Lithium | 33.4 | parts per million by weight | MS_HF |
Lithium | 34.5 | parts per million by weight | AES_HF |
Beryllium | 0.6 | parts per million by weight | MS_HF |
Beryllium | <1 | parts per million by weight | AES_HF |
Sodium | 18.3 | percent by weight | AES_HF |
Magnesium | 0.37 | percent by weight | AES_HF |
Magnesium | 0.42 | percent by weight | MS_HF |
Aluminum | 2.1 | percent by weight | AES_HF |
Aluminum | 2.21 | percent by weight | MS_HF |
Phosphorus | 0.01 | percent by weight | MS_HF |
Phosphorus | 0.01 | percent by weight | AES_HF |
Potassium | 1.02 | percent by weight | AES_HF |
Potassium | 0.99 | percent by weight | MS_HF |
Calcium | 2.01 | percent by weight | AES_HF |
Calcium | 2.1 | percent by weight | MS_HF |
Scandium | 2 | parts per million by weight | MS_HF |
Scandium | <2 | parts per million by weight | AES_HF |
Titanium | 0.08 | percent by weight | MS_HF |
Titanium | 0.09 | percent by weight | AES_HF |
Vanadium | 12.1 | parts per million by weight | AES_HF |
Vanadium | 13.6 | parts per million by weight | MS_HF |
Chromium | 44.8 | parts per million by weight | AES_HF |
Chromium | 47.1 | parts per million by weight | MS_HF |
Manganese | 0.01 | percent by weight | AES_HF |
Manganese | 0.01 | percent by weight | MS_HF |
Iron | 0.7 | percent by weight | AES_HF |
Iron | 0.68 | percent by weight | MS_HF |
Cobalt | 2.5 | parts per million by weight | AES_HF |
Cobalt | 1.9 | parts per million by weight | MS_HF |
Nickel | 10.2 | parts per million by weight | AES_HF |
Nickel | 9.3 | parts per million by weight | MS_HF |
Copper | 5.75 | parts per million by weight | AES_HF |
Copper | 7.1 | parts per million by weight | MS_HF |
Zinc | 17 | parts per million by weight | MS_HF |
Zinc | 15.1 | parts per million by weight | AES_HF |
Gallium | 4.4 | parts per million by weight | MS_HF |
Gallium | <4 | parts per million by weight | AES_HF |
Arsenic | <10 | parts per million by weight | AES_HF |
Arsenic | 6.1 | parts per million by weight | MS_HF |
Rubidium | 30.3 | parts per million by weight | MS_HF |
Strontium | 264 | parts per million by weight | AES_HF |
Strontium | 272 | parts per million by weight | MS_HF |
Yttrium | 7.3 | parts per million by weight | MS_HF |
Yttrium | 5.46 | parts per million by weight | AES_HF |
Niobium | 5.2 | parts per million by weight | MS_HF |
Niobium | <4 | parts per million by weight | AES_HF |
Molybdenum | 2 | parts per million by weight | MS_HF |
Molybdenum | <2 | parts per million by weight | AES_HF |
Silver | <2 | parts per million by weight | AES_HF |
Silver | <2 | parts per million by weight | MS_HF |
Cadmium | <2 | parts per million by weight | AES_HF |
Cadmium | 0.05 | parts per million by weight | MS_HF |
Tin | <5 | parts per million by weight | AES_HF |
Antimony | 0.28 | parts per million by weight | MS_HF |
Cesium | 1.1 | parts per million by weight | MS_HF |
Barium | 150 | parts per million by weight | AES_HF |
Barium | 254 | parts per million by weight | MS_HF |
Lanthanum | 12.2 | parts per million by weight | MS_HF |
Lanthanum | 13.1 | parts per million by weight | AES_HF |
Cerium | 21.2 | parts per million by weight | MS_HF |
Cerium | 22.9 | parts per million by weight | AES_HF |
Neodymium | 10.1 | parts per million by weight | AES_HF |
Europium | <2 | parts per million by weight | AES_HF |
Holmium | <4 | parts per million by weight | AES_HF |
Ytterbium | <1 | parts per million by weight | AES_HF |
Tantalum | <20 | parts per million by weight | AES_HF |
Gold | <8 | parts per million by weight | AES_HF |
Thallium | 0.16 | parts per million by weight | MS_HF |
Lead | 4.54 | parts per million by weight | AES_HF |
Lead | 5.3 | parts per million by weight | MS_HF |
Bismuth | <0.06 | parts per million by weight | MS_HF |
Bismuth | <10 | parts per million by weight | AES_HF |
Thorium | 3.12 | parts per million by weight | MS_HF |
Thorium | <4 | parts per million by weight | AES_HF |
Uranium | 0.61 | parts per million by weight | MS_HF |
Uranium | <100 | parts per million by weight | AES_HF |