Field | Value |
---|---|
Lab ID | D360663 |
Field ID | LK056SSB |
Job ID | UC55 |
Sample submitter | Kelley, Karen D. |
Date submitted | 8/27/1990 |
Project name | Lik Soil Study |
State | AK |
Country | United States |
Latitude (WGS84) | 68.17132693 |
Longitude (WGS84) | -163.18564781 |
Original datum | (NAD27) |
Original latitude | 68.17194444 |
Original longitude | -163.1825 |
Location precision | 1 second |
Sample source | stream/river |
Collection method | composite |
Primary media type | sediment |
Notes on sample | stream |
Sieve size | -30 +80 mesh |
(click for info) | |
Geologic map unit | -163.18564781, 68.17132693 |
Nearby scientific data | Find additional scientific data near this location |
Element | Measured value | Units of measure | Analytical method |
---|---|---|---|
Lithium | 44 | parts per million by weight | AES_HF |
Beryllium | 2 | parts per million by weight | AES_HF |
Sodium | 0.33 | percent by weight | AES_HF |
Magnesium | 0.62 | percent by weight | AES_HF |
Aluminum | 4.86 | percent by weight | AES_HF |
Phosphorus | 0.1 | percent by weight | AES_HF |
Potassium | 1.29 | percent by weight | AES_HF |
Calcium | 5.88 | percent by weight | AES_HF |
Scandium | 10 | parts per million by weight | AES_HF |
Titanium | 0.21 | percent by weight | AES_HF |
Vanadium | 130 | parts per million by weight | AES_HF |
Chromium | 130 | parts per million by weight | AES_HF |
Manganese | 0.06 | percent by weight | AES_HF |
Iron | 3.88 | percent by weight | AES_HF |
Cobalt | 16 | parts per million by weight | AES_HF |
Nickel | 102 | parts per million by weight | AES_HF |
Copper | 47 | parts per million by weight | AES_HF |
Zinc | 2790 | parts per million by weight | AES_HF |
Gallium | 11 | parts per million by weight | AES_HF |
Arsenic | 20 | parts per million by weight | AES_HF |
Strontium | 372 | parts per million by weight | AES_HF |
Yttrium | 24 | parts per million by weight | AES_HF |
Niobium | <4 | parts per million by weight | AES_HF |
Molybdenum | 4 | parts per million by weight | AES_HF |
Silver | <2 | parts per million by weight | AES_HF |
Cadmium | 5 | parts per million by weight | AES_HF |
Tin | <10 | parts per million by weight | AES_HF |
Barium | 330 | parts per million by weight | AES_HF |
Lanthanum | 25 | parts per million by weight | AES_HF |
Cerium | 39 | parts per million by weight | AES_HF |
Neodymium | 21 | parts per million by weight | AES_HF |
Europium | <2 | parts per million by weight | AES_HF |
Holmium | <4 | parts per million by weight | AES_HF |
Ytterbium | 2 | parts per million by weight | AES_HF |
Tantalum | <40 | parts per million by weight | AES_HF |
Gold | <8 | parts per million by weight | AES_HF |
Lead | 252 | parts per million by weight | AES_HF |
Bismuth | <10 | parts per million by weight | AES_HF |
Thorium | 6 | parts per million by weight | AES_HF |
Uranium | <100 | parts per million by weight | AES_HF |
Element | Value | Units | Technique |
---|---|---|---|
Lithium | 44 | parts per million by weight | AES_HF |
Beryllium | 2 | parts per million by weight | AES_HF |
Sodium | 0.33 | percent by weight | AES_HF |
Magnesium | 0.62 | percent by weight | AES_HF |
Aluminum | 4.86 | percent by weight | AES_HF |
Phosphorus | 0.1 | percent by weight | AES_HF |
Potassium | 1.29 | percent by weight | AES_HF |
Calcium | 5.88 | percent by weight | AES_HF |
Scandium | 10 | parts per million by weight | AES_HF |
Titanium | 0.21 | percent by weight | AES_HF |
Vanadium | 130 | parts per million by weight | AES_HF |
Chromium | 130 | parts per million by weight | AES_HF |
Manganese | 0.06 | percent by weight | AES_HF |
Iron | 3.88 | percent by weight | AES_HF |
Cobalt | 16 | parts per million by weight | AES_HF |
Nickel | 102 | parts per million by weight | AES_HF |
Copper | 41 | parts per million by weight | AES_AZ_P |
Copper | 47 | parts per million by weight | AES_HF |
Zinc | G1600.11 | parts per million by weight | AES_AZ_P |
Zinc | 2790 | parts per million by weight | AES_HF |
Gallium | 11 | parts per million by weight | AES_HF |
Arsenic | 14 | parts per million by weight | AES_AZ_P |
Arsenic | 20 | parts per million by weight | AES_HF |
Strontium | 372 | parts per million by weight | AES_HF |
Yttrium | 24 | parts per million by weight | AES_HF |
Niobium | L4 | parts per million by weight | AES_HF |
Molybdenum | 5.4 | parts per million by weight | AES_AZ_P |
Molybdenum | 4 | parts per million by weight | AES_HF |
Silver | N0.04 | parts per million by weight | AES_AZ_P |
Silver | L2 | parts per million by weight | AES_HF |
Cadmium | 5.5 | parts per million by weight | AES_AZ_P |
Cadmium | 5 | parts per million by weight | AES_HF |
Tin | L10 | parts per million by weight | AES_HF |
Antimony | N0.6 | parts per million by weight | AES_AZ_P |
Barium | 330 | parts per million by weight | AES_HF |
Lanthanum | 25 | parts per million by weight | AES_HF |
Cerium | 39 | parts per million by weight | AES_HF |
Neodymium | 21 | parts per million by weight | AES_HF |
Europium | L2 | parts per million by weight | AES_HF |
Holmium | L4 | parts per million by weight | AES_HF |
Ytterbium | 2 | parts per million by weight | AES_HF |
Tantalum | L40 | parts per million by weight | AES_HF |
Gold | N0.15 | parts per million by weight | AES_AZ_P |
Gold | L8 | parts per million by weight | AES_HF |
Lead | 380 | parts per million by weight | AES_AZ_P |
Lead | 252 | parts per million by weight | AES_HF |
Bismuth | L10 | parts per million by weight | AES_HF |
Bismuth | N0.6 | parts per million by weight | AES_AZ_P |
Thorium | 6 | parts per million by weight | AES_HF |
Uranium | L100 | parts per million by weight | AES_HF |