Lithium | 18.2 | parts per million by weight | MS_HF |
Lithium | 17.4 | parts per million by weight | AES_HF |
Beryllium | <1 | parts per million by weight | AES_HF |
Beryllium | 0.12 | parts per million by weight | MS_HF |
Sodium | 27.1 | percent by weight | AES_HF |
Magnesium | 0.08 | percent by weight | AES_HF |
Magnesium | 0.09 | percent by weight | MS_HF |
Aluminum | 0.41 | percent by weight | AES_HF |
Aluminum | 0.46 | percent by weight | MS_HF |
Phosphorus | 0.00551 | percent by weight | MS_HF |
Phosphorus | 0.00518 | percent by weight | AES_HF |
Potassium | 0.25 | percent by weight | AES_HF |
Potassium | 0.25 | percent by weight | MS_HF |
Calcium | 0.43 | percent by weight | AES_HF |
Calcium | 0.47 | percent by weight | MS_HF |
Scandium | <2 | parts per million by weight | AES_HF |
Scandium | 0.5 | parts per million by weight | MS_HF |
Titanium | 0.02 | percent by weight | MS_HF |
Titanium | 0.01 | percent by weight | AES_HF |
Vanadium | 2.74 | parts per million by weight | AES_HF |
Vanadium | 3.1 | parts per million by weight | MS_HF |
Chromium | 3.13 | parts per million by weight | AES_HF |
Chromium | 4.7 | parts per million by weight | MS_HF |
Manganese | 0.00246 | percent by weight | AES_HF |
Manganese | 0.00267 | percent by weight | MS_HF |
Iron | 0.13 | percent by weight | AES_HF |
Iron | 0.13 | percent by weight | MS_HF |
Cobalt | <1 | parts per million by weight | AES_HF |
Cobalt | 0.37 | parts per million by weight | MS_HF |
Nickel | <2 | parts per million by weight | AES_HF |
Nickel | 0.8 | parts per million by weight | MS_HF |
Copper | <1 | parts per million by weight | AES_HF |
Copper | 1.5 | parts per million by weight | MS_HF |
Zinc | 4 | parts per million by weight | MS_HF |
Zinc | 2.85 | parts per million by weight | AES_HF |
Gallium | 0.94 | parts per million by weight | MS_HF |
Gallium | <4 | parts per million by weight | AES_HF |
Arsenic | <10 | parts per million by weight | AES_HF |
Arsenic | 9.1 | parts per million by weight | MS_HF |
Rubidium | 6.7 | parts per million by weight | MS_HF |
Strontium | 60.2 | parts per million by weight | MS_HF |
Strontium | 58.5 | parts per million by weight | AES_HF |
Yttrium | 1.7 | parts per million by weight | MS_HF |
Yttrium | <2 | parts per million by weight | AES_HF |
Niobium | 1.8 | parts per million by weight | MS_HF |
Niobium | <4 | parts per million by weight | AES_HF |
Molybdenum | 3.4 | parts per million by weight | MS_HF |
Molybdenum | <2 | parts per million by weight | AES_HF |
Silver | <2 | parts per million by weight | AES_HF |
Silver | <2 | parts per million by weight | MS_HF |
Cadmium | 0.02 | parts per million by weight | MS_HF |
Cadmium | <2 | parts per million by weight | AES_HF |
Tin | <5 | parts per million by weight | AES_HF |
Antimony | 0.1 | parts per million by weight | MS_HF |
Cesium | 0.24 | parts per million by weight | MS_HF |
Barium | 68.8 | parts per million by weight | AES_HF |
Barium | 63.7 | parts per million by weight | MS_HF |
Lanthanum | 2.6 | parts per million by weight | MS_HF |
Lanthanum | 2.36 | parts per million by weight | AES_HF |
Cerium | 4.7 | parts per million by weight | MS_HF |
Cerium | <4 | parts per million by weight | AES_HF |
Neodymium | <4 | parts per million by weight | AES_HF |
Europium | <2 | parts per million by weight | AES_HF |
Holmium | <4 | parts per million by weight | AES_HF |
Ytterbium | <1 | parts per million by weight | AES_HF |
Tantalum | <20 | parts per million by weight | AES_HF |
Gold | <8 | parts per million by weight | AES_HF |
Thallium | <0.08 | parts per million by weight | MS_HF |
Lead | <4 | parts per million by weight | AES_HF |
Lead | 1.15 | parts per million by weight | MS_HF |
Bismuth | <0.06 | parts per million by weight | MS_HF |
Bismuth | <10 | parts per million by weight | AES_HF |
Thorium | 0.69 | parts per million by weight | MS_HF |
Thorium | <4 | parts per million by weight | AES_HF |
Uranium | 0.27 | parts per million by weight | MS_HF |
Uranium | <100 | parts per million by weight | AES_HF |