Field | Value |
---|---|
Lab ID | D285047 |
Field ID | LH0436S |
Job ID | SK21 |
Sample submitter | Allen, Michael S. |
Date submitted | 9/9/1987 |
Project name | Lime Hills AMRAP |
State | AK |
Country | United States |
Latitude (WGS84) | 61.37909996 |
Longitude (WGS84) | -153.62758165 |
Original datum | (NAD27) |
Original latitude | 61.37972222 |
Original longitude | -153.62527778 |
Location precision | 1 second |
Sample source | stream/river |
Collection method | single/grab |
Primary media type | sediment |
Notes on sample | stream |
Sieve size | -80 mesh |
(click for info) | |
Geologic map unit | -153.62758165, 61.37909996 |
Nearby scientific data | Find additional scientific data near this location |
Element | Measured value | Units of measure | Analytical method |
---|---|---|---|
Beryllium | 2 | parts per million by weight | ES_SQ |
Boron | 15 | parts per million by weight | ES_SQ |
Sodium | 3 | percent by weight | ES_SQ |
Magnesium | 2 | percent by weight | ES_SQ |
Phosphorus | <0.2 | percent by weight | ES_SQ |
Calcium | 3 | percent by weight | ES_SQ |
Scandium | 30 | parts per million by weight | ES_SQ |
Titanium | 0.7 | percent by weight | ES_SQ |
Vanadium | 300 | parts per million by weight | ES_SQ |
Chromium | 300 | parts per million by weight | ES_SQ |
Manganese | 0.15 | percent by weight | ES_SQ |
Iron | 7 | percent by weight | ES_SQ |
Cobalt | 30 | parts per million by weight | ES_SQ |
Nickel | 30 | parts per million by weight | ES_SQ |
Copper | 50 | parts per million by weight | ES_SQ |
Zinc | <200 | parts per million by weight | ES_SQ |
Gallium | 30 | parts per million by weight | ES_SQ |
Germanium | <10 | parts per million by weight | ES_SQ |
Arsenic | <200 | parts per million by weight | ES_SQ |
Strontium | 1500 | parts per million by weight | ES_SQ |
Yttrium | 50 | parts per million by weight | ES_SQ |
Zirconium | 150 | parts per million by weight | ES_SQ |
Niobium | <20 | parts per million by weight | ES_SQ |
Molybdenum | <5 | parts per million by weight | ES_SQ |
Silver | <0.5 | parts per million by weight | ES_SQ |
Cadmium | <20 | parts per million by weight | ES_SQ |
Tin | <10 | parts per million by weight | ES_SQ |
Antimony | <100 | parts per million by weight | ES_SQ |
Barium | 1500 | parts per million by weight | ES_SQ |
Lanthanum | 70 | parts per million by weight | ES_SQ |
Tungsten | <20 | parts per million by weight | ES_SQ |
Gold | <0.002 | parts per million by weight | AA_GF_HBr |
Mercury | 0.12 | parts per million by weight | AA_CV |
Lead | 50 | parts per million by weight | ES_SQ |
Bismuth | <10 | parts per million by weight | ES_SQ |
Thorium | <100 | parts per million by weight | ES_SQ |
Uranium | 3.9 | parts per million by weight | FL_HF |
Element | Value | Units | Technique |
---|---|---|---|
Beryllium | 2 | parts per million by weight | ES_SQ |
Boron | 15 | parts per million by weight | ES_SQ |
Sodium | 3 | percent by weight | ES_SQ |
Magnesium | 2 | percent by weight | ES_SQ |
Phosphorus | N0.2 | percent by weight | ES_SQ |
Calcium | 3 | percent by weight | ES_SQ |
Scandium | 30 | parts per million by weight | ES_SQ |
Titanium | 0.7 | percent by weight | ES_SQ |
Vanadium | 300 | parts per million by weight | ES_SQ |
Chromium | 300 | parts per million by weight | ES_SQ |
Manganese | 0.15 | percent by weight | ES_SQ |
Iron | 7 | percent by weight | ES_SQ |
Cobalt | 30 | parts per million by weight | ES_SQ |
Nickel | 30 | parts per million by weight | ES_SQ |
Copper | 50 | parts per million by weight | ES_SQ |
Copper | 30 | parts per million by weight | AES_AZ_P |
Zinc | 82 | parts per million by weight | AES_AZ_P |
Zinc | 77 | parts per million by weight | AES_AZ_P |
Zinc | N200 | parts per million by weight | ES_SQ |
Gallium | 30 | parts per million by weight | ES_SQ |
Germanium | N10 | parts per million by weight | ES_SQ |
Arsenic | 41 | parts per million by weight | AES_AZ_P |
Arsenic | N200 | parts per million by weight | ES_SQ |
Strontium | 1500 | parts per million by weight | ES_SQ |
Yttrium | 50 | parts per million by weight | ES_SQ |
Zirconium | 150 | parts per million by weight | ES_SQ |
Niobium | L20 | parts per million by weight | ES_SQ |
Molybdenum | 0.66 | parts per million by weight | AES_AZ_P |
Molybdenum | N5 | parts per million by weight | ES_SQ |
Silver | 0.22 | parts per million by weight | AES_AZ_P |
Silver | N0.5 | parts per million by weight | ES_SQ |
Cadmium | 0.38 | parts per million by weight | AES_AZ_P |
Cadmium | N20 | parts per million by weight | ES_SQ |
Tin | N10 | parts per million by weight | ES_SQ |
Antimony | 0.71 | parts per million by weight | AES_AZ_P |
Antimony | N100 | parts per million by weight | ES_SQ |
Barium | 1500 | parts per million by weight | ES_SQ |
Lanthanum | 70 | parts per million by weight | ES_SQ |
Tungsten | N20 | parts per million by weight | ES_SQ |
Gold | L0.002 | parts per million by weight | AA_GF_HBr |
Gold | N0.15 | parts per million by weight | AES_AZ_P |
Gold | N10 | parts per million by weight | ES_SQ |
Gold | N0.05 | parts per million by weight | AA_F_HBr |
Mercury | 0.12 | parts per million by weight | AA_CV |
Lead | 21 | parts per million by weight | AES_AZ_P |
Lead | 50 | parts per million by weight | ES_SQ |
Bismuth | N0.6 | parts per million by weight | AES_AZ_P |
Bismuth | N10 | parts per million by weight | ES_SQ |
Thorium | N100 | parts per million by weight | ES_SQ |
Uranium | 3.9 | parts per million by weight | FL_HF |