Lithium | 13 | parts per million by weight | AES_AR_P |
Beryllium | 2 | parts per million by weight | ES_SQ |
Beryllium | 0.69 | parts per million by weight | AES_AR_P |
Boron | N2 | parts per million by weight | AES_AR_P |
Boron | 50 | parts per million by weight | ES_SQ |
Sodium | 0.02 | percent by weight | AES_AR_P |
Sodium | 1 | percent by weight | ES_SQ |
Magnesium | 0.42 | percent by weight | AES_AR_P |
Magnesium | 0.7 | percent by weight | ES_SQ |
Aluminum | 1 | percent by weight | AES_AR_P |
Phosphorus | L0.2 | percent by weight | ES_SQ |
Phosphorus | N0.0005 | percent by weight | AES_AR_P |
Potassium | 0.06 | percent by weight | AES_AR_P |
Calcium | 0.28 | percent by weight | AES_AR_P |
Calcium | 0.15 | percent by weight | ES_SQ |
Scandium | 15 | parts per million by weight | ES_SQ |
Titanium | N2e05 | percent by weight | AES_AR_P |
Titanium | 0.3 | percent by weight | ES_SQ |
Vanadium | 100 | parts per million by weight | ES_SQ |
Vanadium | N2 | parts per million by weight | AES_AR_P |
Chromium | 21 | parts per million by weight | AES_AR_P |
Chromium | 100 | parts per million by weight | ES_SQ |
Manganese | 0.08 | percent by weight | AES_AR_P |
Manganese | 0.1 | percent by weight | ES_SQ |
Iron | 2.5 | percent by weight | AES_AR_P |
Iron | 3 | percent by weight | ES_SQ |
Cobalt | 11 | parts per million by weight | AES_AR_P |
Cobalt | 15 | parts per million by weight | ES_SQ |
Nickel | N3 | parts per million by weight | AES_AR_P |
Nickel | 50 | parts per million by weight | ES_SQ |
Copper | 32 | parts per million by weight | AES_AR_P |
Copper | 50 | parts per million by weight | ES_SQ |
Zinc | L200 | parts per million by weight | ES_SQ |
Zinc | 78 | parts per million by weight | AES_AR_P |
Gallium | 30 | parts per million by weight | ES_SQ |
Germanium | N10 | parts per million by weight | ES_SQ |
Arsenic | N200 | parts per million by weight | ES_SQ |
Arsenic | 9.6 | parts per million by weight | AES_AR_P |
Strontium | N1 | parts per million by weight | AES_AR_P |
Strontium | 100 | parts per million by weight | ES_SQ |
Yttrium | 5.6 | parts per million by weight | AES_AR_P |
Yttrium | 30 | parts per million by weight | ES_SQ |
Zirconium | 1.6 | parts per million by weight | AES_AR_P |
Zirconium | 150 | parts per million by weight | ES_SQ |
Niobium | N1 | parts per million by weight | AES_AR_P |
Niobium | L20 | parts per million by weight | ES_SQ |
Molybdenum | N2 | parts per million by weight | AES_AR_P |
Molybdenum | N5 | parts per million by weight | ES_SQ |
Silver | N0.2 | parts per million by weight | AES_AR_P |
Silver | L0.5 | parts per million by weight | ES_SQ |
Cadmium | N20 | parts per million by weight | ES_SQ |
Cadmium | N1 | parts per million by weight | AES_AR_P |
Tin | N10 | parts per million by weight | AES_AR_P |
Tin | N10 | parts per million by weight | ES_SQ |
Antimony | N5 | parts per million by weight | AES_AR_P |
Antimony | N100 | parts per million by weight | ES_SQ |
Barium | 410 | parts per million by weight | AES_AR_P |
Barium | 1000 | parts per million by weight | ES_SQ |
Lanthanum | 2.5 | parts per million by weight | AES_AR_P |
Lanthanum | 50 | parts per million by weight | ES_SQ |
Cerium | N4 | parts per million by weight | AES_AR_P |
Tungsten | N10 | parts per million by weight | AES_AR_P |
Tungsten | N20 | parts per million by weight | ES_SQ |
Gold | N10 | parts per million by weight | ES_SQ |
Lead | N2 | parts per million by weight | AES_AR_P |
Lead | 50 | parts per million by weight | ES_SQ |
Bismuth | N5 | parts per million by weight | AES_AR_P |
Bismuth | N10 | parts per million by weight | ES_SQ |
Thorium | N100 | parts per million by weight | ES_SQ |