Field | Value |
---|---|
Lab ID | D384870 |
Field ID | 581 |
Job ID | UR01 |
Sample submitter | Goldfarb, Richard J., and Sutley, Stephen J. |
Date submitted | 7/26/1991 |
Project name | Seldovia AMRAP |
State | AK |
Country | United States |
Latitude (WGS84) | 59.52269332 |
Longitude (WGS84) | -150.51931969 |
Original datum | (NAD27) |
Original latitude | 59.5233 |
Original longitude | -150.5172 |
Location precision | 1 second |
Sample source | stream/river |
Primary media type | sediment |
Notes on sample | unconsolidated sediment;; stream |
Sieve size | -80 mesh |
(click for info) | |
Geologic map unit | -150.51931969, 59.52269332 |
Nearby scientific data | Find additional scientific data near this location |
Element | Measured value | Units of measure | Analytical method |
---|---|---|---|
Beryllium | <1 | parts per million by weight | ES_SQ |
Boron | 30 | parts per million by weight | ES_SQ |
Sodium | 1 | percent by weight | ES_SQ |
Magnesium | 2 | percent by weight | ES_SQ |
Phosphorus | <0.2 | percent by weight | ES_SQ |
Calcium | 0.7 | percent by weight | ES_SQ |
Scandium | 15 | parts per million by weight | ES_SQ |
Titanium | 0.5 | percent by weight | ES_SQ |
Vanadium | 150 | parts per million by weight | ES_SQ |
Chromium | 50 | parts per million by weight | ES_SQ |
Manganese | 0.1 | percent by weight | ES_SQ |
Iron | 5 | percent by weight | ES_SQ |
Cobalt | 20 | parts per million by weight | ES_SQ |
Nickel | 30 | parts per million by weight | ES_SQ |
Copper | 70 | parts per million by weight | ES_SQ |
Zinc | <200 | parts per million by weight | ES_SQ |
Gallium | 20 | parts per million by weight | ES_SQ |
Germanium | <10 | parts per million by weight | ES_SQ |
Arsenic | <200 | parts per million by weight | ES_SQ |
Strontium | 200 | parts per million by weight | ES_SQ |
Yttrium | 20 | parts per million by weight | ES_SQ |
Zirconium | 100 | parts per million by weight | ES_SQ |
Niobium | <20 | parts per million by weight | ES_SQ |
Molybdenum | <5 | parts per million by weight | ES_SQ |
Silver | <0.5 | parts per million by weight | ES_SQ |
Cadmium | <20 | parts per million by weight | ES_SQ |
Tin | <10 | parts per million by weight | ES_SQ |
Antimony | <100 | parts per million by weight | ES_SQ |
Barium | 500 | parts per million by weight | ES_SQ |
Lanthanum | <50 | parts per million by weight | ES_SQ |
Tungsten | <20 | parts per million by weight | ES_SQ |
Gold | 0.008 | parts per million by weight | AA_GF_HBr |
Lead | 15 | parts per million by weight | ES_SQ |
Bismuth | <10 | parts per million by weight | ES_SQ |
Thorium | <100 | parts per million by weight | ES_SQ |
Element | Value | Units | Technique |
---|---|---|---|
Beryllium | L1 | parts per million by weight | ES_SQ |
Boron | 30 | parts per million by weight | ES_SQ |
Sodium | 1 | percent by weight | ES_SQ |
Magnesium | 2 | percent by weight | ES_SQ |
Phosphorus | L0.2 | percent by weight | ES_SQ |
Calcium | 0.7 | percent by weight | ES_SQ |
Scandium | 15 | parts per million by weight | ES_SQ |
Titanium | 0.5 | percent by weight | ES_SQ |
Vanadium | 150 | parts per million by weight | ES_SQ |
Chromium | 50 | parts per million by weight | ES_SQ |
Manganese | 0.1 | percent by weight | ES_SQ |
Iron | 5 | percent by weight | ES_SQ |
Cobalt | 20 | parts per million by weight | ES_SQ |
Nickel | 30 | parts per million by weight | ES_SQ |
Copper | 70 | parts per million by weight | ES_SQ |
Copper | 80 | parts per million by weight | AES_AZ_P |
Zinc | N200 | parts per million by weight | ES_SQ |
Zinc | 150 | parts per million by weight | AES_AZ_P |
Gallium | 20 | parts per million by weight | ES_SQ |
Germanium | N10 | parts per million by weight | ES_SQ |
Arsenic | N200 | parts per million by weight | ES_SQ |
Arsenic | 40 | parts per million by weight | AES_AZ_P |
Strontium | 200 | parts per million by weight | ES_SQ |
Yttrium | 20 | parts per million by weight | ES_SQ |
Zirconium | 100 | parts per million by weight | ES_SQ |
Niobium | N20 | parts per million by weight | ES_SQ |
Molybdenum | 1.1 | parts per million by weight | AES_AZ_P |
Molybdenum | N5 | parts per million by weight | ES_SQ |
Silver | 0.09 | parts per million by weight | AES_AZ_P |
Silver | N0.5 | parts per million by weight | ES_SQ |
Cadmium | 0.5 | parts per million by weight | AES_AZ_P |
Cadmium | N20 | parts per million by weight | ES_SQ |
Tin | N10 | parts per million by weight | ES_SQ |
Antimony | 2 | parts per million by weight | AES_AZ_P |
Antimony | N100 | parts per million by weight | ES_SQ |
Barium | 500 | parts per million by weight | ES_SQ |
Lanthanum | L50 | parts per million by weight | ES_SQ |
Tungsten | N20 | parts per million by weight | ES_SQ |
Gold | N0.1 | parts per million by weight | AES_AZ_P |
Gold | N10 | parts per million by weight | ES_SQ |
Gold | 0.008 | parts per million by weight | AA_GF_HBr |
Lead | 15 | parts per million by weight | ES_SQ |
Lead | 18 | parts per million by weight | AES_AZ_P |
Bismuth | N10 | parts per million by weight | ES_SQ |
Bismuth | N0.67 | parts per million by weight | AES_AZ_P |
Thorium | N100 | parts per million by weight | ES_SQ |