Lithium | N0.2 | parts per million by weight | AES_AR_P |
Beryllium | N0.01 | parts per million by weight | AES_AR_P |
Beryllium | L1 | parts per million by weight | ES_SQ |
Boron | N0.1 | parts per million by weight | AES_AR_P |
Boron | L10 | parts per million by weight | ES_SQ |
Magnesium | 0.58 | percent by weight | AES_AR_P |
Magnesium | 2 | percent by weight | ES_SQ |
Aluminum | 1.9 | percent by weight | AES_AR_P |
Phosphorus | 0.02 | percent by weight | AES_AR_P |
Calcium | 0.53 | percent by weight | AES_AR_P |
Calcium | 1 | percent by weight | ES_SQ |
Scandium | 20 | parts per million by weight | ES_SQ |
Titanium | 0.14 | percent by weight | AES_AR_P |
Titanium | 0.7 | percent by weight | ES_SQ |
Vanadium | 300 | parts per million by weight | ES_SQ |
Vanadium | 130 | parts per million by weight | AES_AR_P |
Chromium | 28 | parts per million by weight | AES_AR_P |
Chromium | 100 | parts per million by weight | ES_SQ |
Manganese | 0.07 | percent by weight | AES_AR_P |
Manganese | 0.1 | percent by weight | ES_SQ |
Iron | 3.9 | percent by weight | AES_AR_P |
Iron | 7 | percent by weight | ES_SQ |
Cobalt | 20 | parts per million by weight | ES_SQ |
Cobalt | 10 | parts per million by weight | AES_AR_P |
Nickel | 10 | parts per million by weight | AES_AR_P |
Nickel | 15 | parts per million by weight | ES_SQ |
Copper | 220 | parts per million by weight | AES_AR_P |
Copper | 50 | parts per million by weight | ES_SQ |
Zinc | 210 | parts per million by weight | AES_AR_P |
Zinc | L200 | parts per million by weight | ES_SQ |
Arsenic | N5 | parts per million by weight | AES_AR_P |
Arsenic | N200 | parts per million by weight | ES_SQ |
Strontium | 48 | parts per million by weight | AES_AR_P |
Strontium | 300 | parts per million by weight | ES_SQ |
Yttrium | N0.04 | parts per million by weight | AES_AR_P |
Yttrium | 20 | parts per million by weight | ES_SQ |
Zirconium | 100 | parts per million by weight | ES_SQ |
Zirconium | N0.9 | parts per million by weight | AES_AR_P |
Niobium | N1 | parts per million by weight | AES_AR_P |
Niobium | N20 | parts per million by weight | ES_SQ |
Molybdenum | L5 | parts per million by weight | ES_SQ |
Molybdenum | N0.4 | parts per million by weight | AES_AR_P |
Silver | N0.3 | parts per million by weight | AES_AR_P |
Silver | N0.5 | parts per million by weight | ES_SQ |
Cadmium | N20 | parts per million by weight | ES_SQ |
Cadmium | N0.4 | parts per million by weight | AES_AR_P |
Tin | N4 | parts per million by weight | AES_AR_P |
Tin | N10 | parts per million by weight | ES_SQ |
Antimony | N100 | parts per million by weight | ES_SQ |
Antimony | N2.5 | parts per million by weight | AES_AR_P |
Barium | 49 | parts per million by weight | AES_AR_P |
Barium | 700 | parts per million by weight | ES_SQ |
Lanthanum | N20 | parts per million by weight | ES_SQ |
Lanthanum | 3.6 | parts per million by weight | AES_AR_P |
Cerium | 3.3 | parts per million by weight | AES_AR_P |
Tungsten | N50 | parts per million by weight | ES_SQ |
Tungsten | N3 | parts per million by weight | AES_AR_P |
Gold | N10 | parts per million by weight | ES_SQ |
Lead | 76 | parts per million by weight | AES_AR_P |
Lead | 30 | parts per million by weight | ES_SQ |
Bismuth | N10 | parts per million by weight | ES_SQ |
Bismuth | N8 | parts per million by weight | AES_AR_P |
Thorium | N100 | parts per million by weight | ES_SQ |