Lithium | 9.4 | parts per million by weight | AES_AR_P |
Beryllium | 0.98 | parts per million by weight | AES_AR_P |
Beryllium | 1 | parts per million by weight | ES_SQ |
Boron | 8.6 | parts per million by weight | AES_AR_P |
Boron | 100 | parts per million by weight | ES_SQ |
Sodium | 0.08 | percent by weight | AES_AR_P |
Magnesium | 2.1 | percent by weight | AES_AR_P |
Magnesium | 3 | percent by weight | ES_SQ |
Aluminum | 1.7 | percent by weight | AES_AR_P |
Phosphorus | 0.04 | percent by weight | AES_AR_P |
Potassium | 0.12 | percent by weight | AES_AR_P |
Calcium | 0.47 | percent by weight | AES_AR_P |
Calcium | 2 | percent by weight | ES_SQ |
Scandium | 50 | parts per million by weight | ES_SQ |
Titanium | 0.03 | percent by weight | AES_AR_P |
Titanium | 0.5 | percent by weight | ES_SQ |
Vanadium | 42 | parts per million by weight | AES_AR_P |
Vanadium | 200 | parts per million by weight | ES_SQ |
Chromium | 150 | parts per million by weight | ES_SQ |
Chromium | 16 | parts per million by weight | AES_AR_P |
Manganese | 0.15 | percent by weight | ES_SQ |
Manganese | 0.03 | percent by weight | AES_AR_P |
Iron | 10 | percent by weight | ES_SQ |
Iron | 1 | percent by weight | AES_AR_P |
Cobalt | 10 | parts per million by weight | AES_AR_P |
Cobalt | 100 | parts per million by weight | ES_SQ |
Nickel | 12 | parts per million by weight | AES_AR_P |
Nickel | 70 | parts per million by weight | ES_SQ |
Copper | 32 | parts per million by weight | AES_AR_P |
Copper | 67 | parts per million by weight | AA_F_HNO3_P |
Copper | 100 | parts per million by weight | ES_SQ |
Zinc | 46 | parts per million by weight | AES_AR_P |
Zinc | 90 | parts per million by weight | AA_F_HNO3_P |
Zinc | N200 | parts per million by weight | ES_SQ |
Arsenic | 9.6 | parts per million by weight | AES_AR_P |
Arsenic | N200 | parts per million by weight | ES_SQ |
Strontium | 32 | parts per million by weight | AES_AR_P |
Strontium | 300 | parts per million by weight | ES_SQ |
Yttrium | 2.7 | parts per million by weight | AES_AR_P |
Yttrium | 50 | parts per million by weight | ES_SQ |
Zirconium | 2.2 | parts per million by weight | AES_AR_P |
Zirconium | 150 | parts per million by weight | ES_SQ |
Niobium | 300 | parts per million by weight | AES_AR_P |
Niobium | L20 | parts per million by weight | ES_SQ |
Molybdenum | N0.35 | parts per million by weight | AES_AR_P |
Molybdenum | N5 | parts per million by weight | ES_SQ |
Silver | N0.5 | parts per million by weight | ES_SQ |
Silver | N0.3 | parts per million by weight | AES_AR_P |
Cadmium | 2.4 | parts per million by weight | AES_AR_P |
Cadmium | N20 | parts per million by weight | ES_SQ |
Tin | N10 | parts per million by weight | AES_AR_P |
Tin | N10 | parts per million by weight | ES_SQ |
Antimony | N5 | parts per million by weight | AES_AR_P |
Antimony | N100 | parts per million by weight | ES_SQ |
Barium | 64 | parts per million by weight | AES_AR_P |
Barium | 500 | parts per million by weight | ES_SQ |
Lanthanum | 2 | parts per million by weight | AES_AR_P |
Lanthanum | 50 | parts per million by weight | ES_SQ |
Cerium | 4.2 | parts per million by weight | AES_AR_P |
Tungsten | 12 | parts per million by weight | AES_AR_P |
Tungsten | N50 | parts per million by weight | ES_SQ |
Gold | N10 | parts per million by weight | ES_SQ |
Lead | 10 | parts per million by weight | AES_AR_P |
Lead | 50 | parts per million by weight | ES_SQ |
Lead | 40 | parts per million by weight | AA_F_HNO3_P |
Bismuth | N10 | parts per million by weight | ES_SQ |
Bismuth | 4.9 | parts per million by weight | AES_AR_P |