Field | Value |
---|---|
Lab ID | D382852 |
Field ID | 991 |
Job ID | UQ11 |
Sample submitter | Cathrall, John B. |
Date submitted | 7/17/1991 |
Project name | Craig AMRAP |
State | AK |
Country | United States |
Latitude (WGS84) | 55.37652646 |
Longitude (WGS84) | -132.97095367 |
Original datum | (NAD27) |
Original latitude | 55.37694444 |
Original longitude | -132.96944444 |
Location precision | 1 second |
Sample source | stream/river |
Collection method | composite |
Primary media type | sediment |
Notes on sample | stream |
Sieve size | -60 mesh |
(click for info) | |
Geologic map unit | -132.97095367, 55.37652646 |
Nearby scientific data | Find additional scientific data near this location |
Element | Measured value | Units of measure | Analytical method |
---|---|---|---|
Beryllium | 1 | parts per million by weight | ES_SQ |
Boron | 20 | parts per million by weight | ES_SQ |
Sodium | 0.7 | percent by weight | ES_SQ |
Magnesium | 3 | percent by weight | ES_SQ |
Phosphorus | <0.2 | percent by weight | ES_SQ |
Calcium | 0.1 | percent by weight | ES_SQ |
Scandium | 5 | parts per million by weight | ES_SQ |
Titanium | 0.2 | percent by weight | ES_SQ |
Vanadium | 50 | parts per million by weight | ES_SQ |
Chromium | 10 | parts per million by weight | ES_SQ |
Manganese | 0.51 | percent by weight | ES_SQ |
Iron | 15 | percent by weight | ES_SQ |
Cobalt | 10 | parts per million by weight | ES_SQ |
Nickel | <5 | parts per million by weight | ES_SQ |
Copper | 7000 | parts per million by weight | ES_SQ |
Zinc | 10000 | parts per million by weight | ES_SQ |
Gallium | 70 | parts per million by weight | ES_SQ |
Germanium | <10 | parts per million by weight | ES_SQ |
Arsenic | <200 | parts per million by weight | ES_SQ |
Strontium | <100 | parts per million by weight | ES_SQ |
Yttrium | 100 | parts per million by weight | ES_SQ |
Zirconium | 500 | parts per million by weight | ES_SQ |
Niobium | <20 | parts per million by weight | ES_SQ |
Molybdenum | 15 | parts per million by weight | ES_SQ |
Silver | 10 | parts per million by weight | ES_SQ |
Cadmium | 100 | parts per million by weight | ES_SQ |
Tin | <10 | parts per million by weight | ES_SQ |
Antimony | <100 | parts per million by weight | ES_SQ |
Barium | 100 | parts per million by weight | ES_SQ |
Lanthanum | <50 | parts per million by weight | ES_SQ |
Tungsten | <20 | parts per million by weight | ES_SQ |
Gold | 0.25 | parts per million by weight | AA_F_HBr |
Mercury | 3.3 | parts per million by weight | AA_CV |
Lead | 100 | parts per million by weight | ES_SQ |
Bismuth | <10 | parts per million by weight | ES_SQ |
Thorium | <100 | parts per million by weight | ES_SQ |
Element | Value | Units | Technique |
---|---|---|---|
Beryllium | 1 | parts per million by weight | ES_SQ |
Boron | 20 | parts per million by weight | ES_SQ |
Sodium | 0.7 | percent by weight | ES_SQ |
Magnesium | 3 | percent by weight | ES_SQ |
Phosphorus | N0.2 | percent by weight | ES_SQ |
Calcium | 0.1 | percent by weight | ES_SQ |
Scandium | 5 | parts per million by weight | ES_SQ |
Titanium | 0.2 | percent by weight | ES_SQ |
Vanadium | 50 | parts per million by weight | ES_SQ |
Chromium | 10 | parts per million by weight | ES_SQ |
Manganese | G0.51 | percent by weight | ES_SQ |
Iron | 15 | percent by weight | ES_SQ |
Cobalt | 10 | parts per million by weight | ES_SQ |
Nickel | N5 | parts per million by weight | ES_SQ |
Copper | 7000 | parts per million by weight | ES_SQ |
Copper | 4100 | parts per million by weight | AES_AZ_P |
Zinc | 3100 | parts per million by weight | AES_AZ_P |
Zinc | 10000 | parts per million by weight | ES_SQ |
Gallium | 70 | parts per million by weight | ES_SQ |
Germanium | N10 | parts per million by weight | ES_SQ |
Arsenic | N200 | parts per million by weight | ES_SQ |
Arsenic | 45 | parts per million by weight | AES_AZ_P |
Strontium | N100 | parts per million by weight | ES_SQ |
Yttrium | 100 | parts per million by weight | ES_SQ |
Zirconium | 500 | parts per million by weight | ES_SQ |
Niobium | N20 | parts per million by weight | ES_SQ |
Molybdenum | 15 | parts per million by weight | ES_SQ |
Molybdenum | 39 | parts per million by weight | AES_AZ_P |
Silver | 24 | parts per million by weight | AES_AZ_P |
Silver | 10 | parts per million by weight | ES_SQ |
Cadmium | 33 | parts per million by weight | AES_AZ_P |
Cadmium | 100 | parts per million by weight | ES_SQ |
Tin | N10 | parts per million by weight | ES_SQ |
Antimony | N100 | parts per million by weight | ES_SQ |
Antimony | 9.6 | parts per million by weight | AES_AZ_P |
Barium | 100 | parts per million by weight | ES_SQ |
Lanthanum | N50 | parts per million by weight | ES_SQ |
Tungsten | N20 | parts per million by weight | ES_SQ |
Gold | N10 | parts per million by weight | ES_SQ |
Gold | 0.25 | parts per million by weight | AA_F_HBr |
Gold | N1.1 | parts per million by weight | AES_AZ_P |
Mercury | 3.3 | parts per million by weight | AA_CV |
Lead | 100 | parts per million by weight | ES_SQ |
Lead | 140 | parts per million by weight | AES_AZ_P |
Bismuth | N10 | parts per million by weight | ES_SQ |
Bismuth | N7 | parts per million by weight | AES_AZ_P |
Thorium | N100 | parts per million by weight | ES_SQ |