HF |
Copper | 18.1 | parts per million by weight | MS_HF |
Copper | 13.8 | parts per million by weight | AES_HF |
Zinc | 58.7 | parts per million by weight | MS_HF |
Zinc | 61.2 | parts per million by weight | AES_HF |
Gallium | 13.7 | parts per million by weight | MS_HF |
Gallium | 14.8 | parts per million by weight | AES_HF |
Arsenic | <20 | parts per million by weight | AES_HF |
Arsenic | 12 | parts per million by weight | MS_HF |
Rubidium | 111 | parts per million by weight | MS_HF |
Strontium | 837 | parts per million by weight | MS_HF |
Strontium | 830 | parts per million by weight | AES_HF |
Yttrium | 18.6 | parts per million by weight | MS_HF |
Yttrium | 14.6 | parts per million by weight | AES_HF |
Niobium | 11 | parts per million by weight | MS_HF |
Niobium | <8 | parts per million by weight | AES_HF |
Molybdenum | 0.68 | parts per million by weight | MS_HF |
Molybdenum | <4 | parts per million by weight | AES_HF |
Silver | <4 | parts per million by weight | AES_HF |
Silver | <2 | parts per million by weight | MS_HF |
Cadmium | <4 | parts per million by weight | AES_HF |
Cadmium | 0.16 | parts per million by weight | MS_HF |
Tin | <10 | parts per million by weight | AES_HF |
Antimony | 1 | parts per million by weight | MS_HF |
Cesium | 7.5 | parts per million by weight | MS_HF |
Barium | 656 | parts per million by weight | MS_HF |
Barium | 587 | parts per million by weight | AES_HF |
Lanthanum | 31.5 | parts per million by weight | MS_HF |
Lanthanum | 32.4 | parts per million by weight | AES_HF |
Cerium | 56.3 | parts per million by weight | MS_HF |
Cerium | 50.3 | parts per million by weight | AES_HF |
Neodymium | 22.4 | parts per million by weight | AES_HF |
Europium | <4 | parts per million by weight | AES_HF |
Holmium | <8 | parts per million by weight | AES_HF |
Ytterbium | <2 | parts per million by weight | AES_HF |
Tantalum | <30 | parts per million by weight | AES_HF |
Gold | <20 | parts per million by weight | AES_HF |
Thallium | 0.59 | parts per million by weight | MS_HF |
Lead | 16.4 | parts per million by weight | MS_HF |
Bismuth | 0.13 | parts per million by weight | MS_HF |
Bismuth | <20 | parts per million by weight | AES_HF |
Thorium | 8.64 | parts per million by weight | MS_HF |
Thorium | <8 | parts per million by weight | AES_HF |
Uranium | 1.58 | parts per million by weight | MS_HF |
Uranium | <200 | parts per million by weight | AES_HF |