Field | Value |
---|---|
Lab ID | D360650 |
Field ID | LK060SSC |
Job ID | UC54 |
Sample submitter | Kelley, Karen D. |
Date submitted | 8/27/1990 |
Project name | Lik Soil Study |
State | AK |
Country | United States |
Latitude (WGS84) | 68.17271553 |
Longitude (WGS84) | -163.20342604 |
Original datum | (NAD27) |
Original latitude | 68.17333333 |
Original longitude | -163.20027778 |
Location precision | 1 second |
Sample source | stream/river |
Collection method | composite |
Primary media type | sediment |
Notes on sample | stream |
Sieve size | -80 +230 mesh |
(click for info) | |
Geologic map unit | -163.20342604, 68.17271553 |
Nearby scientific data | Find additional scientific data near this location |
Element | Measured value | Units of measure | Analytical method |
---|---|---|---|
Lithium | 31 | parts per million by weight | AES_HF |
Beryllium | <1 | parts per million by weight | AES_HF |
Sodium | 0.26 | percent by weight | AES_HF |
Magnesium | 2.47 | percent by weight | AES_HF |
Aluminum | 3.42 | percent by weight | AES_HF |
Phosphorus | 0.03 | percent by weight | AES_HF |
Potassium | 0.98 | percent by weight | AES_HF |
Calcium | 13.1 | percent by weight | AES_HF |
Scandium | 7 | parts per million by weight | AES_HF |
Titanium | 0.14 | percent by weight | AES_HF |
Vanadium | 72 | parts per million by weight | AES_HF |
Chromium | 65 | parts per million by weight | AES_HF |
Manganese | 0.01 | percent by weight | AES_HF |
Iron | 1.93 | percent by weight | AES_HF |
Cobalt | 9 | parts per million by weight | AES_HF |
Nickel | 40 | parts per million by weight | AES_HF |
Copper | 14 | parts per million by weight | AES_HF |
Zinc | 102 | parts per million by weight | AES_HF |
Gallium | 8 | parts per million by weight | AES_HF |
Arsenic | <10 | parts per million by weight | AES_HF |
Strontium | 280 | parts per million by weight | AES_HF |
Yttrium | 14 | parts per million by weight | AES_HF |
Niobium | <4 | parts per million by weight | AES_HF |
Molybdenum | <2 | parts per million by weight | AES_HF |
Silver | <2 | parts per million by weight | AES_HF |
Cadmium | <2 | parts per million by weight | AES_HF |
Tin | <10 | parts per million by weight | AES_HF |
Barium | 1030 | parts per million by weight | AES_HF |
Lanthanum | 21 | parts per million by weight | AES_HF |
Cerium | 29 | parts per million by weight | AES_HF |
Neodymium | 15 | parts per million by weight | AES_HF |
Europium | <2 | parts per million by weight | AES_HF |
Holmium | <4 | parts per million by weight | AES_HF |
Ytterbium | 2 | parts per million by weight | AES_HF |
Tantalum | <40 | parts per million by weight | AES_HF |
Gold | <8 | parts per million by weight | AES_HF |
Lead | 8 | parts per million by weight | AES_HF |
Bismuth | <10 | parts per million by weight | AES_HF |
Thorium | 5 | parts per million by weight | AES_HF |
Uranium | <100 | parts per million by weight | AES_HF |
Element | Value | Units | Technique |
---|---|---|---|
Lithium | 31 | parts per million by weight | AES_HF |
Beryllium | L1 | parts per million by weight | AES_HF |
Sodium | 0.26 | percent by weight | AES_HF |
Magnesium | 2.47 | percent by weight | AES_HF |
Aluminum | 3.42 | percent by weight | AES_HF |
Phosphorus | 0.03 | percent by weight | AES_HF |
Potassium | 0.98 | percent by weight | AES_HF |
Calcium | 13.1 | percent by weight | AES_HF |
Scandium | 7 | parts per million by weight | AES_HF |
Titanium | 0.14 | percent by weight | AES_HF |
Vanadium | 72 | parts per million by weight | AES_HF |
Chromium | 65 | parts per million by weight | AES_HF |
Manganese | 0.01 | percent by weight | AES_HF |
Iron | 1.93 | percent by weight | AES_HF |
Cobalt | 9 | parts per million by weight | AES_HF |
Nickel | 40 | parts per million by weight | AES_HF |
Copper | 14 | parts per million by weight | AES_HF |
Copper | 12 | parts per million by weight | AES_AZ_P |
Zinc | 87 | parts per million by weight | AES_AZ_P |
Zinc | 102 | parts per million by weight | AES_HF |
Gallium | 8 | parts per million by weight | AES_HF |
Arsenic | 6.6 | parts per million by weight | AES_AZ_P |
Arsenic | L10 | parts per million by weight | AES_HF |
Strontium | 280 | parts per million by weight | AES_HF |
Yttrium | 14 | parts per million by weight | AES_HF |
Niobium | L4 | parts per million by weight | AES_HF |
Molybdenum | 1.1 | parts per million by weight | AES_AZ_P |
Molybdenum | L2 | parts per million by weight | AES_HF |
Silver | 0.07 | parts per million by weight | AES_AZ_P |
Silver | L2 | parts per million by weight | AES_HF |
Cadmium | 0.45 | parts per million by weight | AES_AZ_P |
Cadmium | L2 | parts per million by weight | AES_HF |
Tin | L10 | parts per million by weight | AES_HF |
Antimony | 0.71 | parts per million by weight | AES_AZ_P |
Barium | 1030 | parts per million by weight | AES_HF |
Lanthanum | 21 | parts per million by weight | AES_HF |
Cerium | 29 | parts per million by weight | AES_HF |
Neodymium | 15 | parts per million by weight | AES_HF |
Europium | L2 | parts per million by weight | AES_HF |
Holmium | L4 | parts per million by weight | AES_HF |
Ytterbium | 2 | parts per million by weight | AES_HF |
Tantalum | L40 | parts per million by weight | AES_HF |
Gold | N0.15 | parts per million by weight | AES_AZ_P |
Gold | L8 | parts per million by weight | AES_HF |
Lead | 10 | parts per million by weight | AES_AZ_P |
Lead | 8 | parts per million by weight | AES_HF |
Bismuth | N0.6 | parts per million by weight | AES_AZ_P |
Bismuth | L10 | parts per million by weight | AES_HF |
Thorium | 5 | parts per million by weight | AES_HF |
Uranium | L100 | parts per million by weight | AES_HF |