Beryllium | 1 | parts per million by weight | ES_SQ |
Beryllium | N0.01 | parts per million by weight | AES_AR_P |
Boron | N0.1 | parts per million by weight | AES_AR_P |
Boron | 30 | parts per million by weight | ES_SQ |
Magnesium | 0.68 | percent by weight | AES_AR_P |
Magnesium | 1.5 | percent by weight | ES_SQ |
Aluminum | 0.82 | percent by weight | AES_AR_P |
Phosphorus | 0.13 | percent by weight | AES_AR_P |
Calcium | 0.35 | percent by weight | AES_AR_P |
Calcium | 0.2 | percent by weight | ES_SQ |
Scandium | 20 | parts per million by weight | ES_SQ |
Titanium | 0.02 | percent by weight | AES_AR_P |
Titanium | 0.7 | percent by weight | ES_SQ |
Vanadium | 24 | parts per million by weight | AES_AR_P |
Vanadium | 300 | parts per million by weight | ES_SQ |
Chromium | L13 | parts per million by weight | AES_AR_P |
Chromium | 30 | parts per million by weight | ES_SQ |
Manganese | 0.14 | percent by weight | AES_AR_P |
Manganese | 0.3 | percent by weight | ES_SQ |
Iron | 4.2 | percent by weight | AES_AR_P |
Iron | 5 | percent by weight | ES_SQ |
Cobalt | 50 | parts per million by weight | ES_SQ |
Cobalt | 20 | parts per million by weight | AES_AR_P |
Nickel | 15 | parts per million by weight | ES_SQ |
Nickel | 11 | parts per million by weight | AES_AR_P |
Copper | 88 | parts per million by weight | AES_AR_P |
Copper | 200 | parts per million by weight | ES_SQ |
Zinc | 190 | parts per million by weight | AES_AR_P |
Zinc | 200 | parts per million by weight | ES_SQ |
Zinc | 160 | parts per million by weight | AA_F_AZ_H2O2_P |
Arsenic | L20 | parts per million by weight | AES_AR_P |
Arsenic | 20 | parts per million by weight | AA_F_AZ_H2O2_P |
Arsenic | N200 | parts per million by weight | ES_SQ |
Strontium | 36 | parts per million by weight | AES_AR_P |
Strontium | 500 | parts per million by weight | ES_SQ |
Yttrium | N0.04 | parts per million by weight | AES_AR_P |
Yttrium | 30 | parts per million by weight | ES_SQ |
Zirconium | N1 | parts per million by weight | AES_AR_P |
Zirconium | 100 | parts per million by weight | ES_SQ |
Niobium | N1 | parts per million by weight | AES_AR_P |
Niobium | N20 | parts per million by weight | ES_SQ |
Molybdenum | N5 | parts per million by weight | ES_SQ |
Molybdenum | 0.84 | parts per million by weight | AES_AR_P |
Silver | 0.32 | parts per million by weight | AES_AR_P |
Silver | L0.5 | parts per million by weight | ES_SQ |
Cadmium | N0.4 | parts per million by weight | AES_AR_P |
Cadmium | 1.3 | parts per million by weight | AA_F_AZ_H2O2_P |
Cadmium | N20 | parts per million by weight | ES_SQ |
Tin | N4 | parts per million by weight | AES_AR_P |
Tin | N10 | parts per million by weight | ES_SQ |
Antimony | N2 | parts per million by weight | AA_F_AZ_Fuse_P |
Antimony | N5 | parts per million by weight | AES_AR_P |
Antimony | N100 | parts per million by weight | ES_SQ |
Barium | 300 | parts per million by weight | ES_SQ |
Barium | 14 | parts per million by weight | AES_AR_P |
Lanthanum | 30 | parts per million by weight | ES_SQ |
Lanthanum | 3.8 | parts per million by weight | AES_AR_P |
Cerium | 5.6 | parts per million by weight | AES_AR_P |
Tungsten | N5 | parts per million by weight | AES_AR_P |
Tungsten | N50 | parts per million by weight | ES_SQ |
Gold | 0.4 | parts per million by weight | AA_F_HBr |
Gold | N10 | parts per million by weight | ES_SQ |
Lead | 100 | parts per million by weight | ES_SQ |
Lead | 62 | parts per million by weight | AES_AR_P |
Bismuth | N8 | parts per million by weight | AES_AR_P |
Bismuth | N1 | parts per million by weight | AA_F_AZ_H2O2_P |
Bismuth | N10 | parts per million by weight | ES_SQ |
Thorium | N100 | parts per million by weight | ES_SQ |
SplWtAu | 10 | grams | GV |