Field | Value |
---|---|
Lab ID | D360658 |
Field ID | LK088SSC |
Job ID | UC54 |
Sample submitter | Kelley, Karen D. |
Date submitted | 8/27/1990 |
Project name | Lik Soil Study |
State | AK |
Country | United States |
Latitude (WGS84) | 68.16327098 |
Longitude (WGS84) | -163.19370239 |
Original datum | (NAD27) |
Original latitude | 68.16388889 |
Original longitude | -163.19055556 |
Location precision | 1 second |
Sample source | stream/river |
Collection method | composite |
Primary media type | sediment |
Notes on sample | stream |
Sieve size | -80 +230 mesh |
(click for info) | |
Geologic map unit | -163.19370239, 68.16327098 |
Nearby scientific data | Find additional scientific data near this location |
Element | Measured value | Units of measure | Analytical method |
---|---|---|---|
Lithium | 58 | parts per million by weight | AES_HF |
Beryllium | 2 | parts per million by weight | AES_HF |
Sodium | 0.62 | percent by weight | AES_HF |
Magnesium | 1.57 | percent by weight | AES_HF |
Aluminum | 6.22 | percent by weight | AES_HF |
Phosphorus | 0.07 | percent by weight | AES_HF |
Potassium | 1.73 | percent by weight | AES_HF |
Calcium | 3.32 | percent by weight | AES_HF |
Scandium | 13 | parts per million by weight | AES_HF |
Titanium | 0.3 | percent by weight | AES_HF |
Vanadium | 163 | parts per million by weight | AES_HF |
Chromium | 121 | parts per million by weight | AES_HF |
Manganese | 0.08 | percent by weight | AES_HF |
Iron | 4.19 | percent by weight | AES_HF |
Cobalt | 19 | parts per million by weight | AES_HF |
Nickel | 73 | parts per million by weight | AES_HF |
Copper | 49 | parts per million by weight | AES_HF |
Zinc | 694 | parts per million by weight | AES_HF |
Gallium | 15 | parts per million by weight | AES_HF |
Arsenic | 10 | parts per million by weight | AES_HF |
Strontium | 154 | parts per million by weight | AES_HF |
Yttrium | 18 | parts per million by weight | AES_HF |
Niobium | 7 | parts per million by weight | AES_HF |
Molybdenum | 3 | parts per million by weight | AES_HF |
Silver | <2 | parts per million by weight | AES_HF |
Cadmium | <2 | parts per million by weight | AES_HF |
Tin | <10 | parts per million by weight | AES_HF |
Barium | 445 | parts per million by weight | AES_HF |
Lanthanum | 28 | parts per million by weight | AES_HF |
Cerium | 49 | parts per million by weight | AES_HF |
Neodymium | 26 | parts per million by weight | AES_HF |
Europium | <2 | parts per million by weight | AES_HF |
Holmium | <4 | parts per million by weight | AES_HF |
Ytterbium | 2 | parts per million by weight | AES_HF |
Tantalum | <40 | parts per million by weight | AES_HF |
Gold | <8 | parts per million by weight | AES_HF |
Lead | 68 | parts per million by weight | AES_HF |
Bismuth | <10 | parts per million by weight | AES_HF |
Thorium | 8 | parts per million by weight | AES_HF |
Uranium | <100 | parts per million by weight | AES_HF |
Element | Value | Units | Technique |
---|---|---|---|
Lithium | 58 | parts per million by weight | AES_HF |
Beryllium | 2 | parts per million by weight | AES_HF |
Sodium | 0.62 | percent by weight | AES_HF |
Magnesium | 1.57 | percent by weight | AES_HF |
Aluminum | 6.22 | percent by weight | AES_HF |
Phosphorus | 0.07 | percent by weight | AES_HF |
Potassium | 1.73 | percent by weight | AES_HF |
Calcium | 3.32 | percent by weight | AES_HF |
Scandium | 13 | parts per million by weight | AES_HF |
Titanium | 0.3 | percent by weight | AES_HF |
Vanadium | 163 | parts per million by weight | AES_HF |
Chromium | 121 | parts per million by weight | AES_HF |
Manganese | 0.08 | percent by weight | AES_HF |
Iron | 4.19 | percent by weight | AES_HF |
Cobalt | 19 | parts per million by weight | AES_HF |
Nickel | 73 | parts per million by weight | AES_HF |
Copper | 49 | parts per million by weight | AES_HF |
Copper | 43 | parts per million by weight | AES_AZ_P |
Zinc | 540 | parts per million by weight | AES_AZ_P |
Zinc | 694 | parts per million by weight | AES_HF |
Gallium | 15 | parts per million by weight | AES_HF |
Arsenic | 14 | parts per million by weight | AES_AZ_P |
Arsenic | 10 | parts per million by weight | AES_HF |
Strontium | 154 | parts per million by weight | AES_HF |
Yttrium | 18 | parts per million by weight | AES_HF |
Niobium | 7 | parts per million by weight | AES_HF |
Molybdenum | 3.6 | parts per million by weight | AES_AZ_P |
Molybdenum | 3 | parts per million by weight | AES_HF |
Silver | 0.3 | parts per million by weight | AES_AZ_P |
Silver | L2 | parts per million by weight | AES_HF |
Cadmium | 1.1 | parts per million by weight | AES_AZ_P |
Cadmium | L2 | parts per million by weight | AES_HF |
Tin | L10 | parts per million by weight | AES_HF |
Antimony | 1.7 | parts per million by weight | AES_AZ_P |
Barium | 445 | parts per million by weight | AES_HF |
Lanthanum | 28 | parts per million by weight | AES_HF |
Cerium | 49 | parts per million by weight | AES_HF |
Neodymium | 26 | parts per million by weight | AES_HF |
Europium | L2 | parts per million by weight | AES_HF |
Holmium | L4 | parts per million by weight | AES_HF |
Ytterbium | 2 | parts per million by weight | AES_HF |
Tantalum | L40 | parts per million by weight | AES_HF |
Gold | N0.15 | parts per million by weight | AES_AZ_P |
Gold | L8 | parts per million by weight | AES_HF |
Lead | 68 | parts per million by weight | AES_HF |
Lead | 110 | parts per million by weight | AES_AZ_P |
Bismuth | N0.6 | parts per million by weight | AES_AZ_P |
Bismuth | L10 | parts per million by weight | AES_HF |
Thorium | 8 | parts per million by weight | AES_HF |
Uranium | L100 | parts per million by weight | AES_HF |