Field | Value |
---|---|
Lab ID | D360667 |
Field ID | LK061SSB |
Job ID | UC55 |
Sample submitter | Kelley, Karen D. |
Date submitted | 8/27/1990 |
Project name | Lik Soil Study |
State | AK |
Country | United States |
Latitude (WGS84) | 68.1721602 |
Longitude (WGS84) | -163.19092578 |
Original datum | (NAD27) |
Original latitude | 68.17277778 |
Original longitude | -163.18777778 |
Location precision | 1 second |
Sample source | stream/river |
Collection method | composite |
Primary media type | sediment |
Notes on sample | stream |
Sieve size | -30 +80 mesh |
(click for info) | |
Geologic map unit | -163.19092578, 68.1721602 |
Nearby scientific data | Find additional scientific data near this location |
Element | Measured value | Units of measure | Analytical method |
---|---|---|---|
Lithium | 57 | parts per million by weight | AES_HF |
Beryllium | 2 | parts per million by weight | AES_HF |
Sodium | 0.61 | percent by weight | AES_HF |
Magnesium | 0.99 | percent by weight | AES_HF |
Aluminum | 6.35 | percent by weight | AES_HF |
Phosphorus | 0.1 | percent by weight | AES_HF |
Potassium | 1.55 | percent by weight | AES_HF |
Calcium | 0.65 | percent by weight | AES_HF |
Scandium | 14 | parts per million by weight | AES_HF |
Titanium | 0.33 | percent by weight | AES_HF |
Vanadium | 166 | parts per million by weight | AES_HF |
Chromium | 157 | parts per million by weight | AES_HF |
Manganese | 0.1 | percent by weight | AES_HF |
Iron | 4.99 | percent by weight | AES_HF |
Cobalt | 23 | parts per million by weight | AES_HF |
Nickel | 87 | parts per million by weight | AES_HF |
Copper | 57 | parts per million by weight | AES_HF |
Zinc | 730 | parts per million by weight | AES_HF |
Gallium | 16 | parts per million by weight | AES_HF |
Arsenic | 10 | parts per million by weight | AES_HF |
Strontium | 187 | parts per million by weight | AES_HF |
Yttrium | 23 | parts per million by weight | AES_HF |
Niobium | 6 | parts per million by weight | AES_HF |
Molybdenum | <2 | parts per million by weight | AES_HF |
Silver | <2 | parts per million by weight | AES_HF |
Cadmium | 3 | parts per million by weight | AES_HF |
Tin | <10 | parts per million by weight | AES_HF |
Barium | 1890 | parts per million by weight | AES_HF |
Lanthanum | 26 | parts per million by weight | AES_HF |
Cerium | 45 | parts per million by weight | AES_HF |
Neodymium | 26 | parts per million by weight | AES_HF |
Europium | <2 | parts per million by weight | AES_HF |
Holmium | <4 | parts per million by weight | AES_HF |
Ytterbium | 2 | parts per million by weight | AES_HF |
Tantalum | <40 | parts per million by weight | AES_HF |
Gold | <8 | parts per million by weight | AES_HF |
Lead | 244 | parts per million by weight | AES_HF |
Bismuth | <10 | parts per million by weight | AES_HF |
Thorium | 9 | parts per million by weight | AES_HF |
Uranium | <100 | parts per million by weight | AES_HF |
Element | Value | Units | Technique |
---|---|---|---|
Lithium | 57 | parts per million by weight | AES_HF |
Beryllium | 2 | parts per million by weight | AES_HF |
Sodium | 0.61 | percent by weight | AES_HF |
Magnesium | 0.99 | percent by weight | AES_HF |
Aluminum | 6.35 | percent by weight | AES_HF |
Phosphorus | 0.1 | percent by weight | AES_HF |
Potassium | 1.55 | percent by weight | AES_HF |
Calcium | 0.65 | percent by weight | AES_HF |
Scandium | 14 | parts per million by weight | AES_HF |
Titanium | 0.33 | percent by weight | AES_HF |
Vanadium | 166 | parts per million by weight | AES_HF |
Chromium | 157 | parts per million by weight | AES_HF |
Manganese | 0.1 | percent by weight | AES_HF |
Iron | 4.99 | percent by weight | AES_HF |
Cobalt | 23 | parts per million by weight | AES_HF |
Nickel | 87 | parts per million by weight | AES_HF |
Copper | 44 | parts per million by weight | AES_AZ_P |
Copper | 57 | parts per million by weight | AES_HF |
Zinc | 530 | parts per million by weight | AES_AZ_P |
Zinc | 730 | parts per million by weight | AES_HF |
Gallium | 16 | parts per million by weight | AES_HF |
Arsenic | 11 | parts per million by weight | AES_AZ_P |
Arsenic | 10 | parts per million by weight | AES_HF |
Strontium | 187 | parts per million by weight | AES_HF |
Yttrium | 23 | parts per million by weight | AES_HF |
Niobium | 6 | parts per million by weight | AES_HF |
Molybdenum | L2 | parts per million by weight | AES_HF |
Molybdenum | 3.5 | parts per million by weight | AES_AZ_P |
Silver | 0.33 | parts per million by weight | AES_AZ_P |
Silver | L2 | parts per million by weight | AES_HF |
Cadmium | 3.1 | parts per million by weight | AES_AZ_P |
Cadmium | 3 | parts per million by weight | AES_HF |
Tin | L10 | parts per million by weight | AES_HF |
Antimony | 1.8 | parts per million by weight | AES_AZ_P |
Barium | 1890 | parts per million by weight | AES_HF |
Lanthanum | 26 | parts per million by weight | AES_HF |
Cerium | 45 | parts per million by weight | AES_HF |
Neodymium | 26 | parts per million by weight | AES_HF |
Europium | L2 | parts per million by weight | AES_HF |
Holmium | L4 | parts per million by weight | AES_HF |
Ytterbium | 2 | parts per million by weight | AES_HF |
Tantalum | L40 | parts per million by weight | AES_HF |
Gold | N0.15 | parts per million by weight | AES_AZ_P |
Gold | L8 | parts per million by weight | AES_HF |
Lead | 260 | parts per million by weight | AES_AZ_P |
Lead | 244 | parts per million by weight | AES_HF |
Bismuth | 0.72 | parts per million by weight | AES_AZ_P |
Bismuth | L10 | parts per million by weight | AES_HF |
Thorium | 9 | parts per million by weight | AES_HF |
Uranium | L100 | parts per million by weight | AES_HF |