Field | Value |
---|---|
Lab ID | D360705 |
Field ID | LK087SSE |
Job ID | UC57 |
Sample submitter | Kelley, Karen D. |
Date submitted | 8/27/1990 |
Project name | Lik Soil Study |
State | AK |
Country | United States |
Latitude (WGS84) | 68.16438192 |
Longitude (WGS84) | -163.20425824 |
Original datum | (NAD27) |
Original latitude | 68.165 |
Original longitude | -163.20111111 |
Location precision | 1 second |
Sample source | stream/river |
Collection method | composite |
Primary media type | sediment |
Notes on sample | stream |
Sieve size | -230 mesh |
(click for info) | |
Geologic map unit | -163.20425824, 68.16438192 |
Nearby scientific data | Find additional scientific data near this location |
Element | Measured value | Units of measure | Analytical method |
---|---|---|---|
Lithium | 60 | parts per million by weight | AES_HF |
Beryllium | 2 | parts per million by weight | AES_HF |
Sodium | 0.71 | percent by weight | AES_HF |
Magnesium | 1 | percent by weight | AES_HF |
Aluminum | 7.26 | percent by weight | AES_HF |
Phosphorus | 0.08 | percent by weight | AES_HF |
Potassium | 1.92 | percent by weight | AES_HF |
Calcium | 1.76 | percent by weight | AES_HF |
Scandium | 16 | parts per million by weight | AES_HF |
Titanium | 0.33 | percent by weight | AES_HF |
Vanadium | 182 | parts per million by weight | AES_HF |
Chromium | 150 | parts per million by weight | AES_HF |
Manganese | 0.07 | percent by weight | AES_HF |
Iron | 3.88 | percent by weight | AES_HF |
Cobalt | 18 | parts per million by weight | AES_HF |
Nickel | 75 | parts per million by weight | AES_HF |
Copper | 54 | parts per million by weight | AES_HF |
Zinc | 293 | parts per million by weight | AES_HF |
Gallium | 17 | parts per million by weight | AES_HF |
Arsenic | 10 | parts per million by weight | AES_HF |
Strontium | 140 | parts per million by weight | AES_HF |
Yttrium | 23 | parts per million by weight | AES_HF |
Niobium | 7 | parts per million by weight | AES_HF |
Molybdenum | <2 | parts per million by weight | AES_HF |
Silver | <2 | parts per million by weight | AES_HF |
Cadmium | <2 | parts per million by weight | AES_HF |
Tin | <10 | parts per million by weight | AES_HF |
Barium | 1920 | parts per million by weight | AES_HF |
Lanthanum | 33 | parts per million by weight | AES_HF |
Cerium | 57 | parts per million by weight | AES_HF |
Neodymium | 29 | parts per million by weight | AES_HF |
Europium | <2 | parts per million by weight | AES_HF |
Holmium | <4 | parts per million by weight | AES_HF |
Ytterbium | 2 | parts per million by weight | AES_HF |
Tantalum | <40 | parts per million by weight | AES_HF |
Gold | <8 | parts per million by weight | AES_HF |
Lead | 62 | parts per million by weight | AES_HF |
Bismuth | <10 | parts per million by weight | AES_HF |
Thorium | 10 | parts per million by weight | AES_HF |
Uranium | <100 | parts per million by weight | AES_HF |
Element | Value | Units | Technique |
---|---|---|---|
Lithium | 60 | parts per million by weight | AES_HF |
Beryllium | 2 | parts per million by weight | AES_HF |
Sodium | 0.71 | percent by weight | AES_HF |
Magnesium | 1 | percent by weight | AES_HF |
Aluminum | 7.26 | percent by weight | AES_HF |
Phosphorus | 0.08 | percent by weight | AES_HF |
Potassium | 1.92 | percent by weight | AES_HF |
Calcium | 1.76 | percent by weight | AES_HF |
Scandium | 16 | parts per million by weight | AES_HF |
Titanium | 0.33 | percent by weight | AES_HF |
Vanadium | 182 | parts per million by weight | AES_HF |
Chromium | 150 | parts per million by weight | AES_HF |
Manganese | 0.07 | percent by weight | AES_HF |
Iron | 3.88 | percent by weight | AES_HF |
Cobalt | 18 | parts per million by weight | AES_HF |
Nickel | 75 | parts per million by weight | AES_HF |
Copper | 54 | parts per million by weight | AES_HF |
Copper | 47 | parts per million by weight | AES_AZ_P |
Zinc | 220 | parts per million by weight | AES_AZ_P |
Zinc | 293 | parts per million by weight | AES_HF |
Gallium | 17 | parts per million by weight | AES_HF |
Arsenic | 10 | parts per million by weight | AES_AZ_P |
Arsenic | 10 | parts per million by weight | AES_HF |
Strontium | 140 | parts per million by weight | AES_HF |
Yttrium | 23 | parts per million by weight | AES_HF |
Niobium | 7 | parts per million by weight | AES_HF |
Molybdenum | L2 | parts per million by weight | AES_HF |
Molybdenum | 3.6 | parts per million by weight | AES_AZ_P |
Silver | 0.28 | parts per million by weight | AES_AZ_P |
Silver | L2 | parts per million by weight | AES_HF |
Cadmium | 0.81 | parts per million by weight | AES_AZ_P |
Cadmium | L2 | parts per million by weight | AES_HF |
Tin | L10 | parts per million by weight | AES_HF |
Antimony | 2.5 | parts per million by weight | AES_AZ_P |
Barium | 1920 | parts per million by weight | AES_HF |
Lanthanum | 33 | parts per million by weight | AES_HF |
Cerium | 57 | parts per million by weight | AES_HF |
Neodymium | 29 | parts per million by weight | AES_HF |
Europium | L2 | parts per million by weight | AES_HF |
Holmium | L4 | parts per million by weight | AES_HF |
Ytterbium | 2 | parts per million by weight | AES_HF |
Tantalum | L40 | parts per million by weight | AES_HF |
Gold | L8 | parts per million by weight | AES_HF |
Gold | N0.15 | parts per million by weight | AES_AZ_P |
Lead | 62 | parts per million by weight | AES_AZ_P |
Lead | 62 | parts per million by weight | AES_HF |
Bismuth | N0.6 | parts per million by weight | AES_AZ_P |
Bismuth | L10 | parts per million by weight | AES_HF |
Thorium | 10 | parts per million by weight | AES_HF |
Uranium | L100 | parts per million by weight | AES_HF |