Beryllium | N0.01 | parts per million by weight | AES_AR_P |
Beryllium | N1 | parts per million by weight | ES_SQ |
Boron | N0.1 | parts per million by weight | AES_AR_P |
Boron | L10 | parts per million by weight | ES_SQ |
Magnesium | 0.63 | percent by weight | AES_AR_P |
Magnesium | 2 | percent by weight | ES_SQ |
Aluminum | 0.89 | percent by weight | AES_AR_P |
Phosphorus | 0.11 | percent by weight | AES_AR_P |
Calcium | 0.43 | percent by weight | AES_AR_P |
Calcium | 0.5 | percent by weight | ES_SQ |
Scandium | 30 | parts per million by weight | ES_SQ |
Titanium | 0.07 | percent by weight | AES_AR_P |
Titanium | 1 | percent by weight | ES_SQ |
Vanadium | 40 | parts per million by weight | AES_AR_P |
Vanadium | 300 | parts per million by weight | ES_SQ |
Chromium | 15 | parts per million by weight | AES_AR_P |
Chromium | 20 | parts per million by weight | ES_SQ |
Manganese | 0.02 | percent by weight | AES_AR_P |
Manganese | 0.1 | percent by weight | ES_SQ |
Iron | 1.7 | percent by weight | AES_AR_P |
Iron | 7 | percent by weight | ES_SQ |
Cobalt | 5.3 | parts per million by weight | AES_AR_P |
Cobalt | 20 | parts per million by weight | ES_SQ |
Nickel | 3.3 | parts per million by weight | AES_AR_P |
Nickel | 5 | parts per million by weight | ES_SQ |
Copper | 4 | parts per million by weight | AES_AR_P |
Copper | L5 | parts per million by weight | ES_SQ |
Zinc | N200 | parts per million by weight | ES_SQ |
Zinc | 37 | parts per million by weight | AES_AR_P |
Zinc | 45 | parts per million by weight | AA_F_AZ_H2O2_P |
Arsenic | N5 | parts per million by weight | AES_AR_P |
Arsenic | N10 | parts per million by weight | AA_F_AZ_H2O2_P |
Arsenic | N200 | parts per million by weight | ES_SQ |
Strontium | 24 | parts per million by weight | AES_AR_P |
Strontium | 300 | parts per million by weight | ES_SQ |
Yttrium | 0.69 | parts per million by weight | AES_AR_P |
Yttrium | 50 | parts per million by weight | ES_SQ |
Zirconium | G1000.11 | parts per million by weight | ES_SQ |
Zirconium | N1 | parts per million by weight | AES_AR_P |
Niobium | N1 | parts per million by weight | AES_AR_P |
Niobium | N20 | parts per million by weight | ES_SQ |
Molybdenum | N5 | parts per million by weight | ES_SQ |
Molybdenum | N0.4 | parts per million by weight | AES_AR_P |
Silver | N0.3 | parts per million by weight | AES_AR_P |
Silver | N0.5 | parts per million by weight | ES_SQ |
Cadmium | 0.1 | parts per million by weight | AA_F_AZ_H2O2_P |
Cadmium | N0.4 | parts per million by weight | AES_AR_P |
Cadmium | N20 | parts per million by weight | ES_SQ |
Tin | N4 | parts per million by weight | AES_AR_P |
Tin | N10 | parts per million by weight | ES_SQ |
Antimony | L5 | parts per million by weight | AES_AR_P |
Antimony | N2 | parts per million by weight | AA_F_AZ_H2O2_P |
Antimony | N100 | parts per million by weight | ES_SQ |
Barium | 190 | parts per million by weight | AES_AR_P |
Barium | 1000 | parts per million by weight | ES_SQ |
Lanthanum | 50 | parts per million by weight | ES_SQ |
Lanthanum | 6.4 | parts per million by weight | AES_AR_P |
Cerium | 9.8 | parts per million by weight | AES_AR_P |
Tungsten | N5 | parts per million by weight | AES_AR_P |
Tungsten | N50 | parts per million by weight | ES_SQ |
Gold | 0.3 | parts per million by weight | AA_F_HBr |
Gold | N10 | parts per million by weight | ES_SQ |
Lead | 7.8 | parts per million by weight | AES_AR_P |
Lead | 10 | parts per million by weight | ES_SQ |
Bismuth | N8 | parts per million by weight | AES_AR_P |
Bismuth | N10 | parts per million by weight | ES_SQ |
Bismuth | N1 | parts per million by weight | AA_F_AZ_H2O2_P |
Thorium | N100 | parts per million by weight | ES_SQ |