Beryllium | L1 | parts per million by weight | ES_SQ |
Beryllium | N0.01 | parts per million by weight | AES_AR_P |
Boron | N0.1 | parts per million by weight | AES_AR_P |
Boron | 10 | parts per million by weight | ES_SQ |
Magnesium | 1 | percent by weight | AES_AR_P |
Magnesium | 2 | percent by weight | ES_SQ |
Aluminum | 1.1 | percent by weight | AES_AR_P |
Phosphorus | 0.07 | percent by weight | AES_AR_P |
Calcium | 0.32 | percent by weight | AES_AR_P |
Calcium | 0.5 | percent by weight | ES_SQ |
Scandium | 20 | parts per million by weight | ES_SQ |
Titanium | 0.06 | percent by weight | AES_AR_P |
Titanium | 0.7 | percent by weight | ES_SQ |
Vanadium | 58 | parts per million by weight | AES_AR_P |
Vanadium | 300 | parts per million by weight | ES_SQ |
Chromium | 50 | parts per million by weight | ES_SQ |
Chromium | 32 | parts per million by weight | AES_AR_P |
Manganese | 0.08 | percent by weight | AES_AR_P |
Manganese | 0.2 | percent by weight | ES_SQ |
Iron | 2.5 | percent by weight | AES_AR_P |
Iron | 5 | percent by weight | ES_SQ |
Cobalt | 30 | parts per million by weight | ES_SQ |
Cobalt | 14 | parts per million by weight | AES_AR_P |
Nickel | 20 | parts per million by weight | AES_AR_P |
Nickel | 20 | parts per million by weight | ES_SQ |
Copper | 200 | parts per million by weight | ES_SQ |
Copper | 85 | parts per million by weight | AES_AR_P |
Zinc | 70 | parts per million by weight | AES_AR_P |
Zinc | 100 | parts per million by weight | AA_F_AZ_H2O2_P |
Zinc | N200 | parts per million by weight | ES_SQ |
Arsenic | L26 | parts per million by weight | AES_AR_P |
Arsenic | 40 | parts per million by weight | AA_F_AZ_H2O2_P |
Arsenic | N200 | parts per million by weight | ES_SQ |
Strontium | 500 | parts per million by weight | ES_SQ |
Strontium | 17 | parts per million by weight | AES_AR_P |
Yttrium | N0.04 | parts per million by weight | AES_AR_P |
Yttrium | 50 | parts per million by weight | ES_SQ |
Zirconium | N1 | parts per million by weight | AES_AR_P |
Zirconium | 150 | parts per million by weight | ES_SQ |
Niobium | N1 | parts per million by weight | AES_AR_P |
Niobium | N20 | parts per million by weight | ES_SQ |
Molybdenum | 1.2 | parts per million by weight | AES_AR_P |
Molybdenum | N5 | parts per million by weight | ES_SQ |
Silver | N0.3 | parts per million by weight | AES_AR_P |
Silver | L0.5 | parts per million by weight | ES_SQ |
Cadmium | N0.4 | parts per million by weight | AES_AR_P |
Cadmium | 0.5 | parts per million by weight | AA_F_AZ_H2O2_P |
Cadmium | N20 | parts per million by weight | ES_SQ |
Tin | N10 | parts per million by weight | ES_SQ |
Tin | N4 | parts per million by weight | AES_AR_P |
Antimony | N100 | parts per million by weight | ES_SQ |
Antimony | N5 | parts per million by weight | AES_AR_P |
Antimony | N2 | parts per million by weight | AA_F_AZ_H2O2_P |
Barium | 97 | parts per million by weight | AES_AR_P |
Barium | 1000 | parts per million by weight | ES_SQ |
Lanthanum | 3.1 | parts per million by weight | AES_AR_P |
Lanthanum | 30 | parts per million by weight | ES_SQ |
Cerium | 3.4 | parts per million by weight | AES_AR_P |
Tungsten | N5 | parts per million by weight | AES_AR_P |
Tungsten | N50 | parts per million by weight | ES_SQ |
Gold | N0.05 | parts per million by weight | AA_F_HBr |
Gold | N10 | parts per million by weight | ES_SQ |
Lead | 9.9 | parts per million by weight | AES_AR_P |
Lead | 15 | parts per million by weight | ES_SQ |
Bismuth | N1 | parts per million by weight | AA_F_AZ_H2O2_P |
Bismuth | N8 | parts per million by weight | AES_AR_P |
Bismuth | N10 | parts per million by weight | ES_SQ |
Thorium | N100 | parts per million by weight | ES_SQ |