Beryllium | N0.01 | parts per million by weight | AES_AR_P |
Beryllium | L1 | parts per million by weight | ES_SQ |
Boron | N0.1 | parts per million by weight | AES_AR_P |
Boron | 15 | parts per million by weight | ES_SQ |
Magnesium | 0.89 | percent by weight | AES_AR_P |
Magnesium | 1 | percent by weight | ES_SQ |
Aluminum | 0.97 | percent by weight | AES_AR_P |
Phosphorus | 0.04 | percent by weight | AES_AR_P |
Calcium | 0.45 | percent by weight | AES_AR_P |
Calcium | 0.7 | percent by weight | ES_SQ |
Scandium | 10 | parts per million by weight | ES_SQ |
Titanium | 0.04 | percent by weight | AES_AR_P |
Titanium | 0.3 | percent by weight | ES_SQ |
Vanadium | 37 | parts per million by weight | AES_AR_P |
Vanadium | 100 | parts per million by weight | ES_SQ |
Chromium | 37 | parts per million by weight | AES_AR_P |
Chromium | 200 | parts per million by weight | ES_SQ |
Manganese | 0.06 | percent by weight | AES_AR_P |
Manganese | 0.1 | percent by weight | ES_SQ |
Iron | 2.1 | percent by weight | AES_AR_P |
Iron | 2 | percent by weight | ES_SQ |
Cobalt | 8.9 | parts per million by weight | AES_AR_P |
Cobalt | 15 | parts per million by weight | ES_SQ |
Nickel | 29 | parts per million by weight | AES_AR_P |
Nickel | 20 | parts per million by weight | ES_SQ |
Copper | 13 | parts per million by weight | AES_AR_P |
Copper | 5 | parts per million by weight | ES_SQ |
Zinc | 31 | parts per million by weight | AES_AR_P |
Zinc | N200 | parts per million by weight | ES_SQ |
Arsenic | N5 | parts per million by weight | AES_AR_P |
Arsenic | N200 | parts per million by weight | ES_SQ |
Strontium | 26 | parts per million by weight | AES_AR_P |
Strontium | 500 | parts per million by weight | ES_SQ |
Yttrium | N0.04 | parts per million by weight | AES_AR_P |
Yttrium | 20 | parts per million by weight | ES_SQ |
Zirconium | N1 | parts per million by weight | AES_AR_P |
Zirconium | 200 | parts per million by weight | ES_SQ |
Niobium | N1 | parts per million by weight | AES_AR_P |
Niobium | N20 | parts per million by weight | ES_SQ |
Molybdenum | N0.4 | parts per million by weight | AES_AR_P |
Molybdenum | N5 | parts per million by weight | ES_SQ |
Silver | N0.3 | parts per million by weight | AES_AR_P |
Silver | N0.5 | parts per million by weight | ES_SQ |
Cadmium | N0.4 | parts per million by weight | AES_AR_P |
Cadmium | N20 | parts per million by weight | ES_SQ |
Tin | N4 | parts per million by weight | AES_AR_P |
Tin | N10 | parts per million by weight | ES_SQ |
Antimony | N5 | parts per million by weight | AES_AR_P |
Antimony | N100 | parts per million by weight | ES_SQ |
Barium | 63 | parts per million by weight | AES_AR_P |
Barium | 700 | parts per million by weight | ES_SQ |
Lanthanum | 4 | parts per million by weight | AES_AR_P |
Lanthanum | 20 | parts per million by weight | ES_SQ |
Cerium | 6.1 | parts per million by weight | AES_AR_P |
Tungsten | N5 | parts per million by weight | AES_AR_P |
Tungsten | N50 | parts per million by weight | ES_SQ |
Gold | N10 | parts per million by weight | ES_SQ |
Lead | N2.4 | parts per million by weight | AES_AR_P |
Lead | 10 | parts per million by weight | ES_SQ |
Bismuth | N8 | parts per million by weight | AES_AR_P |
Bismuth | N10 | parts per million by weight | ES_SQ |
Thorium | N100 | parts per million by weight | ES_SQ |