Lithium | 22 | parts per million by weight | MS_HF |
Lithium | 20.6 | parts per million by weight | AES_HF |
Beryllium | 0.36 | parts per million by weight | MS_HF |
Beryllium | <1 | parts per million by weight | AES_HF |
Sodium | 19.3 | percent by weight | AES_HF |
Magnesium | 0.31 | percent by weight | MS_HF |
Magnesium | 0.3 | percent by weight | AES_HF |
Aluminum | 1.59 | percent by weight | MS_HF |
Aluminum | 1.45 | percent by weight | AES_HF |
Phosphorus | 0.02 | percent by weight | MS_HF |
Phosphorus | 0.02 | percent by weight | AES_HF |
Potassium | 0.95 | percent by weight | MS_HF |
Potassium | 0.9 | percent by weight | AES_HF |
Calcium | 2.87 | percent by weight | MS_HF |
Calcium | 2.6 | percent by weight | AES_HF |
Scandium | 1.6 | parts per million by weight | MS_HF |
Scandium | <2 | parts per million by weight | AES_HF |
Titanium | 0.06 | percent by weight | MS_HF |
Titanium | 0.05 | percent by weight | AES_HF |
Vanadium | 7.97 | parts per million by weight | AES_HF |
Vanadium | 9.9 | parts per million by weight | MS_HF |
Chromium | 17.8 | parts per million by weight | MS_HF |
Chromium | 13.6 | parts per million by weight | AES_HF |
Manganese | 0.01 | percent by weight | MS_HF |
Manganese | 0.01 | percent by weight | AES_HF |
Iron | 0.39 | percent by weight | MS_HF |
Iron | 0.38 | percent by weight | AES_HF |
Cobalt | 1.2 | parts per million by weight | MS_HF |
Cobalt | 1.74 | parts per million by weight | AES_HF |
Nickel | 2.12 | parts per million by weight | AES_HF |
Nickel | 2.5 | parts per million by weight | MS_HF |
Copper | 4 | parts per million by weight | MS_HF |
Copper | 3.08 | parts per million by weight | AES_HF |
Zinc | 9 | parts per million by weight | MS_HF |
Zinc | 7.2 | parts per million by weight | AES_HF |
Gallium | 2.8 | parts per million by weight | MS_HF |
Gallium | <4 | parts per million by weight | AES_HF |
Arsenic | 7.5 | parts per million by weight | MS_HF |
Arsenic | 10.9 | parts per million by weight | AES_HF |
Rubidium | 24.8 | parts per million by weight | MS_HF |
Strontium | 195 | parts per million by weight | MS_HF |
Strontium | 184 | parts per million by weight | AES_HF |
Yttrium | 5.8 | parts per million by weight | MS_HF |
Yttrium | 4.23 | parts per million by weight | AES_HF |
Niobium | 2.5 | parts per million by weight | MS_HF |
Niobium | <4 | parts per million by weight | AES_HF |
Molybdenum | 1.2 | parts per million by weight | MS_HF |
Molybdenum | <2 | parts per million by weight | AES_HF |
Silver | <2 | parts per million by weight | MS_HF |
Silver | <2 | parts per million by weight | AES_HF |
Cadmium | 0.02 | parts per million by weight | MS_HF |
Cadmium | <2 | parts per million by weight | AES_HF |
Tin | <5 | parts per million by weight | AES_HF |
Antimony | 0.22 | parts per million by weight | MS_HF |
Cesium | 0.88 | parts per million by weight | MS_HF |
Barium | 259 | parts per million by weight | MS_HF |
Barium | 258 | parts per million by weight | AES_HF |
Lanthanum | 11.7 | parts per million by weight | MS_HF |
Lanthanum | 10.6 | parts per million by weight | AES_HF |
Cerium | 26.6 | parts per million by weight | MS_HF |
Cerium | 26 | parts per million by weight | AES_HF |
Neodymium | 9.95 | parts per million by weight | AES_HF |
Europium | <2 | parts per million by weight | AES_HF |
Holmium | <4 | parts per million by weight | AES_HF |
Ytterbium | <1 | parts per million by weight | AES_HF |
Tantalum | <20 | parts per million by weight | AES_HF |
Gold | <8 | parts per million by weight | AES_HF |
Thallium | 0.17 | parts per million by weight | MS_HF |
Lead | 5.09 | parts per million by weight | AES_HF |
Lead | 5.3 | parts per million by weight | MS_HF |
Bismuth | <0.06 | parts per million by weight | MS_HF |
Bismuth | <10 | parts per million by weight | AES_HF |
Thorium | 4.14 | parts per million by weight | MS_HF |
Thorium | 4.74 | parts per million by weight | AES_HF |
Uranium | 0.85 | parts per million by weight | MS_HF |
Uranium | <100 | parts per million by weight | AES_HF |