Beryllium | N0.01 | parts per million by weight | AES_AR_P |
Beryllium | L1 | parts per million by weight | ES_SQ |
Boron | N0.1 | parts per million by weight | AES_AR_P |
Boron | 10 | parts per million by weight | ES_SQ |
Magnesium | 1.1 | percent by weight | AES_AR_P |
Magnesium | 1.5 | percent by weight | ES_SQ |
Aluminum | 1.3 | percent by weight | AES_AR_P |
Phosphorus | 0.08 | percent by weight | AES_AR_P |
Calcium | 0.7 | percent by weight | ES_SQ |
Calcium | 0.55 | percent by weight | AES_AR_P |
Scandium | 20 | parts per million by weight | ES_SQ |
Titanium | 0.07 | percent by weight | AES_AR_P |
Titanium | 0.7 | percent by weight | ES_SQ |
Vanadium | 39 | parts per million by weight | AES_AR_P |
Vanadium | 100 | parts per million by weight | ES_SQ |
Chromium | 44 | parts per million by weight | AES_AR_P |
Chromium | 70 | parts per million by weight | ES_SQ |
Manganese | 0.07 | percent by weight | ES_SQ |
Manganese | 0.02 | percent by weight | AES_AR_P |
Iron | 2.4 | percent by weight | AES_AR_P |
Iron | 3 | percent by weight | ES_SQ |
Cobalt | 11 | parts per million by weight | AES_AR_P |
Cobalt | 15 | parts per million by weight | ES_SQ |
Nickel | 28 | parts per million by weight | AES_AR_P |
Nickel | 20 | parts per million by weight | ES_SQ |
Copper | 31 | parts per million by weight | AES_AR_P |
Copper | 10 | parts per million by weight | ES_SQ |
Zinc | 57 | parts per million by weight | AES_AR_P |
Zinc | N200 | parts per million by weight | ES_SQ |
Arsenic | N5 | parts per million by weight | AES_AR_P |
Arsenic | N200 | parts per million by weight | ES_SQ |
Strontium | 20 | parts per million by weight | AES_AR_P |
Strontium | 300 | parts per million by weight | ES_SQ |
Yttrium | 30 | parts per million by weight | ES_SQ |
Yttrium | N0.04 | parts per million by weight | AES_AR_P |
Zirconium | N1 | parts per million by weight | AES_AR_P |
Zirconium | 100 | parts per million by weight | ES_SQ |
Niobium | N1 | parts per million by weight | AES_AR_P |
Niobium | L20 | parts per million by weight | ES_SQ |
Molybdenum | N0.4 | parts per million by weight | AES_AR_P |
Molybdenum | N5 | parts per million by weight | ES_SQ |
Silver | N0.3 | parts per million by weight | AES_AR_P |
Silver | N0.5 | parts per million by weight | ES_SQ |
Cadmium | N0.4 | parts per million by weight | AES_AR_P |
Cadmium | N20 | parts per million by weight | ES_SQ |
Tin | N4 | parts per million by weight | AES_AR_P |
Tin | N10 | parts per million by weight | ES_SQ |
Antimony | N5 | parts per million by weight | AES_AR_P |
Antimony | N100 | parts per million by weight | ES_SQ |
Barium | 190 | parts per million by weight | AES_AR_P |
Barium | 500 | parts per million by weight | ES_SQ |
Lanthanum | 4.2 | parts per million by weight | AES_AR_P |
Lanthanum | 20 | parts per million by weight | ES_SQ |
Cerium | 5.6 | parts per million by weight | AES_AR_P |
Tungsten | N50 | parts per million by weight | ES_SQ |
Tungsten | N5 | parts per million by weight | AES_AR_P |
Gold | N10 | parts per million by weight | ES_SQ |
Lead | N2.4 | parts per million by weight | AES_AR_P |
Lead | L10 | parts per million by weight | ES_SQ |
Bismuth | N8 | parts per million by weight | AES_AR_P |
Bismuth | N10 | parts per million by weight | ES_SQ |
Thorium | N100 | parts per million by weight | ES_SQ |