Field | Value |
---|---|
Lab ID | D360666 |
Field ID | LK060SSB |
Job ID | UC55 |
Sample submitter | Kelley, Karen D. |
Date submitted | 8/27/1990 |
Project name | Lik Soil Study |
State | AK |
Country | United States |
Latitude (WGS84) | 68.17271553 |
Longitude (WGS84) | -163.20342604 |
Original datum | (NAD27) |
Original latitude | 68.17333333 |
Original longitude | -163.20027778 |
Location precision | 1 second |
Sample source | stream/river |
Collection method | composite |
Primary media type | sediment |
Notes on sample | stream |
Sieve size | -30 +80 mesh |
(click for info) | |
Geologic map unit | -163.20342604, 68.17271553 |
Nearby scientific data | Find additional scientific data near this location |
Element | Measured value | Units of measure | Analytical method |
---|---|---|---|
Lithium | 30 | parts per million by weight | AES_HF |
Beryllium | <1 | parts per million by weight | AES_HF |
Sodium | 0.28 | percent by weight | AES_HF |
Magnesium | 0.82 | percent by weight | AES_HF |
Aluminum | 3.27 | percent by weight | AES_HF |
Phosphorus | 0.03 | percent by weight | AES_HF |
Potassium | 0.92 | percent by weight | AES_HF |
Calcium | 14.6 | percent by weight | AES_HF |
Scandium | 7 | parts per million by weight | AES_HF |
Titanium | 0.15 | percent by weight | AES_HF |
Vanadium | 70 | parts per million by weight | AES_HF |
Chromium | 43 | parts per million by weight | AES_HF |
Manganese | 0.01 | percent by weight | AES_HF |
Iron | 1.9 | percent by weight | AES_HF |
Cobalt | 10 | parts per million by weight | AES_HF |
Nickel | 36 | parts per million by weight | AES_HF |
Copper | 15 | parts per million by weight | AES_HF |
Zinc | 89 | parts per million by weight | AES_HF |
Gallium | 8 | parts per million by weight | AES_HF |
Arsenic | <10 | parts per million by weight | AES_HF |
Strontium | 385 | parts per million by weight | AES_HF |
Yttrium | 14 | parts per million by weight | AES_HF |
Niobium | <4 | parts per million by weight | AES_HF |
Molybdenum | <2 | parts per million by weight | AES_HF |
Silver | <2 | parts per million by weight | AES_HF |
Cadmium | <2 | parts per million by weight | AES_HF |
Tin | <10 | parts per million by weight | AES_HF |
Barium | 1340 | parts per million by weight | AES_HF |
Lanthanum | 21 | parts per million by weight | AES_HF |
Cerium | 28 | parts per million by weight | AES_HF |
Neodymium | 15 | parts per million by weight | AES_HF |
Europium | <2 | parts per million by weight | AES_HF |
Holmium | <4 | parts per million by weight | AES_HF |
Ytterbium | 1 | parts per million by weight | AES_HF |
Tantalum | <40 | parts per million by weight | AES_HF |
Gold | <8 | parts per million by weight | AES_HF |
Lead | 7 | parts per million by weight | AES_HF |
Bismuth | <10 | parts per million by weight | AES_HF |
Thorium | 6 | parts per million by weight | AES_HF |
Uranium | <100 | parts per million by weight | AES_HF |
Element | Value | Units | Technique |
---|---|---|---|
Lithium | 30 | parts per million by weight | AES_HF |
Beryllium | L1 | parts per million by weight | AES_HF |
Sodium | 0.28 | percent by weight | AES_HF |
Magnesium | 0.82 | percent by weight | AES_HF |
Aluminum | 3.27 | percent by weight | AES_HF |
Phosphorus | 0.03 | percent by weight | AES_HF |
Potassium | 0.92 | percent by weight | AES_HF |
Calcium | 14.6 | percent by weight | AES_HF |
Scandium | 7 | parts per million by weight | AES_HF |
Titanium | 0.15 | percent by weight | AES_HF |
Vanadium | 70 | parts per million by weight | AES_HF |
Chromium | 43 | parts per million by weight | AES_HF |
Manganese | 0.01 | percent by weight | AES_HF |
Iron | 1.9 | percent by weight | AES_HF |
Cobalt | 10 | parts per million by weight | AES_HF |
Nickel | 36 | parts per million by weight | AES_HF |
Copper | 15 | parts per million by weight | AES_HF |
Copper | 13 | parts per million by weight | AES_AZ_P |
Zinc | 75 | parts per million by weight | AES_AZ_P |
Zinc | 89 | parts per million by weight | AES_HF |
Gallium | 8 | parts per million by weight | AES_HF |
Arsenic | 6.2 | parts per million by weight | AES_AZ_P |
Arsenic | L10 | parts per million by weight | AES_HF |
Strontium | 385 | parts per million by weight | AES_HF |
Yttrium | 14 | parts per million by weight | AES_HF |
Niobium | L4 | parts per million by weight | AES_HF |
Molybdenum | 1.1 | parts per million by weight | AES_AZ_P |
Molybdenum | L2 | parts per million by weight | AES_HF |
Silver | 0.07 | parts per million by weight | AES_AZ_P |
Silver | L2 | parts per million by weight | AES_HF |
Cadmium | 0.39 | parts per million by weight | AES_AZ_P |
Cadmium | L2 | parts per million by weight | AES_HF |
Tin | L10 | parts per million by weight | AES_HF |
Antimony | 0.87 | parts per million by weight | AES_AZ_P |
Barium | 1340 | parts per million by weight | AES_HF |
Lanthanum | 21 | parts per million by weight | AES_HF |
Cerium | 28 | parts per million by weight | AES_HF |
Neodymium | 15 | parts per million by weight | AES_HF |
Europium | L2 | parts per million by weight | AES_HF |
Holmium | L4 | parts per million by weight | AES_HF |
Ytterbium | 1 | parts per million by weight | AES_HF |
Tantalum | L40 | parts per million by weight | AES_HF |
Gold | L8 | parts per million by weight | AES_HF |
Gold | N0.15 | parts per million by weight | AES_AZ_P |
Lead | 8.5 | parts per million by weight | AES_AZ_P |
Lead | 7 | parts per million by weight | AES_HF |
Bismuth | 0.6 | parts per million by weight | AES_AZ_P |
Bismuth | L10 | parts per million by weight | AES_HF |
Thorium | 6 | parts per million by weight | AES_HF |
Uranium | L100 | parts per million by weight | AES_HF |