Beryllium | N0.01 | parts per million by weight | AES_AR_P |
Beryllium | 1 | parts per million by weight | ES_SQ |
Boron | L10 | parts per million by weight | ES_SQ |
Boron | N0.1 | parts per million by weight | AES_AR_P |
Magnesium | 0.42 | percent by weight | AES_AR_P |
Magnesium | 1 | percent by weight | ES_SQ |
Aluminum | 0.7 | percent by weight | AES_AR_P |
Phosphorus | 0.09 | percent by weight | AES_AR_P |
Calcium | 1.1 | percent by weight | AES_AR_P |
Calcium | 2 | percent by weight | ES_SQ |
Scandium | 15 | parts per million by weight | ES_SQ |
Titanium | 0.07 | percent by weight | AES_AR_P |
Titanium | 0.5 | percent by weight | ES_SQ |
Vanadium | 58 | parts per million by weight | AES_AR_P |
Vanadium | 100 | parts per million by weight | ES_SQ |
Chromium | 30 | parts per million by weight | ES_SQ |
Chromium | 21 | parts per million by weight | AES_AR_P |
Manganese | 0.01 | percent by weight | AES_AR_P |
Manganese | 0.07 | percent by weight | ES_SQ |
Iron | 2.6 | percent by weight | AES_AR_P |
Iron | 5 | percent by weight | ES_SQ |
Cobalt | 10 | parts per million by weight | ES_SQ |
Cobalt | N2 | parts per million by weight | AES_AR_P |
Nickel | L5 | parts per million by weight | ES_SQ |
Nickel | 2.7 | parts per million by weight | AES_AR_P |
Copper | 3 | parts per million by weight | AES_AR_P |
Copper | 7 | parts per million by weight | ES_SQ |
Zinc | 26 | parts per million by weight | AES_AR_P |
Zinc | N200 | parts per million by weight | ES_SQ |
Arsenic | N5 | parts per million by weight | AES_AR_P |
Arsenic | N200 | parts per million by weight | ES_SQ |
Strontium | 25 | parts per million by weight | AES_AR_P |
Strontium | 500 | parts per million by weight | ES_SQ |
Yttrium | N0.04 | parts per million by weight | AES_AR_P |
Yttrium | 30 | parts per million by weight | ES_SQ |
Zirconium | N1 | parts per million by weight | AES_AR_P |
Zirconium | 300 | parts per million by weight | ES_SQ |
Niobium | L20 | parts per million by weight | ES_SQ |
Niobium | N1 | parts per million by weight | AES_AR_P |
Molybdenum | N0.4 | parts per million by weight | AES_AR_P |
Molybdenum | N5 | parts per million by weight | ES_SQ |
Silver | N0.5 | parts per million by weight | ES_SQ |
Silver | N0.3 | parts per million by weight | AES_AR_P |
Cadmium | N0.4 | parts per million by weight | AES_AR_P |
Cadmium | N20 | parts per million by weight | ES_SQ |
Tin | N4 | parts per million by weight | AES_AR_P |
Tin | N10 | parts per million by weight | ES_SQ |
Antimony | N5 | parts per million by weight | AES_AR_P |
Antimony | N100 | parts per million by weight | ES_SQ |
Barium | 500 | parts per million by weight | ES_SQ |
Barium | 170 | parts per million by weight | AES_AR_P |
Lanthanum | 4.3 | parts per million by weight | AES_AR_P |
Lanthanum | 50 | parts per million by weight | ES_SQ |
Cerium | 7.2 | parts per million by weight | AES_AR_P |
Tungsten | N5 | parts per million by weight | AES_AR_P |
Tungsten | N50 | parts per million by weight | ES_SQ |
Gold | N10 | parts per million by weight | ES_SQ |
Lead | N2.4 | parts per million by weight | AES_AR_P |
Lead | 15 | parts per million by weight | ES_SQ |
Bismuth | N8 | parts per million by weight | AES_AR_P |
Bismuth | N10 | parts per million by weight | ES_SQ |
Thorium | N100 | parts per million by weight | ES_SQ |